This study presents the correct processing of Co–Cr alloys as a method of preserving the properties of the materials as-cast, and therefore they can be safely placed in contact with the oral cavity tissues as resistance frameworks. The basic materials analyzed in this study were five commercial Co–Cr dental alloys with different components obtained in three processing steps. The analysis of the electrochemical behavior at the surface of the Co–Cr alloys was performed by electrochemical measurements: impedance spectroscopy (EIS), open circuit electrical potential (OCP), and linear polarization (LP). In terms of validation, all five alloys had a tendency to generate a stable oxide layer at the surface. After the measurements and the graphical representation, the alloy that had a higher percentage of tungsten (W) and iron (Fe) in composition showed a higher tendency of anodizing. After the application of the heat treatment, the disappearance of the hexagonal phase was observed, with the appearance of new phases of type (A,B)₂O₃ corresponding to some oxide compounds, such as Fe₂O₃, Cr₂O₃, (Cr,Fe)₂O₃, and CoMnO₃. In conclusion, the processing of Co–Cr alloys by melting and casting in refractory molds remains a viable method that can support innovation, in the context of technology advance in recent years towards digitalization of the manufacturing process, i.e., the construction of prosthetic frameworks conducted by additive methods using Co–Cr powder alloy.

Persistent host inflammatory and immune responses to biofilm play a critical role in the mechanisms that govern soft and hard tissue destruction in periodontal disease. Among the less explored facets of these mechanisms are chemokines, including CCL5 (C-C motif chemokine ligand 5), also known as RANTES (regulated on activation, normal T cell expressed and secreted), a proinflammatory CC subfamily chemokine synthesized by T lymphocytes. Despite its importance, there is currently no comprehensive review of the role of CCL5 in periodontitis in the literature. Therefore, this paper aims to fill this gap by summarizing the existing knowledge on the involvement of CCL5 in the onset and progression of periodontitis. In addition, we aim to stimulate interest in this relatively overlooked factor among periodontitis researchers, potentially accelerating the development of drugs targeting CCL5 or its receptors. The review examines the association of CCL5 with periodontitis risk factors, including aging, cigarette smoking, diabetes, and obesity. It discusses the involvement of CCL5 in pathological processes during periodontitis, such as connective tissue and bone destruction. The data show that CCL5 expression is observed in affected gums and gingival crevicular fluid of periodontitis patients, with bacterial activity contributing significantly to this increase, but the reviewed studies of the association between CCL5 expression and periodontal disease have yielded inconclusive results. Although CCL5 has been implicated in the pathomechanism of periodontitis, a comprehensive understanding of its molecular mechanisms and significance remains elusive, hindering the development of drugs targeting this chemokine or its receptors.

Temporary anchorage devices (TADs) are orthodontic mini-implants with remarkable characteristics that, once inserted, present mechanical retention (primary stability) without the process of bone osseointegration. However, interaction with the biological environment may cause changes in the morphology of the external surface of dental TADs. In this study, we used 17 TADs made of aluminum–vanadium titanium alloy, produced by two companies, which were analyzed through optical microscopy after being removed from the patients during orthodontic treatment. We evaluated the changes that appeared on the TADs’ surfaces after their use in the biological environment, depending on the morphological area in which they were inserted. In our study, we found changes in the morphology of the implant surface, and especially deposits of biological material in all study groups. On all samples examined after clinical use, regardless of the period of use, corrosion surfaces in different locations were observed. Our obtained results support the idea that the biological environment is aggressive for mini-implant structures, always producing changes to their surface during their clinical use.

Cobalt–chromium (Co–Cr) alloys are the most widely used materials for removable and fixed dental prosthetic frameworks. The fitting accuracy between these components in dental prosthetic frameworks assembles (DPFAs) is largely influenced by the manufacturing method. This study presents a novel manufacturing method that combined two common techniques for obtaining one single framework: casting of Co–Cr inserts on top of parts previously manufactured by selective laser melting (SLM) of Co–Cr powder (CoM). Horizontal (n = 4) and vertical (n = 3) surfaces were microscopically analyzed (n = 770 count sum). The results revealed a high precision of the process and high fitting accuracy between the hybrid frameworks. The average distance measured between the frameworks in joined position was 41.08 ± 7.56 µm. In conclusion, the manufacturing of Co–Cr alloys DPFA using the CoM method reduced the deformation of hybrid frameworks and improved the joining accuracy between them.

