Detailed crystallographic information provided by X-ray diffraction (XRD) is complementary to molecular information provided by Raman spectroscopy. Accordingly, the combined use of these techniques allows the identification of an unknown compound without ambiguity. However, a full combination of Raman and XRD results requires an appropriate and reliable reference database with complete information. This is already available for XRD. The main objective of this paper is to introduce and describe the recently developed Raman Open Database (ROD, http://solsa.crystallography.net/rod). It comprises a collection of high-quality uncorrected Raman spectra. The novelty of this database is its interconnectedness with other open databases like the Crystallography Open Database (http://www.crystallography.net/cod and Theoretical Crystallography Open Database (http://www.crystallography.net/tcod/). The syntax adopted to format entries in the ROD is based on the worldwide recognized and used CIF format, which offers a simple way for data exchange, writing and description. ROD also uses JCAMP-DX files as an alternative format for submitted spectra. JCAMP-DX files are compatible to varying degrees with most commercial Raman software and can be read and edited using standard text editors.

The reactivity effect of calcium carbonate, present in ground oyster shells and limestone filler, on the formation of carboaluminate phases in ground granulated blast furnace slag blended cement pastes was reported in this paper. Six different binary and ternary blended cement pastes were prepared using ground granulated blast furnace slag, ground oyster shells and limestone filler with different replacement levels (from 5 to 35%). The carboaluminate formation was assessed and quantified directly using X-ray diffraction (XRD), and indirectly by following the aluminate phase’s reaction (heat flow) and consumed calcium carbonate using Isothermal Calorimetry (IC) and Thermogravimetric Analysis (TGA), respectively. Further, the overall reaction degree calculated based on TGA results and the compressive strength were determined to support the findings obtained. The results revealed that the calcium carbonate present in ground oyster shells is more reactive when compared to that present in limestone filler, where more formed hemi- and monocarboaluminate phases were observed in mixtures containing ground oyster shells. An enhancement in compressive strength and overall reaction degree was observed by adding 5% ground oyster shells as cement replacement.

The French gravel industry produces approximatively 6.5 million tons of gravel wash mud each year. This material offers very promising properties which require an in-depth characterization study before its use as a construction material, otherwise it is removed from value cycles by disposal in landfills. We examined the suitability of gravel wash mud and seashells, with fly ash as a binder, as an unfired earth construction material. Thermal and mechanical characterizations of the smart mixture composed of gravel wash mud, Crepidula fornicata shells and fly ash are performed. The new specimens exhibit high compressive strengths compared to usual earth construction materials, which appears as a good opportunity for a reduction in the thickness of walls. The use of fly ash and Crepidula shells in addition to gravel wash mud provides high silica and calcium contents, which both react with clay, leading to the formation of tobermorite and Al-tobermorite as a result of a pozzolanic reaction. Considering the reduction in porosity and improvements in strength, these new materials are good candidates to contribute significantly to the Sustainable Development Goals (SDGs) and reduce carbon emissions.

Different polytypes of SiC are described and predicted in literature. Here, we report the first occurrence of an orthorhombic 6O-SiC polytype as rock-forming mineral in the nickel laterite mine of Tiebaghi (New Caledonia). This new class of SiC crystallizes in the space group Cmc2₁ with 12 atoms per unit cell [a = 3.0778(6) Å, b = 5.335(2) Å, c = 15.1219(6) Å, α = 90°, β = 90°, γ = 120°]. The density of 6O-SiC is about 3.22 g/cm³ and the calculated indirect bandgap at room temperature of 3.56 eV is identical to 6H-SiC. Our results suggest that 6O-SiC is the intermediate state in the wurtzite to rocksalt transformation of 6H-SiC.

The three different Mollusk shells, Pecten maximus, Crepidula fornicata and Crassostrea gigas, were studied and compared with synthetic and commercial powders. All samples were analysed by X-ray diffraction, Quantitative phase analysis, and quantitative line broadening (microstructure) analysis using the Combined Analysis method. LDPE-CaCO3 composites were prepared in a twin screw extruder in the composition range of 0–10.8 filler content. Ultimate Mechanical properties of dog-bone type injection molded tensile specimens (ISO-527-2-5A) were measured. Results are showing that the biogenic calcium carbonate is less efficient in improving polyethylene stiffness than the synthetic ones, independently of its crystalline form, to use stearic acid coating allows an improvement of the matrix stiffening. The yield strength is unchanged whatever the kind of filler used.