This paper investigates the steady, two dimensional, and magnetohydrodynamic flow of copper and alumina/water hybrid nanofluid on a permeable exponentially shrinking surface in the presence of Joule heating, velocity slip, and thermal slip parameters. Adopting the model of Tiwari and Das, the mathematical formulation of governing partial differential equations was constructed, which was then transformed into the equivalent system of non-linear ordinary differential equations by employing exponential similarity transformation variables. The resultant system was solved numerically using the BVP4C solver in the MATLAB software. For validation purposes, the obtained numerical results were compared graphically with those in previous studies, and found to be in good agreement, as the critical points are the same up to three decimal points. Based on the numerical results, it was revealed that dual solutions exist within specific ranges of the suction and magnetic parameters. Stability analysis was performed on both solutions in order to determine which solution(s) is/are stable. The analysis indicated that only the first solution is stable. Furthermore, it was also found that the temperature increases in both solutions when the magnetic parameter and Eckert number are increased, while it reduces as the thermal slip parameter rises. Furthermore, the coefficient of skin friction and the heat transfer rate increase for the first solution when the magnetic and the suction parameters are increased. Meanwhile, no change is noticed in the boundary layer separation for the various values of the Eckert number in the heat transfer rate.

The present investigation deals with a comprehensive study on the production of aluminum based alloys with the incorporation of different alloying elements and their effect on its electrical conductivity and mechanical properties. Casting of pure aluminum with different concentration and combinations of alloying additives such as cupper (Cu), magnesium (Mg) and silver (Ag) were carried out using a graphite crucible. The as-cast microstructure was modified by hot rolling followed by different heat-treated conditions viz., annealing, normalizing, quenching, and age hardening. The mechanical properties and electrical conductivity of the produced heat-treated alloys sheets under various processing conditions were carried out using tensile testing, hardness, and electrical resistivity measurements. It was found that by increasing the alloying elements content, yield strength results increased significantly by more than 250% and 500% for the as rolled and 8 h aged Al-Cu-Mg alloy, respectively. On the other hand, the electrical conductivity reduces slightly with −14.6% and −16.57% for the as rolled and 8 h aged of the same Al-Cu-Mg alloy, respectively.

Corrosion of iron in sodium chloride (3.5% wt) solutions and its inhibition by ethanedihydrazide (EH) have been reported. Electrochemical impedance spectroscopy (EIS), cyclic potentiodynamic polarization (CPP), and change of current with time at −475 mV (Ag/AgCl) measurements were employed in this study. Scanning electron microscopy (SEM) and energy-dispersive X-ray (EDX) techniques were utilized to report surface morphology and elemental analysis, respectively. The presence of 5 × 10^–5 M EH was found to inhibit the corrosion of iron, and the effect of inhibition profoundly increased with an increase in EH concentration up to 1 × 10^–4 M and further to 5 × 10^–4 M. The low values of corrosion current and high corrosion resistance, which were obtained from the EIS, CPP, and change of current with time experiments, affirmed the adequacy of EH as a corrosion inhibitor for iron. Surface investigations demonstrated that the chloride solution without EH molecules causes severe corrosion, while the coexistence of EH within the chloride solution greatly minimizes the acuteness of chloride, particularly pitting corrosion.

This research paper presents the fabrication of epoxy coatings along with the hybrid combination of SiO₂ and ZrO₂. The epoxy resin is incorporated with SiO₂ as the primary pigment and ZrO₂ as the synergist pigment. The study delves into the adhesion, barrier, and anti-corrosion properties of these coatings, enriched with silica and zirconium nanoparticles, and investigates their impact on the final properties of the epoxy coating. The epoxy resin, a Diglycidyl ether bisphenol-A (DGEBA) type, is cured with a polyamidoamine adduct-based curing agent. To evaluate the protective performance of silica SiO₂ and zirconia ZrO₂ nanoparticles in epoxy coatings, the coated samples were tested in a 3.5% NaCl solution. The experimental results clearly demonstrate a remarkable improvement in the ultimate tensile strength (UTS), yield strength (YS), and Elastic Modulus. In comparison to using SiO₂ separately, the incorporation of both ZrO₂ and SiO₂ resulted in a substantial increase of 43.5% in UTS, 74.2% in YS, and 8.2% in Elastic Modulus. The corrosion test results revealed that the combination of DGEBA, SiO₂, and ZrO₂ significantly enhanced the anti-corrosion efficiency of the organic coatings. Both these pigments exhibited superior anti-corrosion effects and mechanical properties compared to conventional epoxy coatings, leading to a substantial increase in the anti-corrosion efficiency of the developed coating. This research focuses the potential of SiO₂ and ZrO₂ in hybrid combination for applications, where mechanical, corrosion and higher adhesion to the substrates are of prime importance.