In this report, the synthesis of poly(ω-pentadecalactone) (PPDL) (co)polymers and their incorporation into polyurethanes (PUs) are reported. Optimal conditions for the ring-opening polymerization (ROP) of ω-pentadecalactone (PDL) using dibutyltin dilaurate catalyst were established. For the synthesis of linear and crosslinked PUs, 50 kDa poly(ε-caprolactone) (PCL) and 1,6-hexamethylenediisocyanate (HDI) were used. The obtained polyurethanes were characterized by Attenuated Total Reflectance Fourier-Transform Infrared spectroscopy (AT-FTIR), differential scanning calorimetry (DSC), and dynamical mechanical analysis (DMA). The DMA of the selected sample showed a rubbery plateau on the storage modulus versus temperature curve predicting shape memory behavior. Indeed, good shape memory performances were obtained with shape fixity (R_f) and shape recovery (R_r) ratios.

In this paper, the synthesis, characterization, and properties of crosslinked poly(ε-caprolactone)-based polyurethanes as potential tissue replacement materials are reported. The polyurethane prepolymers were prepared from poly(ε-caprolactone)diol (PCD), polyethylene glycol (PEG)/polylactic acid diol (PLAD), and 1,6-hexamethylene diisocyanate (HDI). In these segmented polyurethanes, the role of PEG/PLAD was to tune the hydrophobic/hydrophilic character of the resulting polymer while sucrose served as a crosslinking agent. PLAD was synthesized by the polycondensation reaction of D,L-lactic acid and investigated by matrix-assisted laser desorption/ionization time-of-flight mass spectrometry (MALDI-TOF MS) and nuclear magnetic resonance spectroscopy (NMR). The crosslinked polyurethane samples (SUPURs) obtained were characterized by attenuated total reflectance Fourier-transform infrared spectroscopy (AT-FT-IR), swelling, and mechanical (uniaxial tensile tests) experiments. The thermo and thermomechanical behavior were studied by differential scanning calorimetry (DSC) and dynamical mechanical analysis (DMA). The viability of dental pulp stem cells was investigated in the case of polyurethanes composed of fully biocompatible elements. In our studies, none of our polymers showed toxicity to stem cells (DPSCs).

Sucrose-1,6-hexamethylene diisocyanate (HDI) cooligomers were synthesized and used as new polyols for poly(ε-caprolactone) (PCL)-based polyurethanes. The polyaddition reaction of sucrose and HDI was monitored by MALDI-TOF MS. It was found that by selecting appropriate reaction conditions, mostly linear oligomer chains containing 16 sucrose units could be obtained. For the synthesis of polyurethane networks, prepolymers were prepared by the reaction of poly(ε-caprolactone) (PCL, 10 kg/mol) with HDI or 4,4′-methylene diphenyl diisocyanate (MDI) and were reacted with sucrose-HDI cooligomers. The so-obtained sucrose-containing polyurethanes were characterized by means of attenuated total reflectance Fourier-transform infrared spectroscopy (ATR-FT IR), swelling, mechanical (uniaxial tensile tests) and differential scanning calorimetry (DSC).