The aim of the present study was to assess by atomic force microscopy (AFM) the surface roughness of a traditional glass ionomer cement- GIC (Fuji IX GP, GC Corporation, Tokyo, Japan) and a resin modified glass ionomer cement- RMGIC (Vitremer, 3M ESPE, St. Paul, MN, USA) after different immersion regimes on some acidic drinks. Sixteen cylindrical samples having the height of 5 mm and the thickness of 2 mm were obtained from each material and they were divided into two groups: Group I (Fuji IX samples) and Group II (Vitremer samples). Specimens of each group were then randomly divided into 4 subgroups: subgroup A (control)—15 samples were kept in artificial saliva and in the other three subgroups, each having 15 samples the samples were immersed in Coca-Cola (subgroup B), Cappy lemonade and mint (subgroup C) and Fuzetea (subgroup D) for 7 days (subgroups A1–D1), 14 days (subgroups A2–D2), and 21 days (subgroups A3–D3). AFM qualitative and quantitative surface evaluation (mean value of surface roughness parameter, Sa) of each sample was performed. The highest surface roughness was determined when both materials were submerged 14 days in acidic drinks. Traditional GIC was more affected by acidic environment when comparing to RMGIC.

This in vitro study aimed to assess the erosive effect of hydrochloric acid in association with toothbrushing procedure on the surface condition of three bulk-fill composite resins used for direct restoration. A total of 480 samples (160 from each composite resin): X-tra Fil (VOCO, Germany)—group A, Filtek Bulk-fill Posterior (3M-ESPE, St. Paul, MN, USA)—group B, G-aenial Posterior (GC Japan)—group C were prepared, submitted to chemical attack for 60 min with hydrochloric acid 30% and, subsequently, submitted to the abrasive effect of toothbrushing using 10,000 cycles with medium and hard bristles, at three different times (immediately and after 30 min after acid attack or without any chemical attack). The surface roughness of the samples was measured using a noncontact profilometer (Dektak XT, Bruker, Billerica, MA, USA). The values were analyzed using ANOVA and post hoc Bonferroni tests, with a p < 0.05. Chemical attack for 60 min associated with one year of toothbrushing with toothbrushes having medium or hard bristles increase the surface roughness of tested bulk-fill composite resins. No differences were recorded between toothbrushing with medium or firm bristles immediately or 30 min after acidic challenge for each of the three bulk-fill composite resins. Exposure to hydrochloric acid determines no effect on surface roughness of bulk-fill composite resins.

This study aimed to compare the color changes in two different orthodontic clear aligner systems after submersion in various beverages for 14 days. The tested aligner systems were Taglus Premium made of polyethylene terephthalate glycol (the TAG group) and CA^® Prodin+ made of a transparent copolyester and a thermoplastic elastomer (the PRO group). A total of 56 samples were firstly divided into two groups according to the tested system—TAG and PRO. Each group was subsequently divided in four subgroups according to immersion solution: A—artificial saliva, B—cola, C—coffee, D—red wine. Color measurements were performed on Days 1, 7 and 14 using a portable colorimeter and the CIE L*a*b* system. The obtained results showed significant color changes in both materials when exposed to coffee and red wine (p > 0.05). Samples in the PRO group showed a greater susceptibility to discoloration (higher ΔE values) when compared to the TAG group after submersion in cola (p = 0.025), coffee (p = 0.005) and red wine (p = 0.041) solutions. Statistical analysis revealed that all of the color parameters ΔL*, Δa*, Δb* and ΔE of both tested materials were affected by submersion in coffee solution for 14 days. In conclusion, the CA^® Pro+ aligner system is more prone to staining compared to the Taglus material after submersion for 14 days in cola, coffee and red wine solutions. Submersion for 14 days in coffee solution alters all of the color parameters (ΔL, Δa, Δb and ΔE) of both tested aligner materials.

