Despite Fused Deposition Modeling (FDM) being an economical 3D printing method known for its material versatility and ease of use, the mechanical performance of FDM-produced components is significantly influenced by process parameter settings. This study investigated the effects of the layer thickness, raster angle, build orientation, and extrusion temperature on the ultimate tensile strength (UTS) and elastic modulus of Polylactic Acid (PLA) specimens using Taguchi methods, with significance analyzed through analysis of variance (ANOVA). The results indicated that the build orientation is the primary factor affecting both the UTS and elastic modulus, with a flat orientation yielding the best performance. ANOVA showed that the build orientation, raster angle, and extrusion temperature significantly influence the UTS, with the build orientation contributing 98.16%. For the elastic modulus, the build orientation and raster angle were significant, contributing 94.83% and 1.76%, respectively. The optimal parameters were a 0.16 mm layer thickness, flat build orientation, 30°/−60° raster angle, and 200 °C extrusion temperature, resulting in predicted UTS and elastic modulus values with error percentages of 4.33% and 2.74%, respectively, compared to experimental values. The regression model demonstrated high predictive accuracy, with R-squared values of 99.71% for the UTS and 99.52% for the elastic modulus.

Fused deposition modeling (FDM)-based three-dimensional (3D) fabrication offers a viable approach to manufacturing highly customized carbon fiber-reinforced polyether ether ketone (CFR-PEEK) components with complex geometries. However, the mechanical properties and surface roughness of FDM-fabricated parts are strongly influenced by processing parameters, particularly layer thickness. This study investigates the influence of layer thickness (0.1 mm and 0.2 mm) on the surface roughness, crystallinity, mechanical properties, and morphological characteristics of FDM-printed 10% CFR-PEEK specimens. The specimens were characterized using mechanical testing, differential scanning calorimetry (DSC), confocal laser microscopy, X-ray micro-computed tomography (µCT), and scanning electron microscopy (SEM). The results show that specimens printed with a 0.2 mm layer thickness exhibit higher crystallinity and ball indentation hardness while also showing increased surface roughness and porosity, with µCT analysis revealing larger and more spatially clustered voids near the sub-perimeter regions. In contrast, specimens printed with a 0.1 mm layer thickness demonstrate higher tensile strength, elastic modulus, elongation at break, and compressive stress. SEM fractography further indicates improved interlayer bonding and a relatively cohesive fracture surface in specimens printed with a 0.1 mm layer thickness. These findings demonstrate clear layer-thickness-dependent processing–structure–property relationships in FDM-printed CFR-PEEK composites and provide guidance for optimizing printing parameters to achieve improved mechanical performance.