The aim of this work was to investigate the influence of initial pH value (pH₀) on the isothermal adsorption of Reactive Black 5 (RB5) dye on commercial powdered activated carbon. Four initial pH values were chosen for this experiment: pH₀ = 2.00, 4.00, 8.00, and 10.00. In order to investigate the mechanism of adsorption kinetic, studies have been performed using pseudo-first-order and pseudo-second-order kinetic models as well as an intraparticle diffusion model. In addition, thermodynamic parameters of adsorption were determined for pH₀ = 4.00. Results of this research showed that the initial pH value significantly influences the adsorption of RB5 dye onto activated carbon. The highest adsorption capacities (q_e) and efficiencies of decolouration were observed for initial pH values of pH₀ = 2.00 (q_e = 246.0 mg g⁻¹) and 10.00 (q_e = 239.1 mg g⁻¹) due to strong electrostatic interactions and attractive π···π interactions, respectively. It was also shown that the adsorption of RB5 dye on activated carbon at all initial pH values is kinetically controlled, assuming a pseudo-second-order model, and that intraparticle diffusion is not the only process that influences on the adsorption rate.

Natural dyes are not harmful to the environment owing to their biodegradability. For dye application to textiles, salts are necessary as mordant or electrolytes and make an environmental impact. In this paper, the influence of cationization during mercerization to the dyeing of cotton fabric with natural dye from Dactylopius coccus was researched. For this purpose, bleached cotton fabric as well as fabric cationized with Rewin OS was pre-mordanted using iron(II) sulfate heptahydrate (FeSO₄·7H₂O) and dyed with natural cochineal dye with and without electrolyte addition. For the characterization of surface changes after cationization, an electrokinetic analysis on SurPASS was performed and compared to pre-mordanting. For determination of dye exhaustion, the analysis of dye solution was performed on a UV/VIS spectrophotometer Cary 50 Solascreen. Spectrophotometric analysis was performed using a Datacolor 850 spectrophotometer, measuring remission ”until tolerance” and the whiteness degree, color parameters, color depth (K/S), and colorfastness of dyed fabric were calculated. Levelness was determined by visual assessment. Cationized cotton fabrics showed better absorption and colorfastness. Pre-mordanting and cationization showed synergism. The electrolytes improved the process of dye absorption. However, when natural dyeing was performed on cotton fabric cationized during mercerization, similar chromacity, uniform color, and colorfastness were achieved with and without electrolyte, resulting in pure purple hue of cochineal. For achieving a violet hue, pre-mordanting with Fe-salt was needed. Therefore, salt can be reduced or even unnecessary, which makes this process of natural dyeing more environmentally friendly.

In this study, the natural dye was extracted from Spartium junceum L. (SJL) flowers and applied on cellulose (cotton) and protein (wool) fabric. Fabrics were pre-mordant with alum prior to the dyeing process. Considering the global requirements on zero waste and green policy, the dyeing process was intended to be as much as possible environmentally friendly but still effective. Therefore, mordant concentration was optimized due to the reduction of the negative impact. The efficiency of the dyeing process was investigated by examination of fabrics’ color characteristics and colorfastness to washing properties. In this paper, we have proved that the extracted dye from Spartium junceum L. is an acidic dye (mordant dye) which is more applicable for the treatment of wool fabrics. In this paper, it was proved that phytochemicals responsible for coloring are part of the flavonoids group. The UV absorption spectra of extracted dye show 4 bands in the region of λ_max 224, 268, 308 and 346 nm which are ascribed to bands characteristic for flavonoids. Wool fabric pre-mordant with 3% alum and dyed shows great chromatic (C*) properties where C* value is in a range from 47.76 for unwashed samples to 47.50 for samples after 5 washing cycles and color hue (h°) is in a range 82.13 for unwashed samples to 81.52 for samples after 5 washing cycles. The best result regarding the colorfastness properties is shown by the wool sample treated with 3% alum after 5 washing cycles (total difference in color (Delta E*) = 0.87). These results confirm that metal (Al) from alum mordant make strong chemical bonds with wool substrate and dye since Delta E* values decrease in comparison to Delta E* values of the cotton samples treated the same way. The results revealed it is possible to reduce the concentration of mordant up to 3% and obtain satisfactory results regarding the colorfastness. Nevertheless, future research will go in the direction of replacing synthetic mordant with a more environmentally friendly one.

This article deals with cationization of cotton during mercerization and its effects on trichromatic vat dyeing. If cationization is carried out during the after-treatment, regardless of cotton pretreatment, the reaction takes place on the surface and blocks cellulose groups, subsequently resulting in uneven coloration. However, when cationization is carried out with an epihalohydrin during the mercerization process, new cellulose is formed in which the cationic compound is uniformly distributed and trapped between cellulose chains, resulting in uniform coloration after the dyeing process. The reaction time for the process during mercerization is 24 h, thus a more favorable process was researched. Based on electrokinetic analysis, it was found that 5 h was sufficient for the reaction with 3-chloro-2-hydroxypropyltrimethyl ammonium chloride (CHPTAC). The cationization of cotton contributed to the processes of vat dyeing. The change in charge upon cationization resulted in very high adsorption of vat-dye anions, indicating that ionic bonding occurred in addition to van der Waals forces. The color depth improved by more than 10 times. It should be emphasized that the colors with higher chroma and targeted color hue, especially in trichromatic dyeing, were obtained on cationized cotton, in contrast to standard cotton fabrics. The color differences obtained under the different light sources indicate the occurrence of metamerism. Considering the color fastness to laundering, vat-dyed cationized fabrics of all colors may be used in hospitals or other environments where high hygiene and oxidative bleaching are required.

The influence of 3D printing parameters on compressive properties is an important factor in the application of additive manufacturing processes for products subjected to compressive loads in use. In this study, the compressive strength and compressive modulus of acrylonitrile/butadiene/styrene (ABS) test specimens fabricated using the fused deposition modeling (FDM) process were investigated with the aim of producing products of high-heeled shoes for women. The experimental part of the study includes a central composite experimental design to optimize the main 3D printing parameters (layer thickness, infill density, and extrusion temperature) and the infill geometry (honeycomb and linear at a 45° angle—L45) to achieve maximum printing properties of the 3D-printed products. The results show that the infill density has the greatest influence on the printing properties, followed by the layer thickness and, finally, the extrusion temperature as the least influential factor. The linear infill at a 45° angle resulted in higher compressive strength and lower compressive modulus values compared to the honeycomb infill. By optimizing the results, the maximum compressive strength (that of L45 is 41 N/mm² and that of honeycomb 35 N/mm²) and modulus (that of L45 is 918 N/mm² and that of honeycomb is 868 N/mm²) for both types of infill is obtained at a layer thickness of 0.1 mm and infill density of 40%, while the temperature for L45 can be in the range of 209 °C to 254 °C, but for the honeycomb infill, the processing temperature is 255 °C. Additionally, the study highlights the potential for sustainable manufacturing practices and the integration of advanced 3D printing technologies to enhance the efficiency and eco-friendliness of the production process.