Natural zeolites (NatZ) are widely available, porous, crystalline aluminosilicate minerals that are commonly used as cost-effective adsorbents in water treatment processes. Despite their efficiency in removing various heavy metal ions from wastewater, NatZ show relatively low affinity toward Ni²⁺ and Cr³⁺ ions. This study aimed to develop composite adsorbents based on NatZ and hydroxyapatite using two methods, hydrothermal and mechanochemical, and their adsorption properties for the removal of Ni²⁺ and Cr³⁺ ions from aqueous solutions were investigated. X-ray powder diffraction and scanning electron microscopy analyses confirmed that under hydrothermal conditions, needle-like hydroxyapatite crystals were formed on the surface of NatZ, while the zeolite structure remained unchanged. Compared to the mechanochemically prepared sample, this adsorbent showed higher efficiency, binding 6.91 mg Ni²⁺/g and 16.95 mg Cr³⁺/g. Adsorption kinetics of the tested cations in both cases can be described by a pseudo-second-order model (R² is higher than 0.95 for all adsorbents). It is concluded that the presence of hydroxyapatite on the zeolite surface significantly improves the adsorption performance of NatZ, demonstrating its potential for the removal of heavy metal ions in wastewater treatment.

Efficient extraction of zinc from polymetallic concentrates is crucial for the metallurgical industry. Traditional leaching techniques often rely on strong oxidizing agents, which can be wasteful and environmentally harmful. While cyclic oxidation systems like the Fe³⁺/Fe²⁺ pair are known, they often fail to achieve high leaching rates, especially when the raw material contains multiple sulfide minerals. In this study, we developed a novel oxidation system using manganese dioxide (MnO₂) as the primary oxidizing agent and potassium iodide (KI) as a supporting material to create an I₂/I⁻ oxidation cycle in a sulfuric acid medium, at an atmospheric pressure between 40 °C and 80 °C. Leaching experiments were conducted under varying temperatures and KI doses. The results demonstrated that for the MnO₂-KI system, a zinc leaching degree of 89.78% was achieved after 3 h of leaching at 80 °C, and kinetic studies indicated that the leaching process is diffusion-controlled (through the thin film), with an activation energy of 27.65 kJ mol⁻¹. Moreover, this system offers an improved method for separating iodine from the leachate upon completion, enhancing the overall process efficiency. It also opens opportunities to test other primary oxidizing agents in combination with iodide salts. These findings suggest that the MnO₂-KI oxidation system offers a promising approach for improving zinc recovery from sphalerite concentrates.

The production route for cement clinker, including the clinkerization protocol and temperature, is highly dependent on the selection of raw materials. Natural resource reserves used in cement manufacturing are steadily declining due to rapid urbanization and the growing demand for building materials. Consequently, there is an urgent need to identify alternative resources, potentially from cost-effective primary raw materials or waste products. This study aims to evaluate the feasibility of incorporating recycled concrete as construction and demolition waste (C&DW) with unconventional clayey materials (bentonite and zeolite) into clinker synthesis at a reduced temperature of 1300 °C. The effect of mechanical pretreatment of the clinker raw meal, applied for durations of 10 to 30 min, was investigated. Mix designs combining traditional and alternative raw materials, along with different mechanical pretreatment durations, were systematically tested to assess their impact on raw meal clinkerization and the resulting cement mechanical properties. Despite variations in raw meal composition, the produced clinkers consistently exhibited phase compositions comprising C₃S, C₂S, C₃A, and C₄AF, as confirmed by XRD, FTIR, and SEM/EDS analyses. Among the studied raw materials, clayey components played a dominant role in controlling the formation of the main cement minerals, demonstrating that zeolite and bentonite can effectively substitute standard clays. Additionally, C&DW did not impede clinkerization; rather, it functioned as a silica source, replacing quartz sand. Short mechanical pretreatments (10 min) enhanced the content of cement minerals, whereas longer treatments adversely affected clinkerization. This study offers new insights into cement clinker production at reduced temperatures through the use of C&DW combined with unconventional clayey materials. The clinkerization temperature was reduced by approximately 100 °C from the conventional 1400–1450 °C, while still producing cements with mechanical performance comparable to ordinary Portland cement (OPC). The resulting zeolite- and bentonite-based cements, either mechanically untreated or subjected to short pretreatment, are potentially suitable for structural concrete applications, while cements produced with longer mechanical pretreatments may be more appropriate for lower-demand or non-structural uses.