This paper summarizes the results obtained in the course of the development of a specific group of biocomposites with high functionality of flame retardancy, which are environmentally acceptable at the same time. Conventional biocomposites have to be altered through different modifications, to be able to respond to the stringent standards and environmental requests of the circular economy. The most commonly produced types of biocomposites are those composed of a biodegradable PLA matrix and plant bast fibres. Despite of numerous positive properties of natural fibres, flammability of plant fibres is one of the most pronounced drawbacks for their wider usage in biocomposites production. Most recent novelties regarding the flame retardancy of nanocomposites are presented, with the accent on the agents of nanosize (nanofillers), which have been chosen as they have low or non-toxic environmental impact, but still offer enhanced flame retardant (FR) properties. The importance of a nanofiller’s geometry and shape (e.g., nanodispersion of nanoclay) and increase in polymer viscosity, on flame retardancy has been stressed. Although metal oxydes are considered the most commonly used nanofillers there are numerous other possibilities presented within the paper. Combinations of clay based nanofillers with other nanosized or microsized FR agents can significantly improve the thermal stability and FR properties of nanocomposite materials. Further research is still needed on optimizing the parameters of FR compounds to meet numerous requirements, from the improvement of thermal and mechanical properties to the biodegradability of the composite products. Presented research initiatives provide genuine new opportunities for manufacturers, consumers and society as a whole to create a new class of bionanocomposite materials with added benefits of environmental improvement.

A detailed review of recent developments of layer-by-layer (LbL) deposition as a promising approach to reduce flammability of the most widely used fibers (cotton, polyester, polyamide and their blends) is presented. LbL deposition is an emerging green technology, showing numerous advantages over current commercially available finishing processes due to the use of water as a solvent for a variety of active substances. For flame-retardant (FR) purposes, different ingredients are able to build oppositely charged layers at very low concentrations in water (e.g., small organic molecules and macromolecules from renewable sources, inorganic compounds, metallic or oxide colloids, etc.). Since the layers on a textile substrate are bonded with pH and ion-sensitive electrostatic forces, the greatest technological drawback of LbL deposition for FR finishing is its non-resistance to washing cycles. Several possibilities of laundering durability improvements by different pre-treatments, as well as post-treatments to form covalent bonds between the layers, are presented in this review.

In this study, the natural dye was extracted from Spartium junceum L. (SJL) flowers and applied on cellulose (cotton) and protein (wool) fabric. Fabrics were pre-mordant with alum prior to the dyeing process. Considering the global requirements on zero waste and green policy, the dyeing process was intended to be as much as possible environmentally friendly but still effective. Therefore, mordant concentration was optimized due to the reduction of the negative impact. The efficiency of the dyeing process was investigated by examination of fabrics’ color characteristics and colorfastness to washing properties. In this paper, we have proved that the extracted dye from Spartium junceum L. is an acidic dye (mordant dye) which is more applicable for the treatment of wool fabrics. In this paper, it was proved that phytochemicals responsible for coloring are part of the flavonoids group. The UV absorption spectra of extracted dye show 4 bands in the region of λ_max 224, 268, 308 and 346 nm which are ascribed to bands characteristic for flavonoids. Wool fabric pre-mordant with 3% alum and dyed shows great chromatic (C*) properties where C* value is in a range from 47.76 for unwashed samples to 47.50 for samples after 5 washing cycles and color hue (h°) is in a range 82.13 for unwashed samples to 81.52 for samples after 5 washing cycles. The best result regarding the colorfastness properties is shown by the wool sample treated with 3% alum after 5 washing cycles (total difference in color (Delta E*) = 0.87). These results confirm that metal (Al) from alum mordant make strong chemical bonds with wool substrate and dye since Delta E* values decrease in comparison to Delta E* values of the cotton samples treated the same way. The results revealed it is possible to reduce the concentration of mordant up to 3% and obtain satisfactory results regarding the colorfastness. Nevertheless, future research will go in the direction of replacing synthetic mordant with a more environmentally friendly one.

Environmentally benign layer-by-layer (LbL) deposition was used to obtain flame-retardant and antimicrobial cotton. Cotton was coated with 8, 10, and 12 phytic acid (PA) and chitosan (CH)-urea bilayers (BL) and then immersed into copper (II) sulfate (CuSO₄) solution. Our findings were that 12 BL of PA/CH-urea + Cu²⁺ were able to stop flame on cotton during vertical flammability testing (VFT) with a limiting oxygen index (LOI) value of 26%. Microscale combustion calorimeter (MCC) data showed a reduction of peak heat release rates (pHRR) of more than 61%, while the reduction of total heat release (THR) was more than 54%, relative to untreated cotton. TG-IR analysis of 12 BL-treated cotton showed the release of water, methane, carbon dioxide, carbon monoxide, and aldehydes, while by adding Cu²⁺ ions, the treated cotton produces a lower amount of methane. Treated cotton also showed no levoglucosan. The intumescent behavior of the treatment was indicated by the bubbled structure of the post-burn char. Antibacterial testing showed a 100% reduction of Klebsiella pneumoniae and Staphylococcus aureus. In this study, cotton was successfully functionalized with a multifunctional ecologically benign flame-retardant and antibacterial nanocoating, by means of LbL deposition.