Data on the selective oxidation of methane to synthesis gas on a 9% NiCuCr/2% Ce/(ϑ + α)-Al2O3catalyst in dilute mixtures with Ar at short residence times (2–3 ms) are presented. The composition,...

This research is devoted to solving an environmental problem, cleaning of the Kazakhstan air basin, through treatment of auto-transport toxic exhaust by improving the hydrocarbon composition of motor fuels and neutralizing exhaust gas toxic components. The catalytic hydrodearomatization of gasoline fractions (from the reforming stage) of the Atyrau and Pavlodar Refineries and the neutralization of exhaust gas toxic components from an internal combustion engine (ICE) were studied. Two hydrotreated gasoline fractions were tested during ICE operation. The research shows that 100% benzene conversion is observed over Rh-Pt(9:1)/γ-Al₂O₃ catalysts; that is, benzene is completely removed from both fractions, and the aromatics content decreases from 56.24–58.12% to 21.29–21.89%, within the values of the Euro-5,6 standard. Catalytic treatment of fuels reduces fuel consumption of the ICE engine by 2–3% compared to the initial gasoline fractions, the CO content in the exhaust gases decreases by 6.6–16.2%, and the hydrocarbon content decreases by 7.8–24.7%. In order to neutralize the ICE exhaust gas toxic components, the catalyst 10% Co + 0.5% Pt/Al₂O₃ was used, with which the CO conversion reaches 100% and the hydrocarbon conversion 94.2% and 91.5% for both gasoline fractions. The catalysts were characterized by electron microscopy (EM), X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET), thermoprogrammed desorption (TPD) and thermoprogrammed reduction (TPR) methods. It was shown by the TPD and EM methods that at the addition of Pt to the Rh-catalyst, the formation of mixed bimetallic Rh-Pt-agglomerates occurs, and hydrogen appears in the TPD spectrum, adsorbed in the form of a new single peak uncharacteristic for the Rh-catalyst. This leads to high activity and selectivity in the hydrogenation of benzene and aromatic compounds in the gasoline fractions. The XRD and TPR results show the formation of CoAl₂O₄ spinels, on which inactive oxygen is formed for the oxidation of CO and hydrocarbons. Modification of the catalyst by Pt and Mg prevents spinel formation, thereby increasing the activity of the catalysts.

Co–Mg catalysts for methane combustion were synthesized and studied, revealing the transformation of MgCo₂O₄ spinel into a CoO–MgO solid solution with oxygen release from the spinel lattice as the calcination temperature increased. Repeated heat treatment of the calcined solid solution at lower temperatures led to spinel regeneration with segregation of the solid solution phase. A TPR of the samples showed the presence of two characteristic peaks, the first of which relates to the transition of Co³⁺_Oh spinel to the Co²⁺_Oh structure of CoO, and the second to the reduction of CoO to Co°. The second peak was observed at 540–620 °C for samples calcined at temperatures below spinel decomposition, and for high-temperature samples at 900–1100 °C. Taking into account the identity of the structure of phases obtained in both cases, the formation of not a true CoO–MgO solid solution, but rather a mixture of ordered oxides (“pseudo-solid solution”) in the low-temperature region, was postulated. A study of the activity of the samples showed the high activity of the spinel systems and a linear relationship between the activation energy of methane oxidation and the heat treatment temperature.

The catalytically active vanadium-containing system of γ-Al₂O₃ was studied using a wide range of physical and chemical methods, depending on the synthesis conditions. It is shown that the vanadium-containing system includes several complexes with different thermal stabilities and catalytic activities. Low-active complexes are destroyed with the formation of more active ones based on V₂O₅ oxide, as the temperature of heat treatment increases. It can be assumed that V₂O₅ oxide has the decisive role in its catalytic activity. It was concluded that the vanadium-containing catalytic system on aluminium oxide, in the studied temperature range, is thermally stable and shows high activity not only in the reduction of nitrogen oxides but also in the oxidation of hydrocarbons (even of the most difficult ones, such as oxidizable methane). These properties of the system make it quite promising in the field of application for the purification of the exhaust gases of motor transport and industrial enterprises with environmentally harmful components, as well as for understanding the mechanism of the action of the catalysts in these processes, which is very important for solving the problems of decarbonization and achieving carbon neutrality.