Zinc oxide layers on soda-lime glass substrates were fabricated using the sol-gel method and the dip-coating technique. Zinc acetate dihydrate was applied as the precursor, while diethanolamine as the stabilizing agent. This study aimed to determine what effect has the duration of the sol aging process on the properties of fabricated ZnO films. Investigations were carried out with the sol that was aged during the period from 2 to 64 days. The sol was studied using the dynamic light scattering method to determine its distribution of molecule size. The properties of ZnO layers were studied using the following methods: scanning electron microscopy, atomic force microscopy, transmission and reflection spectroscopy in the UV-Vis range, and the goniometric method for determination of the water contact angle. Furthermore, photocatalytic properties of ZnO layers were studied by the observation and quantification of the methylene blue dye degradation in an aqueous solution under UV illumination. Our studies showed that ZnO layers have grain structure, and their physical–chemical properties depend on the duration of aging. The strongest photocatalytic activity was observed for layers produced from the sol that was aged over 30 days. These layers have also the greatest porosity (37.1%) and the largest water contact angle (68.53°). Our studies have also shown that there are two absorption bands in studied ZnO layers, and values of optical energy band gaps determined from positions of maxima in reflectance characteristics are equal to those determined using the Tauc method. Optical energy band gaps of the ZnO layer fabricated from the sol aged over 30 days are E_g^I = 4.485 eV and E_g^II = 3.300 eV for the first and second bands, respectively. This layer also showed the highest photocatalytic activity, causing the pollution to degrade 79.5% after 120 min of UV irradiation. We believe that ZnO layers presented here, thanks to their attractive photocatalytic properties, may find application in environmental protection for the degradation of organic pollutants.

Purpose: – The paper aims to present results of investigations carried out on the front electrode of the solar cell. The front-side electrode for solar cells based on crystalline material is obtained by the screen printing method. Screen printing has been the prevailing method of electrode deposition because of its low cost. One of the ways to improve the cell efficiency and reduce the production costs is a further refinement of the metal electrode screen printing process. Design/methodology/approach: – The researches were focused on the modification of mechanical parameters of screen printing process to ensure the best possible cross-section of the front electrode geometry. The main printing process parameters were constant, however, the print speed was variable. The obtained fine line of front contact was characterized morphologically – the dimension and geometry of the front contact cross-section – by scanning electron microscopy technique. Findings: – The thin paths of 100 μm in width were screen printed applying a new silver-paste made by Du Pont. The printing speed has significant effect on print quality in the way that the lower speed enhanced the printed results. Research limitations/implications: – For newest pastes (e.g. PV17D) influence of screen printing parameters on the front metallic electrodes geometry of solar cell is not so significant. Presented screen printing process can still give good results, but the further optimization for the new paste must be performed to achieve better cross-section geometry. Originality/value: – This paper confirms that one-step screen printing process can still give good results. The screen printed thin paths of 100 μm in width have good cross-section aspect ratio.