The health of the environment is worsening every day. Monitoring of potentially toxic elements and remediation of environmental pollution are necessary. Therefore, the research and development of simple, inexpensive, portable and effective sensors is important. Electrochemistry is a useful component of the field of environment monitoring. The present study focuses on evaluating and comparing three types of electrodes (PIGE, PIGE/MWCNT/HNO₃ and PIGE/MWCNT/EDTA/HNO₃) employed for the simultaneous electrochemical determination of four potentially toxic elements: Cd(II), Pb(II), Cu(II) and Hg(II). Cyclic voltammograms were measured in an acetate buffer. The LOD, LOQ, the standard and relative precisions of the method and a prediction intervals were calculated (according to the technical procedure DIN 32 645) for the three electrodes and for each measured element. The LOD for PIGE/CNT/HNO₃ (the electrode with narrowest calculated prediction intervals) was 2.98 × 10⁻⁷ mol L⁻¹ for Cd(II), 4.83 × 10⁻⁷ mol L⁻¹ for Pb(II), 3.81 × 10⁻⁷ mol L⁻¹ for Cu(II), 6.79 × 10⁻⁷ mol L⁻¹ for Hg(II). One of the benefits of this study was the determination of the amount of Hg(II) in the mixture of other elements.

Slags produced in the steelmaking industry could be a source of chromium. Slags contain, depending on different types of slags, between 2 to 5 wt.% of Cr. Roasting of slag with NaOH, followed by subsequent leaching can produce leachates which can be efficiently processed using electrocoagulation (EC). This paper provides results from the EC process optimization for Cr(VI) solutions with initial concentration 1000 mg/L of Cr(VI). Influence of pH, current intensity and NaCl concentration on the efficiency of chromium recovery, energy consumption as well as solid product composition is discussed in detail. Optimum of pH = 6 was chosen for EC processing of Cr leachates as well as current intensities of 0.1–0.5 A because of the higher Cr/Fe ratio in solid product compared to higher current intensities. Results of EC processing of four real leachates of electric arc furnace carbon steel slag (EAFC), electric arc furnace stainless steel slag (EAFS), low carbon ferrochrome slag (LC FeCr) and high carbon ferrochrome slag (HC FeCr) were evaluated. Comparison of the results of four real leachate samples is presented. Obtained final solid product was identified as (Fe_0.6 Cr_0.4)₂O₃ and with up to 20% of Cr could be used as source of chromium in the ferrochrome production.

Diamond-like carbon (DLC) coatings enhance tool wear resistance across various temperatures. The sp³/sp² bond ratio within DLC significantly impacts its properties and thermal stability. Elevated temperatures can alter DLC’s structure, while metallic elements and interlayers like chromium can modify its microstructure and performance. To evaluate the potential of W-DLC coatings with a chromium interlayer on 40CrMoV5-1 hot work tool steel under elevated temperatures, mechanical and tribological properties were assessed at room temperature and at temperatures of 100, 200, 300, 400, and 500 °C. Nanoindentation revealed a maximum hardness of 14.1 ± 1.3 GPa for the coating deposited at room temperature, attributed to a high sp³ content confirmed by Raman spectroscopy. Hardness decreased to 9.3 ± 1.0 GPa at 400 °C due to graphitization. The elastic modulus remained relatively constant across all temperatures. Tribological tests indicated a low coefficient of friction (CoF) of 0.15 at room temperature, increasing to 0.35 at 100 °C. The CoF further rose to 0.5 at 200 °C, coinciding with increased graphitization. However, the CoF reduced to 0.45 and 0.35 at 400 °C and 500 °C, respectively, likely due to the formation of a WO₃ tribo-film and the protective effect of the chromium interlayer.

The paper describes cementation as a suitable method applied in the refining of EAFD leachates in order to obtain required purity of ZnO for specific industrial application. For study of cementation conditions, the leachate from alkaline leaching with (NH₄)₂CO₃ was used. The leachates contained a high amount of zinc (8000–12,000 µg/mL) and a low content of impurities such as iron, lead, copper, chromium and manganese in the range of 1–21 µg/mL. Cementation conditions were predicted by thermodynamic study, theoretically confirming the viability of the proposed experiments at the considered pH = 8–9. Cementation experiments were carried out using powdered zinc and aluminium (5 g/L) as cementation agents in the first phase separately. To increase the cementation efficiency, their combination was used (2.5:2.5 g/L or 5:5 g/L) at temperatures of 20, 40, 60 and 80 °C for 30 min. The optimum cementation conditions were established as: Zn:Al = 5:5 g/L, 60 °C. Under the given conditions, 100% of Fe, Cu, Pb and Mn were removed from the leachate. The ZnO with the maximum purity of 96.67% was obtained by crystallization of cemented leachate at 105 °C, followed by calcination at 900 °C for 4 h. ZnO with such a purity is suitable for use in the electrical or rubber industries.

In the presented article, an electrocoagulation method using a steel cathode and a steel anode was used to obtain chromium from laboratory-prepared model solutions with known compositions. The study aimed to analyze the effect of solution conductivity, pH, and 100% efficiency of chromium removal from the solution, as well as the highest possible Cr/Fe ratio in the final solid product throughout the process of electrocoagulation. Different concentrations of chromium (VI) (100, 1000, and 2500 mg/L) and different pH values (4.5, 6, and 8) were investigated. Various solution conductivities were provided by the addition of 1000, 2000, and 3000 mg/L of NaCl to the studied solutions. Chromium removal efficiency equal to 100% was achieved for all studied model solutions for different experiment times, depending on the selected current intensity. The final solid product contained up to 15% chromium in the form of mixed FeCr hydroxides obtained under optimal experimental conditions: pH = 6, I = 0.1 A, and c (NaCl) = 3000 mg/L. The experiment indicated the advisability of using a pulsed change of electrode polarity, which led to a reduction in the time of the electrocoagulation process. The results may help in the rapid adjustment of the conditions for further electrocoagulation experiments, and they can be used as the optimization experimental matrix.