(1) Background: This study evaluates the effect of a conventional/low-voltage light-curing protocol (LV protocol) (10 s with 1340 mW/cm²) and high-voltage light-curing protocol (HV protocol) (3 s with 3440 mW/cm²) on the microhardness (MH) of dental resin-based composites (RBCs). Five resin composites were tested: conventional Evetric (EVT), Tetric Prime (TP), Tetric Evo Flow (TEF), bulk-fill Tetric Power Fill (PFL), and Tetric Power Flow (PFW). (2) Materials and Methods: Two tested composites (PFW and PFL) were designed for high-intensity light curing. The samples were made in the laboratory in specially designed cylindrical molds; diameter = 6 mm and height = 2 or 4 mm, depending on the type of composite. Initial MH was measured on the top and bottom surfaces of composite specimens 24 h after light curing using a digital microhardness tester (QNESS 60 M EVO, ATM Qness GmbH, Mammelzen, Germany). The correlation between the filler content (wt%, vol%) and the MH of the RBCs was tested. For the calculation of depth-dependent curing effectiveness, the bottom/top ratio for initial MH was used. (3) Conclusions: MH of RBCs is more dependent on material composition than on light-curing protocol. Filler wt% has a greater influence on MH values compared to filler vol%. The bottom/top ratio showed values over 80% for bulk composites, while for conventional sculptable composites, borderline or suboptimal values were measured for both curing protocols.

This study investigated the correlation between bone characteristics, the design of orthodontic mini-implants, the pull-out force, and primary stability. This experimental in vitro study has examined commercial orthodontic mini-implants of different sizes and designs, produced by two manufacturers: Tomas-pin SD (Dentaurum, Ispringen, Germany) and Perfect Anchor (Hubit, Seoul, Korea). The total number of 40 mini-implants were tested. There are two properties that are common to all tested implants—one is the material of which they are made (titanium alloy Ti-6Al-4V), and the other is the method of their insertion. The main difference between the mini-implants, which is why they have been selected as the subject of research in the first place, is reflected in their geometry or design. Regardless of the type of implant, the average pull-out forces were found to be higher for a cortical bone thickness (CBTC) of 0.62–0.67 mm on average, compared to the CBTC < 0.62 mm, where the measured force averages were found to be lower. The analysis of variance tested the impact of the mini-implant geometry on the pull-out force and proved that there is a statistically significant impact (p < 0.015) of all three analyzed geometric factors on the pull-out force of the implant. The design of the mini-implant affects its primary stability. The design of the mini-implant affects the pulling force. The bone quality at the implant insertion point is important for primary stability; thus, the increase in the cortical bone thickness increases the value of the pulling force significantly.

This paper presents research results of a stiffness analysis of a Sarafix external fixation system. The stiffness property of the external fixator affects the local biomechanical and biological environment of fracture healing. The research has been conducted in a case when one of the Sarafix unilateral biplanar fixator configurations has been applied to a tibia with an open fracture. A stiffness analysis was performed using FEA and experimental testing under three types of loads: axial compression, AP (anterior-posterior) four-point bending and torsion. 3D geometrical and FEM model of the fixator configuration was formed using CATIA V5 software system and a structural analysis was performed afterwards. Verification of the results obtained from a structural analysis was carried out through experimental testing by comparing values of an appropriate component of displacement at the point of load

There is a lot of papers concerning gears topology optimization, but all of them are limited to the topology optimization of gear body. Gear tooth is not taken into consideration so far. Gear tooth was not optimized before because optimised structure could not be produced. By advancing of additive manufacturing technology, now, gear tooth can be produced in a form of shell body with empty space inside. In this paper, mass of spur gear tooth is optimized in relation to Von- Misses stress on critical places on the gear tooth. Optimization goal is to find optimal shell thickness of shell body spur gear tooth.

(1) Background: This study investigates the effects of curing light intensity, exposure time, and distance on the Vickers microhardness (VMH), hardness bottom-to-top ratio (HR), and temperature rise (TR) of conventional dental resin-based composite (RBC). (2) Materials and Methods: Specimens of one conventional RBC (Tetric EvoCeram, Ivoclar Vivadent) were cured with 12 different curing protocols (CPs), created with three different light intensities (Quartz Tungsten Halogen 300 mW/cm², LED 650 mW/cm², LED 1100 mW/cm²), two exposure times (20 and 40 s), and two distances of curing tip (0 and 8 mm). The VMH of top (VMH-T) and bottom (VMH-B) surfaces was measured. The hardness bottom-to-top ratio (HR) was calculated from VMH-B and VMH-T. The HR below 80% was rated as inadequate polymerization. The TR at the depth of 2 mm within the RBC was measured using a K-type thermocouple. Data were analyzed using Levene’s test and the multivariate analysis of variance (MANOVA). The level of significance was set at p < 0.05. (3) Results: Exposure time and distance significantly influenced VMH-B and HR. Increased distance significantly reduced VMH-B, HR, and TR. CPs 300 mW/cm²/8 mm/20 s and 650 mW/cm²/8 mm/20 s produced inadequate polymerization (HR < 80%). Prolonged exposure time produced higher values of VMH-B and HR. The TR was significantly influenced by light intensity and distance. (4) Conclusions: Suboptimal light intensity (<800 mW/cm²) can produce inadequate polymerization at the lower side of the composite layer when used from a distance. Prolonged irradiation can improve the polymerization to a certain extent. Clinicians are advised to monitor the intensity of the LCUs in order to optimize the photopolymerization process. Caution is required when polymerizing with high-intensity curing light in direct contact with the RBC with longer exposure times than recommended.

(1) Background: With the ever-increasing number of polymer materials and limited data on polymer gear calculations, designers are often required to perform extensive experimental testing in order to establish reliable operational data for specific gear applications. This research investigates the potential of a Polyvinyldene fluoride (PVDF) polymer material in gear applications, considering various loading conditions and different types of gear transmission configurations, including both self-mated mesh and steel/PVDF mesh. (2) Methods: PVDF gear samples were tested on a specially designed test rig that enables active torque control and temperature monitoring in order to obtain the necessary design parameters and failure modes. Each test for certain load conditions was repeated five times, and to fully investigate the potential of PVDF gear samples, comparative testing was performed for Polyoxymethylene (POM) gear. (3) Results: Tribological compatibility, tooth load capacity, and lifespan assessment, along with the types of failure, which, for some configurations, include several types of failures, such as wear and melting, were determined. Temperature monitoring data were used to estimate the coefficient of friction at the tooth contact of analyzed gear pairs, while optical methods were used to determine a wear coefficient. (4) Conclusions: The tribological compatibility of polymer gear pairs needs to be established in order to design a gear pair for a specific application. PVDF gear samples mated with steel gear showed similar lifespan properties compared to POM samples. Temperature monitoring and optical methods serve as a basis for the determination of the design parameters. PVDF is an appropriate material to use in gear applications, considering its comparable properties with POM. The particular significance of this research is reflected in the establishment of the design parameters of PVDF gear, as well as in the analysis of the potential of the PVDF material in gear applications, which gives exceptional significance to the current knowledge on polymer gears, considering that the PVDF material has not previously been analyzed in gear applications.