Background: Sinus-lift (SL) is a pre-prosthetic procedure with the objective of increasing bone height to achieve implant insertion primary stability in implant-supported prostheses. The biomechanical properties of SL augmentation materials are influenced by their origin, manufacture, bioactive substances addition, receiver, and surgical procedure. This systematic review provides insights into state-of-the-art SL biomaterials, focusing on autologous bone grafting as the gold standard. Methods: The study followed the PRISMA flow diagram, searching WoS (Web of Science), Embase, Cochrane, and PubMed databases using the search terms «sinus lift» OR «sinus augmentation» OR «bone graft» OR «bovine» OR «porcine» OR «autologous» OR «allogenic» OR «xenogeneic» OR «alloplastic» OR «hydroxyapatite» OR «β-tricalcium phosphate (β-TCP)» OR «equine» OR «PRF». Results: The highest bone gain was provided by Bioglass at 42%. Articles written between 2014 and 2024 in English or French, containing human studies and with full text available, were included. Participants were required to be in good general health, without acute, chronic, or congenital diseases, or substance abuse (drugs, alcohol, or nicotine). SL surgery was performed using the lateral approach, with no Schneiderian membrane perforation or postoperative complications. The network meta-analysis was conducted using the R statistical computing environment. To assess the inconsistency between direct and indirect evidence, we used a net heat plot. To evaluate heterogeneity across studies, we used the chi-squared-based Q-test and I² statistic. A significance level of 0.05 was applied throughout all analyses. Results: Allogeneic bovine bone and hydrox yapatite demonstrated the lowest resorption rates. Significant differences were found for residual graft and connective tissue between allogenous bovine bone (ABB) + AlB vs. β-TCP + PRF (p = 0.028); ABB + AlB vs. β-TCP (p = 0.034); ABB + AlB vs. BCP (p = 0.037). Meta-analysis showed that the overall heterogeneity was 51.8% (6.9–75%; p = 0.019), with significant heterogeneity within designs (p = 0.007) and no significant heterogeneity between designs (p = 0.39). AB had a better bone regeneration ratio compared to many of the other interventions, but only two passed the threshold of significance: A1B and B-TCP + AB. Conclusions: A grafting material’s superiority is determined by its new bone formation ratio, connective tissue integration, residual graft content, and bone resorptionratio. Although autologous bone grafting has exhibited superior bone regeneration compared to other biomaterials, it was not favored due to its unpredictable connective tissue concentration and bone resorption ratio. Additionally, autologous bone exhibited the fastest metabolic turnover among all grafting materials.

In oral rehabilitation, the treatment of partial edentulism (PEd) is performed by removable partial dentures (RPD) or assembled prosthetic works (APW) composed of several components, fixed to the prosthetic field (Pa) and a removable one (Pb), in order to facilitate the daily hygiene but also the damping of the occlusal forces applied in mastication. Cobalt-Chromium alloys are materials used to manufacture modern prosthetic assembles. In order for this study to be relevant, it was necessary to standardize the design of the framework (Pa) in terms of shape and volume so that the experiment could be reproducible for the five Co-Cr alloys: 0-A (Co-Cr-Mo), 5-A and 10-A (Co-Cr-Mo-W), 15-A and 16.4-A (Co-Cr-W-Fe) and for the three fabrication methods of dental assembled prosthetic frameworks: refractory duplicate method (RD) resulting removable framework (Pb), direct construction method (DC) resulting removable framework (Pb-) and casting over metal method (CoM) resulting removable framework (Pb+). The time allocated to the adaptation process (AP), mechanical processing and sandblasting, in order to assemble the two components was between 43–70 min, even though the assembly between the Pa-framework and the complementary framework (Pb+) was not necessary, CoM-method hs been provide the elimination of AP step. By applying the arithmetic simple rule of three, the percentages for each of the three methods used were calculated, the values of the difference were obtained. The CoM method improves the joining precision between the components of the removable assembly of prosthetic frameworks by 91.7% compared to the RD method and by 80.62% compared to the DC method. According to the efficiency of the methods used in the precision of joining between frameworks components, their order is: casting over metal, direct construction and refractory duplicate method.