In the field of orthopedics and traumatology, polyether ether ketone (PEEK) serves a significant role as a suitable alternative to traditional metal-based implants like titanium. PEEK is being used more commonly to replace traditional dental products. For bonding with various adhesive agents and preserved teeth, the surface alteration of PEEK was investigated. The aim of this research was to understand how different types and contents of nano-sized silica (SiO₂) fillers influenced the surface and mechanical properties of PEEK nanocomposites used in prosthodontics. In this work, PEEK based nanocomposites containing hydrophilic or hydrophobic nano-silica were prepared by a compression molding technique. The influence of nano-SiO₂ type and content (10, 20 and 30% wt) on surface properties of the resultant nanocomposites was investigated by the use of scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), surface roughness analysis, and contact angle measurement. The crystalline structures of PEEK/SiO₂ nanocomposites were examined by X-ray diffraction (XRD) spectroscopy. Mechanical properties were measured by microhardness, elastic compression modulus, and flexural strength. All nanocomposites showed increased surface roughness compared to pure PEEK. SEM images revealed that nanocomposites filled with low content hydrophobic nano-SiO₂ showed uniform dispersion within the PEEK matrix. The introduction of 10 wt% of hydrophobic nano-SiO₂ to the PEEK matrix improved elastic modulus, flexural strength, and microhardness, according to the findings. The addition of nano-SiO₂ fillers in a higher weight percentage, over 10%, significantly damages the mechanical characteristics of the resultant nanocomposite. On the basis of the obtained results, PEEK/SiO₂ nanocomposites loaded with low content hydrophobic nano-SiO₂ are recommended as promising candidates for orthopedic and prosthodontics materials.

In this work, a chitosan–gelatin–ferulic acid blend was used in different ratios for preparing novel films that can be used in biomedical applications. Both acetic and formic acid were tested as solvents for the chitosan–gelatin–ferulic acid blend. Glycerol was tested as a plasticizer. The thickness, mechanical strength, static water contact angle and water uptake of the prepared films were determined. Also, the prepared films were characterized using different analysis techniques such as Fourier transform infrared spectroscopy (FT-IR) analysis, X-ray diffraction (XRD), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). Acetic acid produced continuous compact surfaces that are not recommended for testing in biomedical applications. The plasticized chitosan–gelatin–ferulic acid blend, using formic acid solvent, produced novel hexagonal porous films with a pore size of around 10–14 µm. This blend is recommended for preparing films (scaffolds) for testing in biomedical applications as it has the advantage of a decreased thickness.

Polyether-ether-ketone (PEEK) biomaterial has been increasingly employed for orthopedic, trauma, spinal, and dental implants due to its biocompatibility and in vivo stability. However, a lack of bioactivity and binding ability to natural bone tissue has significantly limited PEEK for many challenging dental implant applications. In this work, nanocomposites based on PEEK reinforced with bioactive silicate-based bioceramics (forsterite or bioglass) as nanofillers were prepared using high energy ball milling followed by melt blending and compression molding. The influence of nanofillers type and content (10, 20 and 30 wt.%) on the crystalline structure, morphology, surface roughness, hydrophilicity, microhardness, elastic compression modulus, and flexural strength of the nanocomposites was investigated. The scanning electron microscopy images of the nanocomposites with low nanofillers content showed a homogenous surface with uniform dispersion within the PEEK matrix with no agglomerates. All nanocomposites showed an increased surface roughness compared to pristine PEEK. It was found that the incorporation of 20 wt.% forsterite was the most effective in the nanocomposite formulation compared with bioglass-based nanocomposites; it has significantly improved the elastic modulus, flexural strength, and microhardness. In vitro bioactivity evaluation, which used biomimetic simulated body fluid indicated the ability of PEEK nanocomposites loaded with forsterite or bioglass nanofillers to precipitate calcium and phosphate bone minerals on its surface. These nanocomposites are expected to be used in long-term load-bearing implant applications and could be recommended as a promising alternative to titanium and zirconia when used as a dental implant material.

Chemical cross-linking was used to create nanocomposite hydrogels made up of gelatin (G) and borosilicate bioactive glass (BBG) with different content (0, 3, and 5 wt.%). The G/BBG nanocomposite hydrogels were studied for their morphology, mechanical properties, and viscoelasticity. SEM images revealed a macroporous interconnected structure with particles scattered across the pore walls. Studies of water absorption and degradation confirmed that the nanocomposite scaffolds were hydrophilic and biodegradable. The addition of 5% BBG to the scaffold formulations increased the compressive modulus by 413% and the compressive intensity by 20%, respectively. At all frequency ranges tested, the storage modulus (G′) was greater than the loss modulus (G″), revealing a self-standing elastic nanocomposite hydrogel. The nanocomposite scaffolds facilitated apatite formation while immersed in simulated body fluid (SBF). According to the findings, G/BBG nanocomposite scaffolds could be a promising biomaterial for bone regeneration.