An electrochemical amperometric ethylene sensor with solid polymer electrolyte (SPE) and semi-planar three electrode topology involving a working, pseudoreference, and counter electrode is presented. The polymer electrolyte is based on the ionic liquid 1-butyl 3-methylimidazolium bis(trifluoromethylsulfonyl)imide [BMIM][NTf₂] immobilized in a poly(vinylidene fluoride) matrix. An innovative aerosol-jet printing technique was used to deposit the gold working electrode (WE) on the solid polymer electrolyte layer to make a unique electrochemical active SPE/WE interface. The analyte, gaseous ethylene, was detected by oxidation at 800 mV vs. the platinum pseudoreference electrode. The sensor parameters such as sensitivity, response/recovery time, repeatability, hysteresis, and limits of detection and quantification were determined and their relation to the morphology and microstructure of the SPE/WE interface examined. The use of additive printing techniques for sensor preparation demonstrates the potential of polymer electrolytes with respect to the mass production of printed electrochemical gas sensors.

This article addresses reliability under the sweat of interconnection techniques for the mounting surface mounted device (SMD) components and fully printed humidity sensors onto conductive stretchable textile ribbons. Samples underwent testing for the effect of ageing by artificial sweat on their electrical resistance using both alkaline and acidic artificial sweat. The best results in terms of electrical resistance change were obtained for samples soldered to the conductive fibers interwoven in the ribbon. However, this method can damage the ribbon due to the high temperature during soldering and significantly reduce the mechanical properties and flexibility of the ribbon, which can lead to a limited service life of samples. On the other hand, adhesive bonding is a very interesting alternative, where the above-mentioned properties are preserved, but there is a significant effect of sweat ageing on electrical resistance. The results of fully printed graphene-based humidity sensors show that, for the intended use of these sensors (i.e., detection of changes in moisture on the human body), usage of the samples is possible, and the samples are sufficiently reliable in the case of sweat degradation. In addition, the response of the sensor to humidity is quite high: 98% at a relative humidity of 98%.

Nowadays, a range of sensors and actuators can be realized directly in the structure of textile substrates using metal-plated yarns, metal-filament yarns, or functionalized yarns with nanomaterials, such as nanowires, nanoparticles, or carbon materials. However, the evaluation or control circuits still depend upon the use of semiconductor components or integrated circuits, which cannot be currently implemented directly into the textiles or substituted by functionalized yarns. This study is focused on a novel thermo-compression interconnection technique intended for the realization of the electrical interconnection of SMD components or modules with textile substrates and their encapsulation in one single production step using commonly widespread cost-effective devices, such as 3D printers and heat-press machines, intended for textile applications. The realized specimens are characterized by low resistance (median 21 mΩ), linear voltage–current characteristics, and fluid-resistant encapsulation. The contact area is comprehensively analyzed and compared with the theoretical Holm’s model.

This paper presents a method for recycling and reusing SMD chip components in e-textiles using a special contacting technique. The method involves using a UV-curable, non-conductive acrylic adhesive to connect SMD components onto electrically conductive textile stretchable ribbons. At the end of the product’s life-cycle, the components are removed from the ribbon and reused to manufacture new products. The recycling procedure involves several steps, including disassembly, inspection, cleaning, repair, and reassembly of components. The results of an experiment testing the electrical resistance of new and reused components after washing and drying cycles showed that electrical resistance of reused joints did not significantly deteriorate compared to new joints. The reused components maintain their functionality and performance, suffering no significant impairment. They perform comparably to new components, even after repeated washing and drying cycles. The method offers several benefits, including conservation of raw materials, minimization of waste, and reduction of production costs. It can also help mitigate component shortages. However, it is found that the suitability of this remanufacturing method varies with different types of components. Certain component types may be more susceptible to damage or even unsuitable for this method. The method is particularly beneficial for higher-value or components experiencing market shortages, demonstrating its potential to address urgent industry challenges while contributing to environmental sustainability.