Polyether-ether-ketone (PEEK) biomaterial has been increasingly employed for orthopedic, trauma, spinal, and dental implants due to its biocompatibility and in vivo stability. However, a lack of bioactivity and binding ability to natural bone tissue has significantly limited PEEK for many challenging dental implant applications. In this work, nanocomposites based on PEEK reinforced with bioactive silicate-based bioceramics (forsterite or bioglass) as nanofillers were prepared using high energy ball milling followed by melt blending and compression molding. The influence of nanofillers type and content (10, 20 and 30 wt.%) on the crystalline structure, morphology, surface roughness, hydrophilicity, microhardness, elastic compression modulus, and flexural strength of the nanocomposites was investigated. The scanning electron microscopy images of the nanocomposites with low nanofillers content showed a homogenous surface with uniform dispersion within the PEEK matrix with no agglomerates. All nanocomposites showed an increased surface roughness compared to pristine PEEK. It was found that the incorporation of 20 wt.% forsterite was the most effective in the nanocomposite formulation compared with bioglass-based nanocomposites; it has significantly improved the elastic modulus, flexural strength, and microhardness. In vitro bioactivity evaluation, which used biomimetic simulated body fluid indicated the ability of PEEK nanocomposites loaded with forsterite or bioglass nanofillers to precipitate calcium and phosphate bone minerals on its surface. These nanocomposites are expected to be used in long-term load-bearing implant applications and could be recommended as a promising alternative to titanium and zirconia when used as a dental implant material.

Periodontitis is an inflammation-related condition, caused by an infectious microbiome and host defense that causes damage to periodontium. The natural processes of the mouth, like saliva production and eating, significantly diminish therapeutic medication residency in the region of periodontal disease. Furthermore, the complexity and diversity of pathological mechanisms make successful periodontitis treatment challenging. As a result, developing enhanced local drug delivery technologies and logical therapy procedures provides the foundation for effective periodontitis treatment. Being biocompatible, biodegradable, and easily administered to the periodontal tissues, hydrogels have sparked substantial an intense curiosity in the discipline of periodontal therapy. The primary objective of hydrogel research has changed in recent years to intelligent thermosensitive hydrogels, that involve local adjustable sol-gel transformations and regulate medication release in reaction to temperature, we present a thorough introduction to the creation and efficient construction of new intelligent thermosensitive hydrogels for periodontal regeneration. We also address cutting-edge smart hydrogel treatment options based on periodontitis pathophysiology. Furthermore, the problems and prospective study objectives are reviewed, with a focus on establishing effective hydrogel delivery methods and prospective clinical applications.

Three-dimensionally (3D)-printed fabricated denture bases have shown inferior strength to conventional and subtractively fabricated ones. Several factors could significantly improve the strength of 3D-printed denture base resin, including the addition of nanoparticles and post-curing factors. This study evaluated the effect of TiO₂ nanoparticle (TNP) addition and the post-curing time (PCT) on the flexural properties and hardness of three-dimensionally (3D)-printed denture base resins. A total of 360 specimens were fabricated, with 180 specimens from each type of resin. For evaluating the flexural properties, bar-shaped specimens measuring 64 × 10 × 3.3 mm were used, while, for the hardness testing, disc-shaped specimens measuring 15 × 2 mm were employed. The two 3D-printed resins utilized in this study were Asiga (DentaBASE) and NextDent (Vertex Dental B.V). Each resin was modified by adding TNPs at 1% and 2% concentrations, forming two groups and an additional unmodified group. Each group was divided into three subgroups according to the PCT (15, 60, and 90 min). All the specimens were subjected to artificial aging (5000 cycles), followed by testing of the flexural strength and elastic modulus using a universal testing machine, and the hardness using the Vickers hardness test. A three-way ANOVA was used for the data analysis, and a post hoc Tukey’s test was used for the pairwise comparisons (α = 0.05). Scanning electron microscopy (SEM) was used for the fracture surface analysis. The addition of the TNPs increased the flexural strength in comparison to the unmodified groups (p < 0.001), while there was no significant difference in the elastic modulus and hardness with the 1% TNP concentration. Among the TNP groups, the 2% TNP concentration significantly decreased the elastic modulus and hardness (p < 0.001). The SEM showed a homogenous distribution of the TNPs, and the more irregular fracture surface displayed ductile fractures. The PCT significantly increased the flexural strength, elastic modulus, and hardness (p < 0.001), and this increase was time-dependent. The three-way ANOVA results revealed a significant difference between the material types, TNP concentrations, and PCT interactions (p < 0.001). Both concentrations of the TNPs increased the flexural strength, while the 2% TNP concentration decreased the elastic modulus and hardness of the 3D-printed nanocomposites. The flexural strength and hardness increased as the PCT increased. The material type, TNP concentration, and PCT are important factors that affect the strength of 3D-printed nanocomposites and could improve their mechanical performance.