The article presents the continuation of the research on modification of fibrous carriers based on poly(lactic acid) using the electrophoretic deposition (EPD) method by the two types of biocompatible polymers—sodium hyaluronate and sodium alginate. Such modified nonwovens, differing in the structural parameters due to different manufacturing methods, could be potentially used in different biomedical applications. The results of the analysis indicate that the EPD process significantly changes the structural characteristics of the carrier in terms of thickness and porosity, which not always can be beneficial in terms of the final application. The varying structure of both carriers significantly influences the mode of deposition of the layer, the efficiency of the deposition process as well as the structural characteristics of the carrier after deposition. Microtomographic and SEM studies were employed to analyze the structure of deposits, and FTIR analysis allowed for confirmation of the occurrence of the polymer layers and its chemical structure.

The growth of population and increase in diseases that cause an enormous demand for biomedical material consumption is a pointer to the pressing need to develop new sustainable biomaterials. Electrospun materials derived from green polymers have gained popularity in recent years for biomedical applications such as tissue engineering, wound dressings, and drug delivery. Among the various bioengineering materials used in the synthesis of a biodegradable polymer, poly(lactic acid) (PLA) has received the most attention from researchers. Hypericum perforatum oil (HPO) has antimicrobial activity against a variety of bacteria. This study aimed to investigate the development of an antibacterial sustainable material based on PLA by incorporating HPO via a simple, low-cost electrospinning method. Chemical, morphological, thermal, thickness and, air permeability properties, and in vitro antibacterial activity of the electrospun nonwoven fabric were investigated. Scanning electron microscopy (SEM) was used to examine the morphology of the electrospun nonwoven fabric, which had bead-free morphology ultrafine fibers. Antibacterial tests revealed that the Hypericum perforatum oil-loaded poly(lactic acid) nonwoven fabrics obtained had high antibacterial efficiency against Escherichia coli and Staphylococcus aureus, indicating a strong potential for use in biomedical applications.

Literature reviews have described the applications of silver, copper, and zinc ions and metallic particles of Cu, Ti, and Zn oxides, which have been found to be useful antimicrobial reagents for the biofunctionalization of various materials and their surfaces. For this purpose, compositions of water dispersions containing emulsions of synthetic copolymers based on acrylic and vinyl monomers, polysaccharides (hydroxyethyl cellulose and starch), and various additives with wetting and stabilizing properties were used. Many stable water dispersions of different chemical compositions containing bioactive chemical compounds (copper silicate hydrate, titanium dioxide, and zinc oxide (and other auxiliary substances)) were developed. They were used for the preparation of thin hybrid coatings having good antimicrobial properties against Gram-negative bacteria (Escherichia coli), Gram-positive bacteria (Staphylococcus aureus), and yeast fungus (Candida albicans). Polyester (PES) and polylactide (PLA) nonwovens were modified using the dip-coating method, while PES and cotton fabrics were biofunctionalized by means of dip-coating and coating methods. The antimicrobial (antibacterial and antifungal) properties of the textile materials (nonwovens and fabrics) biofunctionalized with the above-mentioned bioactive agents exhibiting antimicrobial properties (CuSiO₃, TiO₂, ZnO, or ZnO∙SiO₂) were strongly dependent on the agents’ content in the water dispersions. The PES and PLA nonwovens, modified on the surface with water compositions containing copper silicate hydrate, showed good antibacterial properties against the Gram-negative bacteria Escherichia coli, even at a content of 1 wt.% CuSiO₃∙xH₂O, and against the Gram-positive bacteria Staphylococcus aureus, at the content of at least 5 wt.% CuSiO₃∙xH₂O. The bacterial growth reduction factor (R) was greater than 99% for most of the samples tested. Good antifungal properties against the fungus Candida albicans were found for the PES and PLA nonwoven fabrics modified with dispersions containing 5–7 wt.% CuSiO₃∙xH₂O and 4.2–5.0 wt.% TiO₂. The addition of TiO₂ led to a significant improvement in the antifungal properties of the PES and PLA nonwovens modified in this way. For the samples of PES WIFP-270 and FS F-5 nonwovens, modified with water dispersions containing 5.0 wt.% CuSiO₃∙xH₂O and 4.2–5.0 wt.% TiO₂, the growth reduction factor for the fungus Candida albicans (R) reached values in the range of 80.9–98.0%. These new biofunctionalized polymeric nonwoven textile materials can find practical applications in the manufacture of filters for hospital air-conditioning systems and for the automotive industry, as well as in air purification devices. Moreover, similar antimicrobial modification of fabrics with the dip-coating or coating methods can be applied, for example, in the fabrication of fungi- and mold-resistant garden furniture.

