The health of the environment is worsening every day. Monitoring of potentially toxic elements and remediation of environmental pollution are necessary. Therefore, the research and development of simple, inexpensive, portable and effective sensors is important. Electrochemistry is a useful component of the field of environment monitoring. The present study focuses on evaluating and comparing three types of electrodes (PIGE, PIGE/MWCNT/HNO₃ and PIGE/MWCNT/EDTA/HNO₃) employed for the simultaneous electrochemical determination of four potentially toxic elements: Cd(II), Pb(II), Cu(II) and Hg(II). Cyclic voltammograms were measured in an acetate buffer. The LOD, LOQ, the standard and relative precisions of the method and a prediction intervals were calculated (according to the technical procedure DIN 32 645) for the three electrodes and for each measured element. The LOD for PIGE/CNT/HNO₃ (the electrode with narrowest calculated prediction intervals) was 2.98 × 10⁻⁷ mol L⁻¹ for Cd(II), 4.83 × 10⁻⁷ mol L⁻¹ for Pb(II), 3.81 × 10⁻⁷ mol L⁻¹ for Cu(II), 6.79 × 10⁻⁷ mol L⁻¹ for Hg(II). One of the benefits of this study was the determination of the amount of Hg(II) in the mixture of other elements.

Slags produced in the steelmaking industry could be a source of chromium. Slags contain, depending on different types of slags, between 2 to 5 wt.% of Cr. Roasting of slag with NaOH, followed by subsequent leaching can produce leachates which can be efficiently processed using electrocoagulation (EC). This paper provides results from the EC process optimization for Cr(VI) solutions with initial concentration 1000 mg/L of Cr(VI). Influence of pH, current intensity and NaCl concentration on the efficiency of chromium recovery, energy consumption as well as solid product composition is discussed in detail. Optimum of pH = 6 was chosen for EC processing of Cr leachates as well as current intensities of 0.1–0.5 A because of the higher Cr/Fe ratio in solid product compared to higher current intensities. Results of EC processing of four real leachates of electric arc furnace carbon steel slag (EAFC), electric arc furnace stainless steel slag (EAFS), low carbon ferrochrome slag (LC FeCr) and high carbon ferrochrome slag (HC FeCr) were evaluated. Comparison of the results of four real leachate samples is presented. Obtained final solid product was identified as (Fe_0.6 Cr_0.4)₂O₃ and with up to 20% of Cr could be used as source of chromium in the ferrochrome production.

In this paper, results of research on the reactivities of selected biomass types considering their application in pyrometallurgical processes of metal production are presented. Walnut shells, sunflower husk pellets and spent coffee grounds were selected as biomass materials. Their use as potential reducers in the process of metallurgical slag decopperisation is an innovative approach to this subject. The thermogravimetric findings show that all three tested biomass types are classified as highly reactive. The time to reach maximum reactivity ranges from 1.5 to 3 min and, the lowest value is recorded for the sample of spent coffee grounds. The sample hold time of two hours enables copper content reduction to approx. 1 wt% for practically all the reducers tested. A longer duration of liquid slag contact with the reducer results in a decreased copper content in the slag to a value below 1 wt%. Copper concentrations of 0.5 wt% and lower are observed with a hold time of 4 h. The preliminary results indicate that there is great potential for the use of this type of material in non-ferrous metallurgy, which may translate into replacing fossil raw materials and thus introducing the principles of a sustainable process in this case of metal production.

In the presented article, an electrocoagulation method using a steel cathode and a steel anode was used to obtain chromium from laboratory-prepared model solutions with known compositions. The study aimed to analyze the effect of solution conductivity, pH, and 100% efficiency of chromium removal from the solution, as well as the highest possible Cr/Fe ratio in the final solid product throughout the process of electrocoagulation. Different concentrations of chromium (VI) (100, 1000, and 2500 mg/L) and different pH values (4.5, 6, and 8) were investigated. Various solution conductivities were provided by the addition of 1000, 2000, and 3000 mg/L of NaCl to the studied solutions. Chromium removal efficiency equal to 100% was achieved for all studied model solutions for different experiment times, depending on the selected current intensity. The final solid product contained up to 15% chromium in the form of mixed FeCr hydroxides obtained under optimal experimental conditions: pH = 6, I = 0.1 A, and c (NaCl) = 3000 mg/L. The experiment indicated the advisability of using a pulsed change of electrode polarity, which led to a reduction in the time of the electrocoagulation process. The results may help in the rapid adjustment of the conditions for further electrocoagulation experiments, and they can be used as the optimization experimental matrix.