Additive manufacturing technology and its benefits have a significant impact on different industrial applications. The 3D printing technologies help manufacture lightweight intricate geometrical designs with enhanced strengths. The present study investigates the blended effects of previously recommended parameters of different infill patterns (line, triangle, and concentric) and infill densities (75, 80, and 85%) with varying thicknesses of layers (100, 200, and 300 μm). The test samples were created through Fused Filament Fabrication (FFF) technology using Acrylonitrile Butadiene Styrene (ABS) 3D printing. Mechanical properties were evaluated through tensile and impact strength tests conducted in accordance with ASTM standards. The experimental investigation reveals that the infill pattern greatly affected both tensile and impact strength. The best results were obtained with a concentric infill pattern, along with 80% infill density and 100 μm layer thickness. These conditions resulted in 123% and 115% higher tensile strength and 168% and 80% higher impact strength compared to line and triangle patterns, respectively.

In recent times, demand for light weight and high strength materials fabricated from natural fibres has increased tremendously. The use of natural fibres has rapidly increased due to their high availability, low density, and renewable capability over synthetic fibre. Natural leaf fibres are easy to extract from the plant (retting process is easy), which offers high stiffness, less energy consumption, less health risk, environment friendly, and better insulation property than the synthetic fibre-based composite. Natural leaf fibre composites have low machining wear with low cost and excellent performance in engineering applications, and hence established as superior reinforcing materials compared to other plant fibres. In this review, the physical and mechanical properties of different natural leaf fibre-based composites are addressed. The influences of fibre loading and fibre length on mechanical properties are discussed for different matrices-based composite materials. The surface modifications of natural fibre also play a crucial role in improving physical and mechanical properties regarding composite materials due to improved fibre/matrix adhesion. Additionally, the present review also deals with the effect of silane-treated leaf fibre-reinforced thermoset composite, which play an important role in enhancing the mechanical and physical properties of the composites.

In this study, experiments are performed to study the physical and mechanical behaviour of chemically-treated sugarcane bagasse fibre-reinforced epoxy composite. The effect of alkali treatment, fibre varieties, and fibre lengths on physical and mechanical properties of the composites is studied. To study the morphology of the fractured composites, scanning electron microscopy is performed over fractured composite surfaces. The study found that the variety and lengths of fibres significantly influence the physical and mechanical properties of the sugarcane bagasse-reinforced composites. From the wear study, it is found that the composite fabricated from smaller fibre lengths show low wear. The chemically-treated bagasse-reinforced composites fabricated in this study show good physical and mechanical properties and are, therefore, proposed for use in applications in place of conventional natural fibres.

The main focus of the present research work was to explore mechanical and tribological properties of Himalayan nettle fiber and unsaturated polyester resin (GP) using hand lay-up method. Four composite laminates were prepared by adding the Himalayan nettle fibers by weight percentage (5%–20%). The various properties (e.g., tensile strength, hardness, impact strength, and abrasion wear) were calculated for the composite laminates. It was found that the significant variation in properties was observed when fiber addition was in the range 15%. The change in the properties was negligible when fiber addition was increased from 15% by weight.