The COVID-19 pandemic was first reported on 31 December 2019, in Wuhan. Since then, the rapid spread of the virus has directly impacted various aspects of people’s lives, including culture, society, education, and the economy. The environment has also been affected, as the disposal of thousands of tons of single-use personal protective equipment has resulted in a significant increase in waste. The challenge was to create environmentally friendly materials for personal protective equipment. One of the alternatives to polypropylene materials is a biodegradable nonwoven produced using spun-bonded technology. The article discusses various physical and mechanical parameters, the biodegradation process, and the distribution of molar masses during the weeks of nonwoven biodegradation. Additionally, the paper presents the results of in vitro cytotoxicity tests conducted on the material. Biodegradable materials are a viable solution to the challenges posed by a circular economy.

Hyaluronate and alginate are non-toxic and biocompatible polymers, which can be used for surface modification and functionalization of many kinds of materials. Electrophoretic deposition (EPD) has several advantages, including its versatility, simplicity, and ability to coat substrates with complex shapes, and is used for the creation of antimicrobial or hydrophobic coatings on metallic biomaterials, among other applications. However, its utilization for applying biopolymer layers on textiles is very limited due to the more complex structure and spatial characteristics of fibrous materials. The aim of this research was to analyze the effects of selected EPD process parameters and the structural characteristics of fibrous carriers on the kinetics of the process and the microscopic characteristics of the deposited layers. The influence of solution characteristics, process parameters, and carrier structures obtained using two different techniques (melt blown and spun-bonded) were analyzed. The morphology and structure of the created deposits were analyzed using scanning electron microscopy and computed tomography, and molecular structure analysis was performed with Fourier Transform Infrared spectroscopy. The surface mass and thickness of fibrous poly (lactic acid)-based carriers were analyzed in accordance with the respective standards. This study serves as a basis for discussion and further development of this method with regard to fibrous materials for medical applications.

New scaffold materials composed of biodegradable components are of great interest in regenerative medicine. These materials should be: stable, nontoxic, and biodegrade slowly and steadily, allowing the stable release of biodegradable and biologically active substances. We analyzed peptide-polysaccharide conjugates derived from peptides containing RGD motif (H-RGDS-OH (1), H-GRGDS-NH₂ (2), and cyclo(RGDfC) (3)) and polysaccharides as scaffolds to select the most appropriate biomaterials for application in regenerative medicine. Based on the results of MTT and Ki-67 assays, we can state that the conjugates containing calcium alginate and the ternary nonwoven material were the most supportive of muscle tissue regeneration. Scanning electron microscopy imaging and light microscopy studies with hematoxylin–eosin staining showed that C2C12 cells were able to interact with the tested peptide–polysaccharide conjugates. The release factor (Q) varied depending on both the peptide and the structure of the polysaccharide matrix. LDH, Alamarblue^®, Ki-67, and cell cycle assays indicated that peptides 1 and 2 were characterized by the best biological properties. Conjugates containing chitosan and the ternary polysaccharide nonwoven with peptide 1 exhibited very high antibacterial activity against Staphylococcus aureus and Klebsiella pneumoniae. Overall, the results of the study suggested that polysaccharide conjugates with peptides 1 and 2 can be potentially used in regenerative medicine.