The aim of the study was to evaluate the antibacterial activity and surface hardness of a light-activated microhybrid composite resin modified with green silver nanoparticles (AgNPs). AgNPs were synthesized using an Equisetum sylvaticum extract and characterized through different methods such as UV-Vis, EDX, and FTIR. The obtained AgNPs were mixed with a microhybrid composite resin (Herculite XRV, Kerr Corp., Orange, CA, USA) in different concentrations: 0% (group A-control); 0.5% (group B); 1% (group C); and 1.5% (group D). A total of 120 composite resin disk-shaped samples were obtained and divided into 4 groups (n = 30) according to AgNP concentration. Each group was then divided into 2 subgroups: subgroup 1—samples were not soaked in 0.01 M NaOH solution; and subgroup 2—samples were soaked in 0.01 M NaOH solution. The antibacterial activity against Streptococcus mutans was determined using a direct contact test. A digital electronic hardness tester was used to determine the composite resin’s Vickers surface hardness (VH). Statistical analysis was performed using the Mann–Whitney U and Kruskal–Wallis nonparametric tests with a confidence level of 95%. Groups C and D showed higher antibacterial activity against S. mutans when compared to the control group (p < 0.05). No significant differences were recorded between VH values (p > 0.05). The use of AgNPs synthesized from Equisetum sylvaticum as a composite resin filler in 1% wt. and 1.5% wt. reduced the activity of Streptococcus mutans. Soaking of the experimental composite resin decreased the antibacterial efficacy. The loading of a microhybrid composite resin with AgNPs in concentrations of 0.5% wt., 1% wt., and 1.5% wt. did not influence the surface hardness.

There are two main methods used for dentin hypersensitivity (DH) treatment: dentinal tubule occlusion and blockage of nerve activity. Dentifrices are the most common vehicles for active ingredients used for DH treatment. The aim of this study was to evaluate the efficacy of three toothpastes on dentinal tubule occlusion, mineral acquisition, and dentin hardness. Forty human dentin disks were submerged in 40% citric acid for 30 s and then exposed to tooth brushing for 2 min twice a day for 14 days using three toothpastes: Dontodent Sensitive (group 1), Dr. Wolff’s Biorepair (group 2), and Sensodyne Repair and Protect (group 3). In the control group (group 4), the samples were brushed with water. All of the samples were evaluated using scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), and Vickers dentin hardness determination. On SEM images, the degree of dentinal tubule occlusion was assessed using a five-grade scale. The mean score values in groups 1–4 were 3.60 ± 0.69, 2.20 ± 0.91, 2.30 ± 1.16, and 5.00 ± 0.00, significantly higher in study groups when compared to the control group (Kruskal Wallis test p < 0.05). EDX evaluation showed significantly higher calcium and phosphorus concentrations in groups 1 and 3 when compared to control group d. The mean values of Vickers dentin hardness numbers in groups 1–4 were 243.03 ± 10.014, 327.38 ± 56.65, 260.29 ± 37.69, and 225.83 ± 29.93, respectively. No statistically significant results were obtained when comparing the hardness mean values in groups (Kruskal-Wallis statistical test, p = 0.372 > 0.05). All three toothpastes tested demonstrated significant occlusion of dentinal tubules. Dontodent Sensitive and Sensodyne Repair and Protect toothpastes enhanced the calcium and phosphorus content of the dentin surface. None of the toothpastes increased dentin hardness as a result of mineral acquisition.

The aim of this in vitro study was to evaluate the effect of hydrochloric acid associated with the abrasive effect of toothbrushing on the surface condition of three flowable composite resins used for direct restoration. Seventy samples of each composite resin: Grandio Flow (VOCO, Germany)—group A, Filtek Ultimate Flow (3M-ESPE, MN, USA)—group B, G-aenial Flo X (GC Europe)—group C were prepared, submersed in hydrochloric acid 30% for 60 min and then submitted to simulated toothbrushing procedure using 5000 cycles with toothbrushes with medium and hard bristles, immediately after the chemical attack, after 30 min or without any chemical attack. The sample’s surface roughness was analyzed using a noncontact profilometer (Dektak XT, Bruker, USA). ANOVA and post hoc Bonferroni tests, with a p < 0.05, were used to analyze the values. Hydrochloric acid action for 60 min and six months of toothbrushing using toothbrushes having medium hardness or firm bristles affects the surface roughness of tested flowable composite resins. Toothbrushing with firm bristles immediately after acidic challenge determines increased surface roughness for two of the three flowable composite resins (Grandio Flow and Filtek Ultimate Flow). Toothbrushing with medium or firm bristles thirty minutes after the acidic aggression determine no effect on surface condition of flowable composite resins.