Metallic foam is a popular topic due to its diverse industrial applications and unique combination of properties. Metallic foam is significantly lighter than nonfoam metal materials due to its porous structure, which incorporates a substantial amount of air or voids. This lower density makes metallic foam advantageous in applications in which weight reduction is critical. This makes it ideal for the aerospace, automotive, and construction industries; also, its versatile nature continues to make it an attractive material for various industrial applications such as impact absorbers, heat exchangers, and biomedical and marine engineering. However, the choice between metallic foam and nonfoam metal also depends on other factors like mechanical properties, cost, and specific application requirements. This review describes various fabrication methods of metallic foam that include the liquid metallurgy route which uses liquid or semiliquid metal, the powder metallurgy route uses metal in powder form, metal ion, and the metal vapor route which uses electrolytic deposition method to produce metallic foam. These methods include direct gas injection, adding blowing agents in solid or liquid metals, investment casting, the addition of a space holder in the precursor, metallic ion, vapor deposition on a polymer sponge, and many more. The morphology of metallic foam depends upon the method that is chosen for fabrication, and up to 98% porosity can be achieved by these methods. Additive manufacturing for metallic foam fabrication is an emerging field based on selective laser melting and electron beam melting principles. It has exceptional possibilities for generating complicated 3D shapes and customizing the material characteristics. The main purpose of this review article is to give significant insights into the various production procedures for metallic foams to researchers, engineers, and industry experts, assisting in the selection of acceptable methods depending on individual application needs. This review investigates the manufacturing conditions for metallic foams and finally discusses their advantages, drawbacks, and obstacles in mass production. The findings add to current efforts to expand metallic foam technology and encourage its wider application across diverse sectors, opening the path for future research and development.

Bio-char has the ability to isolate carbon in soils and concurrently improve plant growth and soil quality, high energy density and also it can be used as an adsorbent for water treatment. In the current work, the characteristics of four different types of bio-chars, obtained from slow pyrolysis at 375 °C, produced from hard-, medium-, thin- and paper-shelled walnut residues have been studied. Bio-char properties such as proximate, ultimate analysis, heating values, surface area, pH values, thermal degradation behavior, morphological and crystalline nature and functional characterization using FTIR were determined. The pyrolytic behavior of bio-char is studied using thermogravimetric analysis (TGA) in an oxidizing atmosphere. SEM analysis confirmed morphological change and showed heterogeneous and rough texture structure. Crystalline nature of the bio-chars is established by X-ray powder diffraction (XRD) analysis. The maximum higher heating values (HHV), high fixed carbon content and surface area obtained for walnut shells (WS) samples are found as ~ 18.4 MJ kg⁻¹, >80% and 58 m²/g, respectively. Improvement in HHV and decrease of O/C and H/C ratios lead the bio-char samples to fall into the category of coal and confirmed their hydrophobic, carbonized and aromatized nature. From the Fourier transform infra-red spectroscopy (FTIR), it is observed that there is alteration in functional groups with increase in temperature, and illustrated higher aromaticity. This showed that bio-chars have high potential to be used as solid fuel either for direct combustion or for thermal conversion processes in boilers, kilns and furnace. Further, from surface area and pH analysis of bio-chars, it is found that WS bio-chars have similar characteristics of adsorbents used for water purifications, retention of essential elements in soil and carbon sequestration.

Artificial implants are very essential for the disabled as they are utilized for bone and joint function in orthopedics. However, materials used in such implants suffer from restricted mechanical and tribological properties besides the difficulty of using such materials with complex structures. The current study works on developing a new polymer green composite that can be used for artificial implants and allow design flexibility through its usage with 3D printing technology. Therefore, a natural filler extracted from corn cob (CC) was prepared, mixed homogeneously with the Polylactic-acid (PLA), and passed through a complete process to produce a green composite filament suit 3D printer. The corn cob particles were incorporated with PLA with different weight fractions zero, 5%, 10%, 15%, and 20%. The physical, mechanical, and tribological properties of the PLA-CC composites were evaluated. 3D finite element models were constructed to evaluate the PLA-CC composites performance on a real condition implant, hip joints, and through the frictional process. Incorporating corn cob inside PLA revealed an enhancement in the hardness (10%), stiffness (6%), compression ultimate strength (12%), and wear resistance (150%) of the proposed PLA-CC composite. The finite element results of both models proved an enhancement in the load-carrying capacity of the composite. The finite element results came in line with the experimental results.

