In recent years, bio-based wood adhesives have gained an increased industrial and research interest as an environmentally friendly and renewable alternative to the commercial petroleum-based synthetic adhesives used in the wood-based industry. Due to its renewability, abundance, relatively low price, and good adhesion properties, starch is a promising natural feedstock for synthesizing bio-based adhesives for wood-based composites. This review aims to summarize the recent advances in developing sustainable starch-based wood adhesives for manufacturing non-toxic, low-emission wood composites with enhanced properties and lower environmental impact. Recent developments in starch modification, physical, and enzymatic treatments applied to improve the performance of starch-based wood adhesives, mainly in terms of improving their water resistance and bonding strength, are also outlined and discussed.

The need to produce an ever-increasing quantity of material products and food resulting from the planet globalization process has contributed to the spread of modern agriculture based on a linear production resulting in the generation of tons of waste. This huge amount of waste is generally accumulated in landfills, causing different environmental problems. Hence, researchers moved on to study the processes used to recover agro-industrial by-products within a circular and sustainable bio-economy concept. A systematic quest on Scopus and PubMed databases was performed to identify the data available to date on recycling agro-industrial by-products of Olea europaea L. This systematic review summarizes the knowledge regarding the use of olive trees by-products for producing animal feed, biocomposites, bioethanol, cellulose pulp, activated carbon, and as a fuel source for energy production. Furthermore, the data regarding the potential biological activity of extracts from olive roots, wood, bark, and pruning were analyzed. Olive trees by-products are, indeed, rich in molecules with antioxidant, antimicrobial, cardioprotective, and anticancer activity, representing a promising candidate for treat several human diseases.

Extensive research projects have been carried out on thermal modification of wood material, yet thermal properties of thermally modified poplar wood have not been comprehensively investigated. Black poplar (Populus nigra L.) is a Eurasian species native to Italy which is rarely used for the production of high-performance products, though it is one of the least expensive hardwoods on the market. To explore alternative applications of poplar wood such as building facade or fire resistance materials, reliable data of thermal behaviour of thermally modified wood at high temperatures are needed. In this work, the thermal behaviour of native black poplar wood after thermal modification at different temperatures (180 °C, 200 °C and 220 °C) was analyzed. Thermal conductivity, thermal diffusivity and porosity were measured on poplar wood boards, as well as mass loss and wood color changes after heat treatment were quantified. Thermal conductivity of wood samples showed significant changes after treatment at 200 and 220 °C, but not at 180 °C. Wood porosity showed significant differences with the control when the samples were modified at a temperature of 220 °C. Increasing color differences were observed in wood samples by increasing the thermal modification temperature. Also, the mass loss of wood samples increased and equilibrium moisture content significantly dropped down after thermal modification. Our results showed that the use of thermally-modified black poplar wood could be considered as a viable alternative to chemically treated wood products for specific applications where high insulation is needed, such as saunas or windows, and for façades elements.

The objective of this work was to investigate the selected properties of particleboard (PB) containing waste rubber – a mixture of carpets and isolators (GWR) and tires (GWT) from discarded automobiles. Mechanical (tensile strength (IB), bending strength (BS), physical (water absorption (WA), thickness swelling (TS) after 2 and 24 h of immersion), chemical (volatile compounds - VOC using GC-MS method), thermo-physical (thermal conductivity and diffusivity, specific heat capacity) and sound absorption coefficient were analyzed. In addition, a density profile and microscopic analysis of the particleboards were performed. The addition of 10% rubber to the PB either maintains the IB or improves the BS of the composite. The best results for WA after 24 h (97.94%) and TS after 24 h (30.74%) were achieved for composites containing tire granulates. For this reason, these PBs are the most suitable for utilization in areas with higher humidity. Adding 20% of GWR to PB decreased the total content of VOC emissions by 85% so it can be stated that the rubber probably acts as a VOC sorbent. Control PBs had significantly lower thermal conductivity and diffusivity, and comparable specific heat capacity values than PBs containing GWR and GWT. The best sound insulation properties were obtained for PBs containing 20% of GWR. Microscopic analysis pointed to greater GWT and GWR contents resulting in higher C content in the PB. All PBs containing GWR have a higher mean density compared to that of control, ranging from 597 kg·m⁻³ to 615 kg·m⁻³. On the other hand, PB containing GWT had comparable or lower density values.

The aim of this research was to evaluate the multiple effects of both thermal modification and alkyl ketene dimer (AKD) on the deodar cedar (Cedrus deodara Roxb.) wood surface, before and after an irradiation test. The physical and chemical changes that occurred on the cedar wood samples due to the combined effect of these modifications were evaluated by measuring their wettability and colour and using attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR) and X-ray photoelectron spectroscopy (XPS) analyses. The surface analysis by XPS showed the expected variability among the sampled layers for unmodified and thermally modified cedar wood samples and a uniform composition after the AKD coverage, regardless of their pre-treatments. The FTIR spectra before the irradiation test showed that the hydrophobicity of the samples was ensured by the formation of carbonyl groups originating from the reaction between the AKD and hydroxyl groups of cellulose, which is related to the presence of the absorption band between 1700 cm⁻¹ and 1750 cm⁻¹. Markedly, after the irradiation test, a degradation of the amorphous cellulose component occurred, showing that photoisomerisation to the enolic form took place. Overall, although uniform AKD coverage was derived from the surface analysis and wetting test, the combined ATR-FTIR results and colour measurements showed that it could not provide permanent protection to the underlying wood structure due to its own tendency to degrade mainly in colour over time, under the action of UV rays and atmospheric agents.

The sweet chestnut (Castanea sativa Mill.) and European beech (Fagus sylvatica L.) are wood species largely present in the European forest area. The composition and relative variation of the secondary metabolites of chestnut and European beech wood under thermal effect is a little-explored area. The wood material was thermally modified at 170 °C for 3 h using a thermo-vacuum technology. Raw and modified wood extracts were obtained with aqueous extraction techniques in an autoclave, subsequently lyophilized, solubilized in ethyl acetate, and determined by Gas Chromatographic-Mass Spectrometric Analyses (GC-MS). In addition, the volatile compounds were determined by Solid-Phase Micro Extraction (SPME) analyses. As a general statement, the extraction in an autoclave produced a higher number of compounds in the modified chestnut and beech wood compared to unmodified wood material. Beech wood showed low degradation in the compounds after modification. Notably, squalene and ar-tumerone were the main bioactive compounds present in beech wood extractives. Chestnut, conversely, showed a greater degradation after thermo-modification. However, a reduction in chemical compounds in the modified samples was also observed. In this case, the main biologically active compounds detected only in the chestnut control samples were apocynin and ar-tumerone. The recovery of this residual wood material, before energy consumption, could provide a sustainable and environmentally friendly means of obtaining natural chemicals suitable for various industrial applications.