This research is driven by stringent environmental legislation requiring the consumption and use of environmentally friendly materials. In this context, this paper is concerned with the development and characterization of thermoplastic arrowroot starch (TPAS) based biocomposite films by incorporating arrowroot fiber (AF) (0–10%) into a glycerol plasticized matrix by using the solution casting method. Developed TPAS/AF composite films were investigated, such as physical, morphological (FESEM), tensile, and tear strength characteristics. The tensile and tear strengths of TPAS/AF composites were increased significantly from 4.77 to 15.22 MPa and 0.87 to 1.28 MPa, respectively, as compared to the control TPAS films, which were 2.42 MPa and 0.83 MPa, respectively, while elongation was significantly decreased from 25.57 to 6.21% compared to control TPAS film, which was 46.62%. The findings revealed that after the fiber was reinforced, the mechanical properties were enhanced, and the optimum filler content was 10%. Regardless of fiber loadings, the results of water absorption testing revealed that the composite films immersed in seawater and rainwater absorbed more water than distilled water. Overall, the results of this research focus on providing information on biopolymer composite film and revealing the great potential it has for the food packaging industry.

Dragon fruit, also called pitaya or pitahaya, is in the family Cactaceae. It is found in two genera: ‘Selenicereus’ and ‘Hylocereus’. The substantial growth in demand intensifies dragon fruit processing operations, and waste materials such as peels and seeds are generated in more significant quantities. The transformation of waste materials into value-added components needs greater focus since managing food waste is an important environmental concern. Two well-known varieties of dragon fruit are pitaya (Stenocereus) and pitahaya (Hylocereus), which are different in their sour and sweet tastes. The flesh of the dragon fruit constitutes about two-thirds (~65%) of the fruit, and the peel is approximately one-third (~22%). Dragon fruit peel is believed to be rich in pectin and dietary fibre. In this regard, extracting pectin from dragon fruit peel can be an innovative technology that minimises waste disposal and adds value to the peel. Dragon fruit are currently used in several applications, such as bioplastics, natural dyes and cosmetics. Further research is recommended for diverging its development in various areas and maturing the innovation of its usage.

This study set out with the aim of assessing the morphology and properties of lignocellulosic fiber extracted from the tubers mainly found in tropical forests called arrowroot (Maranta arundinacea). Arrowroot bagasse (ABF) and husk fibers (AHF) were extracted and the physical, chemical, thermal, morphological properties, as well as crystallinity, were characterized. The chemical composition analysis revealed that ABF has higher cellulose (45.97%) than AHF (37.35%), cassava bagasse (10.04%), and corn hull (15.30%). In addition, ABF are significantly low in lignin (2.78%) and density (1.11 g/cm³) than AHF, corn hull, and cassava. In this research, the physical, chemical, thermal, structural, and morphological properties of arrowroot bagasse and husk fibers were investigated by particle size analysis, chemical composition analysis, thermogravimetric analysis (TGA), Fourier transform infrared (FTIR) and scanning electron microscopy (SEM), respectively. With respect to the above characterization of fibers, it was found that the lignocellulosic biomasses from arrowroot are alternative promising sustainable material, which can be used in food packaging as a renewable filler.

This paper presents an experimental and numerical investigation of pultruded composite glass fibre-reinforced polymer (pGFRP) cross-arms subjected to flexural creep behaviour to assess their performance and sustainability in composite cross-arm structure applications. The primary objective of this study was to investigate the failure creep behaviour of pGFRP cross-arms with different stacking sequences. Specifically, the study aimed to understand the variations in strain rate exhibited during different stages of the creep process. Therefore, this study emphasizes a simplified approach within the experiment, numerical analysis, and mathematical modelling of three different pGFRP composites to estimate the stiffness reduction factors that determine the prediction of failure. The findings show that Findley’s power law and the Burger model projected very different strains and diverged noticeably outside the testing period. Findley’s model estimated a minimal increase in total strain over 50 years, while the Burger model anticipated PS-1 and PS-2 composites would fail within about 11 and 33 years, respectively. The Burger model’s forecasts might be more reasonable due to the harsh environment the cross-arms are expected to withstand. The endurance and long-term performance of composite materials used in overhead power transmission lines may be predicted mathematically, and this insight into material property factors can help with design and maintenance.