Epoxy is considered to be the most popular polymer and is widely used in various engineering applications. However, environmental considerations require natural materials-based epoxy. This necessity results in further utilization of natural materials as a natural reinforcement for different types of composites. Corn cob is an example of a natural material that can be considered as an agricultural waste. The objective of the present work is to improve the economic feasibility of corn cob by converting the original corn cob material into powder to be utilized in reinforcing epoxy-based composites. In the experiment, the corn cob was crushed and ground using a grain miller before it was characterized by scanning electron microscopy (SEM). The corn cob powder was added to the epoxy with different weight fractions (2, 4, 6, 8, 10 wt%). In order to prevent corn cob powder agglomeration and ensure homogeneous distribution of the reinforcement inside the epoxy, the ultrasonic technique and a mechanical stirrer were used. Then, the composite’s chemical compositions were evaluated using X-ray diffraction (XRD). The mechanical experiments showed an improvement in the Young’s modulus and compressive yield strength of the epoxy composites, increasing corn cob up to 8 wt% by 21.26% and 22.22%, respectively. Furthermore, tribological tests revealed that reinforcing epoxy with 8 wt% corn cob can decrease the coefficient of friction by 35% and increase wear resistance by 4.8%. A finite element model for the frictional process was constructed to identify different contact stresses and evaluate the load-carrying capacity of the epoxy composites. The finite element model showed agreement with the experimental results. An epoxy containing 8 wt% corn cob demonstrated the optimal mechanical and tribological properties. The rubbed surfaces were investigated by SEM to identify the wear mechanism of different composites.

Fog is a resource with great potential to capture fresh water from the atmosphere, regardless of the geographical and hydrological conditions. Micro-sized fog collection requires materials with hydrophilic/phobic patterns. In this study, we prepared hydrophilic poly(lactic acid) (PLA)/poly(ethylene glycol)-poly(propyl glycol)-poly(ethylene glycol) (PEG-PPG-PEG) blended nanofiber membranes with various PEG-PPG-PEG concentrations by electrospinning. Changes in the morphological and chemical properties, surface wettability, and thermal stability of the PLA/PEG-PPG-PEG composite nanofiber membranes were confirmed using field-emission scanning electron microscopy, Fourier-transform infrared spectroscopy, X-ray diffraction, contact angle testing, and thermogravimetric analysis. As the PEG-PPG-PEG content of the nanofiber membranes increased, their hydrophilicity increased. Water stability, membrane porosity, and water transport rate tests were also conducted to observe the behavior of the hydrophilic PLA nanocomposite membranes in aqueous media. Finally, we applied the PLA-based membranes as fog collectors. As the PEG-PPG-PEG content of the nanofiber membranes increased, their ability to collect fog increased by over 40% compared with that collected by a pure PLA membrane. The prepared membranes not only improve the ability of fog collectors to harvest water but also broaden the use of PLA-based membranes in multiple applications, including tissue engineering, drug delivery, scaffolds, and pharmaceuticals.

Reinforced composite materials have many applications in the aerospace, marine, and petroleum industries. Glass fiber-reinforced pipes are of considerable importance as pressurized vessels, infrastructure materials, and petroleum wastewater pipelines. The stress intensity factor due to through-thickness discontinuities is a major parameter in fracture mechanics to understand the failure mechanisms in glass fiber-composite pipes. The stress intensity factor is calculated for a composite cylinder subjected to internal pressure using the linear extended finite element method based on the law of energy release evaluation of surface damage. The analytical model needs two material properties; they are the tensile strength and the fracture toughness; therefore, a standard tensile test was carried out on a standard specimen taken from the pipe’s wall thickness. Moreover, the compact tension test specimen was manufactured from the pipe’s wall thickness to obtain the fracture toughness. The average tensile strength was measured as 21.5 MPa with a standard deviation of 5.59 MPa, moreover, the average Young’s modulus was measured as 32.75 GPa with a standard deviation of 6.64 GPa. The fracture toughness was measured as 2322 ($MPa \sqrt{m}$) with a standard deviation of 142.5 ($MPa \sqrt{m}$), whereas the average surface release energy ($G_{IC}$) was 153.6 kJ/m² with a standard deviation of 22.53 kJ/m². A valuable design equation was extracted from the finite element model to measure the effect of cracks on the hoop stress of the cylinder wall thickness based on a nonlinear model. Moreover, an acceptable equation was used to calculate the correction and shape factor of a cylinder with movable and unmovable through-thickness cracks. This study provides useful tools and guidance for the design and analysis of composite cylinders.