Currently, millions of tons of textile waste from the garment and textile industries are generated worldwide each year. As a promising option in terms of sustainability, textile waste fibers could be used as internal reinforcement of cement-based composites by enhancing ductility and decreasing crack propagation. To this end, two extensive experimental programs were carried out, involving the use of either fractions of short random fibers at 6–10% by weight or nonwoven fabrics in 3–7 laminate layers in the textile waste-reinforcement of cement, and the mechanical and durability properties of the resulting composites were characterized. Flexural resistance in pre- and post-crack, toughness, and stiffness of the resulting composites were assessed in addition to unrestrained drying shrinkage testing. The results obtained from those programs were analyzed and compared to identify the optimal composite and potential applications. Based on the results of experimental analysis, the feasibility of using this textile waste composite as a potential construction material in nonstructural concrete structures such as facade cladding, raised floors, and pavements was confirmed. The optimal composite was proven to be the one reinforced with six layers of nonwoven fabric, with a flexural strength of 15.5 MPa and a toughness of 9.7 kJ/m².

This study aimed to investigate the recycling opportunities for industrial byproducts and their contribution to innovative concrete manufacturing processes. The attention was mainly focused on municipal solid waste incineration fly ash (MSWI-FA) and its employment, after a washing pre-treatment, as the main component in artificially manufactured aggregates containing cement and ground granulated blast furnace slag (GGBFS) in different percentages. The produced aggregates were used to produce lightweight concrete (LWC) containing both artificial aggregates only and artificial aggregates mixed with a relatively small percentage of recycled polyethylene terephthalate (PET) in the sand form. Thereby, the possibility of producing concrete with good mechanical properties and enhanced thermal properties was investigated through effective PET reuse with beneficial impacts on the thermal insulation of structures. Based on the obtained results, the samples containing artificial aggregates had lower compressive strength (up to 30%) but better thermal performance (up to 25%) with respect to the reference sample made from natural aggregates. Moreover, substituting 10% of recycled aggregates with PET led to a greater reduction in resistance while improving the thermal conductivity. This type of concrete could improve the economic and environmental aspects by incorporating industrial wastes—mainly fly ash—thereby lowering the use of cement, which would lead to a reduction in CO₂ emissions.