Post-consumer poly(ethylene terephthalate) (PET) waste disposal is an important task of modern industry, and the development of new PET-based value added products and methods for their production is one of the ways to solve it. Membranes for various purposes, in this regard are such products. The aim of the review, on the one hand, is to systematize the known methods of processing PET and copolyesters, highlighting their advantages and disadvantages and, on the other hand, to show what valuable membrane products could be obtained, and in what areas of the economy they can be used. Among the various approaches to the processing of PET waste, we single out chemical methods as having the greatest promise. They are divided into two large categories: (1) aimed at obtaining polyethylene terephthalate, similar in properties to the primary one, and (2) aimed at obtaining copolyesters. It is shown that among the former, glycolysis has the greatest potential, and among the latter, destruction followed by copolycondensation and interchain exchange with other polyesters, have the greatest prospects. Next, the key technologies for obtaining membranes, based on polyethylene terephthalate and copolyesters are considered: (1) ion track technology, (2) electrospinning, and (3) non-solvent induced phase separation. The methods for the additional modification of membranes to impart hydrophobicity, hydrophilicity, selective transmission of various substances, and other properties are also given. In each case, examples of the use are considered, including gas purification, water filtration, medical and food industry use, analytical and others. Promising directions for further research are highlighted, both in obtaining recycled PET-based materials, and in post-processing and modification methods.

A method for producing nanocomposites of unsaturated polyester resins (UPR) based on recycled polyethylene terephthalate (PET) as a matrix has been proposed. The upcycling method involves three successive stages: (1) oligoesters synthesis, (2) simultaneous glycolysis and interchain exchange of oligoesters with PET, (3) interaction of the obtained resins with glycol and maleic anhydride. UPRs were characterized by FTIR spectroscopy and gel permeation chromatography. The mechanical properties of nanocomposites obtained on the basis of these resins and titanium dioxide have been investigated. It has been shown that 1,2-propylene glycol units, despite their lower reactivity, significantly improve the properties of UPR. The most promising nanocomposite sample exhibited tensile strength 112.62 MPa, elongation at break 157.94%, and Young’s modulus 29.95 MPa. These results indicate that the proposed method made it possible to obtain nanocomposites with high mechanical properties based on recycled PET thus allowing one to create a valuable product from waste.

Lactide is one of the most popular and promising monomers for the synthesis of biocompatible and biodegradable polylactide and its copolymers. The goal of this work was to carry out a full cycle of polylactide production from lactic acid. Process conditions and ratios of reagents were optimized, and the key properties of the synthesized polymers were investigated. The influence of synthesis conditions and the molecular weight of lactic acid oligomers on the yield of lactide was studied. Lactide polymerization was first carried out in a 500 mL flask and then scaled up and carried out in a 2000 mL laboratory reactor setup with a combined extruder. Initially, the lactic acid solution was concentrated to remove free water; then, the oligomerization and synthesis of lactide were carried out in one flask in the presence of various concentrations of tin octoate catalyst at temperatures from 150 to 210 °C. The yield of lactide was 67–69%. The resulting raw lactide was purified by recrystallization in solvents. The yield of lactide after recrystallization in butyl acetate (selected as the optimal solvent for laboratory purification) was 41.4%. Further, the polymerization of lactide was carried out in a reactor unit at a tin octoate catalyst concentration of 500 ppm. Conversion was 95%; Mw = 228 kDa; and PDI = 1.94. The resulting products were studied by differential scanning calorimetry, NMR spectroscopy and gel permeation chromatography. The resulting polylactide in the form of pellets was obtained using an extruder and a pelletizer.

A new method for the recycling of a polyester tire cord under the action of oligoethylene terephthalates, bis(2-hydroxyethyl) terephthalate and ethylene glycol has been proposed. The method involves simultaneous homogeneous glycolysis of polyethylene terephthalate and devulcanization of crumb rubber. Polyester cord and glycolysates were characterized by FTIR spectroscopy and gel permeation chromatography (GPC). The devulcanization process was investigated by swelling-based methods. The rate of the proposed method of homogeneous glycolysis in a melt phase was proved to be higher than one of the heterogeneous glycolysis. The assumption of a more efficient devulcanization in the presence of a softener was also confirmed. The degree of devulcanization 46.07%, the apparent degree of swelling 167.4%, and the apparent swelling rate constant 0.0902 min⁻¹ were achieved. The results indicate that the proposed method made it possible to carry out the glycolysis of the polyester cord of the tire more deeply than the known heterogeneous glycolysis with various agents, but further research is needed for industrial implementation.

The review summarizes recent advances in the production of carbon fiber precursors based on melt-spun acrylonitrile copolymers. Approaches to decrease the melting point of polyacrylonitrile and acrylonitrile copolymers are analyzed, including copolymerization with inert comonomers, plasticization by various solvents and additives, among them the eco-friendly ways to use the carbon dioxide and ionic liquids. The methods for preliminary modification of precursors that provides the thermal oxidative stabilization of the fibers without their melting and the reduction in the stabilization duration without the loss of the mechanical characteristics of the fibers are discussed. Special attention is paid to different ways of crosslinking by irradiation with different sources. Examples of the carbon fibers preparation from melt-processable acrylonitrile copolymers are considered in detail. A patent search was carried out and the information on the methods for producing carbon fibers from precursors based on melt-spun acrylonitrile copolymers are summarized.

The influence of introducing acrylic acid (AA) into the reaction mixture with acrylonitrile at the synthesis of copolymers by free-radical polymerization (FRP) and radical polymerization with reversible addition–fragmentation chain transfer (RAFT) on the rheological properties of their solutions in dimethyl sulfoxide, as well as on the capability to spin fibers by the mechanotropic method, is analyzed. The influence of AA dosing conditions on the rheological properties of the solutions in the concentration range above the crossover point was not revealed. In the case of RAFT synthesis, the rheological properties differ distinctively in the high concentration region that is expressed by unusual viscoelastic characteristics. Dilute solution viscometry revealed the influence of the comonomer loading order on the interaction intensity of the copolymer macromolecules with a solvent, which is more pronounced for samples synthesized by FRP and can be associated with the copolymers’ molecular structure. Fiber spinning from solutions of polyacrylonitrile and its copolymers (PAN) synthesized by the RAFT method was not able to achieve a high degree of orientation drawing, while for polymers with a wider molecular weight distribution synthesized by FRP, it was possible to realize large stretches, which led to high-quality fibers with strength values up to 640 MPa and elongation at a break of 20%.