There is currently a growing demand for more effective thermal insulation materials with the best performance properties. This research paper presents the investigation results on the influence of two types of filler on the structure and properties of rigid polyurethane foam composites. Fly ash as a product of coal combustion in power plants and microspheres of 5, 10, 15, and 20 wt.%, were used as rigid polyurethane foams modifiers. The results of thermal analysis, mechanical properties testing, and cellular structure investigation performed for polyurethane composites show that the addition of fly ash, up to 10 wt.%, significantly improved the majority of the tested parameters. The use of up to 20 wt.% of microspheres improves the mechanical and thermal properties and thermal stability of rigid polyurethane foams.

The aim of the article is to compare two types of fly ash (from the fluidized and pulverized coal combustion process) as a filler for rigid polyurethane foam. Pulverized fly ash (PFA) is widely used in building materials, while fluidized fly ash (FFA) is not currently recycled, but landfilled. The produced rigid polyurethane foams were reinforced with 5 and 10% by weight addition of fly ash from two different types of boilers. The foaming process, physical properties, morphologies and thermal degradation were subject to comparative analysis. The research indicated that fly ash intensifies the reactions of foam synthesis, most commonly, polyurethane (PU) foam with an addition of 10% PFA. What is interesting is that both ashes can be used in PU foam technology as they do not cause deterioration of the physical parameters. As shown, the addition of filler affects the morphology and impairs the brittleness. Additionally, the use of fly ash from coal combustion in the technology of polyurethane materials complies with the guidelines of the circular economy stated in the European Union legislation. Partial replacement of petrochemical components with waste filler also reduces the total energy consumption in the production of PU composites.

According to the assumptions of the European Union, by 2050 it is planned to achieve climate neutrality. For this purpose, a document called the “European Green Deal” was established, which is a set of policies of the European Commission. One of the assumptions is a circular economy that takes into account the use of waste in subsequent production cycles. In order to meet the latest trends in environmentally friendly materials and use of waste in the production of building materials, composites of rigid polyurethane foam with 10 wt.% of waste were produced. Fly ash from coal combustion after modification was used as a filler. Three types of modifications were used: silanization, sieving, and both processes together. The silanization process was carried out for 1 and 2% silane ([3-(2-aminoethylamino)propyl]trimethoxysilane) concentration in relation to the fly ash mass. The sieving was aimed at reaching a fraction with a particle diameter below 75 µm. Six composites with modified fillers were compared and one material containing unchanged fly ash was used as a reference. A comparative analysis was carried out on the basis of surface analysis, thermal stability and physical properties. It turned out that the polyurethane materials modified fly ash silanized with 1% and 2% silane solution proved the best results in performed tests. On the other hand, the polyurethane foam containing sieved ash was characterized by the lowest flammability and the lowest emission of smoke and CO. The use of modified fly ash in technology of polyurethane foams can be a good method of its disposal and can increase the applicability of the composites.

The thermal properties and flammability of rigid polyurethane foams (RPUFs) containing various flame retardants, including solid (melamine, expanded graphite (EG), Exolit OP 935, ammonium polyphosphate (APP)) and liquid (Roflam B7, Roflam PLO) types, added at 30 wt.% and 60 wt.% by weight have been evaluated. Thermogravimetric analysis (TGA) demonstrated enhanced thermal stability, with the maximum 10% weight loss temperature (292 °C, +34 °C vs. reference) observed for foams containing 60 wt.% Exolit OP 935 and APP. The limiting oxygen index (LOI) test demonstrated the optimal performance for 30 wt.% APP and melamine (26.4 vol.% vs. 18.7 vol.% reference). In the UL-94 test, Exolit OP 935 and APP achieved a V-0 rating. The 60 wt.% Exolit with an EG blend also demonstrated a substantial reduction in heat release rate. These findings underscore the cooperative effects of hybrid flame retardants, thereby supporting their utilization in fire-safe RPUFs for construction and transport.