This study investigated the effect of hemp fiber pretreatments (water and sodium hydroxide) combined with silane treatment, first on the fiber properties (microscale) and then on polylactide (PLA) composite properties (macroscale). At the microscale, Fourier transform infrared, thermogravimetric analysis, and scanning electron microscopy investigations highlighted structural alterations in the fibers, with the removal of targeted components and rearrangement in the cell wall. These structural changes influenced unitary fiber properties. At the macroscale, both pretreatments increased the composites’ tensile properties, despite their negative impact on fiber performance. Additionally, silane treatment improved composite performance thanks to higher performance of the fibers themselves and improved fiber compatibility with the PLA matrix brought on by the silane couplings. PLA composites reinforced by 30 wt.% alkali and silane treated hemp fibers exhibited the highest tensile strength (62 MPa), flexural strength (113 MPa), and Young’s modulus (7.6 GPa). Overall, the paper demonstrates the applicability of locally grown, frost-retted hemp fibers for the development of bio-based composites with low density (1.13 to 1.23 g cm⁻³).

In this paper the study of recycling technology for production of refuse derived fuel (RDF) is described. Various types of wastes (wood, carton, paper, plastic and textile) were pro­cessed by two-shaft and single-shaft shredders to obtain the output product (1–2 mm), which is suitable for briquetting process. For samples manufacturing the briquetting equipment developed at Slovak University of Technology in Bratislava was used. Technological test showed that by briquet­ting of the municipal waste higher pressing temperature and compacting pressure should be applied. For quality evaluation of the manufactured briquettes the density and strength properties were determined. The mechanical strength of briquettes from RDF increased after mixing it with wood and paper wastes. The influence of different parameters (fraction size, moisture content, compacting pressure and temperature) to briquette quality was studied. To determine the calorific value of the briquetting stock the tests in the chemical laboratory of the Department of Thermal Engineering of TUT were performed.

The effects of surface pretreatment (water and alkali) and modification with silane on moisture sorption, water resistance, and reaction to fire of hemp fiber reinforced polylactic acid (PLA) composites at two fiber loading contents (30 and 50 wt.%) are investigated in this work. Moisture adsorption was evaluated at 30, 50, 75 and 95% relative humidity, and water resistance was determined after a 28-day immersion period. The cone calorimetry technique was used to investigate response to fire. The fiber surface treatment resulted in the removal of cell wall components, which increased fiber individualization and homogeneity as shown in scanning microscopic pictures of the composite cross-section. Although the improved fiber/matrix bonding increased the composite’s water resistance, the different fiber treatments generated equal moisture adsorption results for the 30 wt.% reinforced composites. Overall, increasing the fiber amount from 30 to 50 wt.% increased the composite sensitivity to moisture/water, mainly due to the availability of more hydroxyl groups and to the development of a higher pore volume, but fire protection improved due to a reduction in the rate of thermal degradation induced by the reduced PLA content. The new Oswin’s model predicted the composite adsorption isotherm well. The 30 wt.% alkali and silane treated hemp fiber composite had the lowest overall adsorption (9%) while the 50 wt.% variant produced the highest ignition temperature (181 ± 18 °C).

In Estonia, hardwoods form approximately 50% of all forest area, where the main species are birch (30%), gray alder (9%), aspen (6%) and black alder (4%). Birch has been extensively used by the veneer-based industry, but species like black alder, gray alder and aspen have not been commonly used by the veneer-based products industry due to the lower quality of this resource. The aim of this research is to determine the effect of different lay-up schemes and usages of gray alder, black alder and aspen on the mechanical properties of plywood, by replacing birch veneer in the plywood core with alternative wood species. The main veneer and plywood characteristics will be evaluated according to the current standards, e.g., veneer strength perpendicular to grain, plywood bonding and bending strength, and modulus of elasticity. All processing parameters will be kept similar to those used generally by birch plywood manufacturers. The results showed that birch and black alder plywood panels had generally the highest bending strength properties, followed by grey alder and aspen. It was also found that, for proper gluing, birch veneers had the lowest glue consumption, 152 g/m², and aspen had the highest glue consumption, 179 g/m². It was found that when lower density wood was used in the plywood, the product density increased. Low density wood veneers had higher glue consumption, and also higher compaction in thickness than birch veneers under the same pressure. Overall, it was shown that the wood species used in this study have slightly lower strength properties, but with proper lay-up schemes, these wood species could be successfully used by the veneer-based products industry.

The goal of the study was to find a cost-effective composition of a particle reinforced composite that is light in weight but has sufficient mechanical properties. The matrix of the particulate composite is unsaturated polyester resin that is reinforced with alumina trihydrate particles. Part of the alumina trihydrate proportion was replaced with hollow glass microspheres to reduce weight and save costs. In order to find out the influence of the light filler on the physical and mechanical properties of composites, materials with different percentages of the light filler were prepared. Test specimens were cut from moulded sheets that were fabricated with vacuum assisted extruder. Tensile strength, indentation hardness measured with a Barcol impressor, and density were determined. Based on the experimental data a multi-criteria optimization problem was formulated and solved to find the optimal design of the material. Artificial neural networks and a hybrid genetic algorithm were used. The optimal solution is given as a Pareto curve to represent the distinction between the density and selected mechanical properties of the composite material. The composite material filled with 6% hollow glass microspheres showed 3% loss in the tensile strength and 26% loss in the surface hardness compared to the composition without the filler. The weight decreased by 13% compared with the initial composition. The addition of hollow glass microspheres did not lower the net value of the material, it increased 7%.

This research investigates an effective alkali (NaOH) treatment and fire-retardant coating to produce biocomposites from frost-retted hemp fiber and PLA. The fiber surface treatment with various NaOH concentrations was investigated throughout a range of soaking times. The results show that the extracted non-cellulosic fiber content increases with treatment duration and NaOH concentration, while the fraction of targeted components removed remains nearly unchanged after soaking for 1, 2, and 4 h with a 5 wt.% NaOH solution. At the composite level, the treatment with 5 wt.% NaOH solution for 1 h emerged as the most efficient, with tensile strength, Young’s modulus, flexural strength, and flexural modulus of 89.6 MPa, 9.1 GPa, 121.6 MPa, and 9.6 GPa, respectively, using 30 wt.% fibrous reinforcement. The fire performance of the examined batches of biocomposites improved significantly with the novel fire-retardant (Palonot F1) coating. However, the tensile strength notably decreased, while the flexural properties showed only a slight reduction. In most cases, the biocomposites with the alkali-treated hemp fiber had delayed ignition during the 5 min exposure to the cone heater. The findings in this work contribute to studies that will be required to give design guidelines for sustainable building options.