Photocatalytic degradation is one of the environmentally friendly methods used in treating dye wastewater. In this study, a series of MXene/g-C₃N₄ heterostructure photocatalysts with different loading amounts of MXene (1, 4, 8, and 12 wt.%) were successfully synthesized via the wet impregnation method and their photocatalytic activity was evaluated via the degradation of methylene blue under visible-light irradiation. As such, the 1 wt.% MXene/g-C₃N₄ heterostructure photocatalyst achieved a high degradation of methylene blue compared to the pure g-C₃N₄ under visible-light illumination of 180 min. This significant improvement was attributed to the intimate interfacial contact, evidently from the FESEM analysis, which allows the smooth photocharge carriers to transport between g-C₃N₄ and MXene. Additionally, the larger BET surface area demonstrated by the 1 wt.% MXene/g-C₃N₄ heterostructure allowed this sample to have higher adsorption of dye molecules and provided a higher number of reactive sites, which was beneficial for the enhancement of the photocatalytic activity. Nevertheless, it was found that the excessive loading of MXene can substantially impede photocatalytic activity. This was attributed to the decrease in the active sites, as well as the weakened crystallinity of the MXene/g-C₃N₄ heterostructure photocatalyst, evident from the FTIR and XRD analysis. All in all, this study has shown the potential of the MXene/g-C₃N₄ photocatalyst as a promising photocatalyst for highly efficient wastewater treatment applications.

Pollution from dye containing wastewater leads to a variety of environmental problems, which can destroy plant life and eco-systems. This study reports development of a seaweed-based biochar as an adsorbent material for efficient adsorption of methylene blue (MB) dye from synthetic wastewater. The Eucheuma cottonii seaweed biochar was developed through pyrolysis using a tube furnace with N₂ gas, and the properties were later improved by sulfuric acid treatment. The adsorption studies were conducted in a batch experimental setup under initial methylene blue concentrations of 50 to 200 mg/L, solution pH of 2 to 10, and temperature of 25 to 75 °C. The characterization results show that the developed biochar had a mesoporous pore morphology. The adsorbent possessed the surface area, pore size, and pore volume of 640 m²/g, 2.32 nm, and 0.54 cm³/g, respectively. An adsorption test for 200 mg/L of initial methylene blue at pH 4 showed the best performance. The adsorption data of the seaweed-based biochar followed the Langmuir isotherm adsorption model and the pseudo-second-order kinetic model, with the corresponding R² of 0.994 and 0.995. The maximum adsorption capacity of methylene blue using the developed seaweed‑based biochar was 133.33 mg/g. The adsorption followed the chemisorption mechanism, which occurred via the formation of a monolayer of methylene blue dye on the seaweed-based biochar surface. The adsorption performance of the produced seaweed biochar is comparable to that of other commercial adsorbents, suggesting its potential for large-scale applications.

Development of strategies for removing heavy metals from aquatic environments is in high demand. Cadmium is one of the most dangerous metals in the environment, even under extremely low quantities. In this study, kenaf and magnetic biochar composite were prepared for the adsorption of Cd²⁺. The synthesized biochar was characterized using (a vibrating-sample magnetometer VSM), Scanning electron microscopy (SEM), X-ray powder diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS). The adsorption batch study was carried out to investigate the influence of pH, kinetics, isotherm, and thermodynamics on Cd²⁺ adsorption. The characterization results demonstrated that the biochar contained iron particles that help in improving the textural properties (i.e., surface area and pore volume), increasing the number of oxygen-containing groups, and forming inner-sphere complexes with oxygen-containing groups. The adsorption study results show that optimum adsorption was achieved under pH 5–6. An increase in initial ion concentration and solution temperature resulted in increased adsorption capacity. Surface modification of biochar using iron oxide for imposing magnetic property allowed for easy separation by external magnet and regeneration. The magnetic biochar composite also showed a higher affinity to Cd²⁺ than the pristine biochar. The adsorption data fit well with the pseudo-second-order and the Langmuir isotherm, with the maximum adsorption capacity of 47.90 mg/g.