The braking system is a crucial element in automotive safety. In order for the braking mechanism to function effectively, the brake pads’ durability as well as quality are crucial aspects to take into account. A brake pad is a part of a vehicle that holds the wheel rotation so that braking can occur. Asbestos, which is harmful to human health, is a raw material that is recently being widely used as a material mixture for the manufacturing of brake pads. Many efforts have been made by researchers to find other natural alternative materials to replace the use of asbestos. Natural materials that have received much attention and research include coconut fiber, wood powder or flour, bamboo fiber, shell powder, etc. This review paper focuses on analyzing the main parameters that affect brake pad performance. The composition of filler and fiber types of reinforcement for polymer composites is discussed. Previous studies’ information on the fabrication and testing of brake pads are also highlighted. Furthermore, the findings of this review can provide researchers and academicians with useful information and points to consider for further research.

Green mussel and crab shells are natural sources of CaCO₃, which is widely used as a bioceramic for biomedical applications, although they are commonly disposed of in landfills. The improper disposal of green mussel and crab shells can cause environmental pollution, reducing the quality of life in the community. Many studies have reported the preparation of CaCO₃ from green mussels and crab shells. However, there are limited studies comparing the characteristics, including the crystal phase obtained, weight percentage (%) of crystal, crystal size, crystal system, and elemental composition of CaCO₃ from green mussel shells, crab shells, and commercial CaCO3. The objective of this research was to compare the calcium carbonate properties formed from green mussel (PMS) and crab (PCS) shells to commercial CaCO₃. Green mussel and crab shells were crushed to powder and were calcined at 900 °C for 5 h. Precipitated Calcium Carbonate (PCC) was synthesized from calcined green mussel and crab shells using a solution of 2M HNO₃, NH₄OH, and CO₂ gas. The effect of setting parameters on the synthesized product was analyzed using XRD and SEM-EDX methods. This study shows that the chemical composition of PMS is nearly identical to that of commercial CaCO₃, where no contaminants were identified. In contrast, PCS has N components other than Ca, C, and O. Furthermore, the predominance of the vaterite crystal phases in PMS and PCS, with respective weight percentages of 91.2% and 98.9%, provides a benefit for biomaterial applications. The crystallite sizes of vaterite in PMS, PCS, and calcite in commercial CaCO₃ are 34 nm, 21 nm, and 15 nm, respectively.

Recently, the most critical issue related to the use of natural fibre-reinforced polymer composites (NFRPC) is the degradation properties of composites exposed to the environment. NFRPC’s moisture absorption behaviour has adverse effects on the composite’s mechanical properties and dimensional stability. The purpose of this study is to analyse the mechanical properties of epoxy composites reinforced by jute–ramie hybridisation. This study also analysed the effect of stacking sequence hybridisation of the jute–ramie composite on water absorption behaviour. A five-layer different type of stacking sequence of single and hybrid jute–ramie is produced with the hand lay-up method. The results obtained from this study found that the mechanical properties and water absorption behaviour of a single jute fibre are lower compared to a single ramie fibre. The hybrid of jute–ramie has been able to increase the performance of composite compared to pure jute composites. The mechanical properties of the hybrid jute–ramie composite show a reduction effect after exposure to an aqueous environment due to the breakdown of fibre matrix interfacial bonding. However, after 28 days of immersion, all types of the stacking sequence’s mechanical properties are still higher than that of pure epoxy resin. In conclusion, the appropriate sequence of stacking and selecting the material used are two factors that predominantly affect the mechanical properties and water absorption behaviour. The hybrid composites with the desired and preferable properties can be manufactured using a hand-lay-up technique and used in the various industrial applications.

Hydroxyapatite has the closest chemical composition to human bone. Despite this, the use of nano-hydroxyapatite (nHA) to produce biocomposite scaffolds from a mixture of polylactic acid (PLA) and polycaprolactone (PCL) using cold isostatic pressing has not been studied intensively. In this study, biocomposites were created employing nHA as an osteoconductive filler and a polymeric blend of PLA and PCL as a polymer matrix for prospective usage in the medical field. Cold isostatic pressing and subsequent sintering were used to create composites with different nHA concentrations that ranged from 0 to 30 weight percent. Using physical and mechanical characterization techniques such as Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and density, porosity, tensile, and flexural standard tests, it was determined how the nHA concentrations affected the biocomposite’s general properties. In this study, the presence of PLA, PCL, and nHA was well identified using FTIR, XRD, and SEM methods. The biocomposites with high nHA content showed intense bands for symmetric stretching and the asymmetric bending vibration of PO₄³⁻. The incorporation of nHA into the polymeric blend matrix resulted in a rather irregular structure and the crystallization became more difficult. The addition of nHA improved the density and tensile and flexural strength of the PLA/PCL matrix (0% nHA). However, with increasing nHA content, the PLA/PCL/nHA biocomposites became more porous. In addition, the density, flexural strength, and tensile strength of the PLA/PCL/nHA biocomposites decreased with increasing nHA concentration. The PLA/PCL/nHA biocomposites with 10% nHA had the highest mechanical properties with a density of 1.39 g/cm³, a porosity of 1.93%, a flexural strength of 55.35 MPa, and a tensile strength of 30.68 MPa.

Polylactic acid (PLA) and polycaprolactone (PCL) are synthetic polymers that are extensively used in biomedical applications. However, the PLA/PCL blend produced by ball milling, followed by pressure compaction and sintering, has not been extensively explored. The goal of this research is to investigate the effect of the composition of biomaterials derived from PLA and PCL prepared by ball milling, followed by pressure compaction and sintering, on mechanical and physical properties. PCL and PLA with various concentrations were blended utilizing a ball milling machine for 2 h at an 80-rpm rotation speed. The obtained mixture was placed in a stainless steel 304 mold for the compacting process, which uses a pressure of 30 MPa to create a green body. The sintering procedure was carried out on the green body created at 150 °C for 2 h using a digital oven. The obtained PLA/PCL blend was tested using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), Scanning electron microscopy (SEM), density, porosity, and three-point bending. Following the interaction between PCL and PLA in the PLA/PCL blend, the FTIR spectra and XRD diffractograms obtained in this work revealed a number of modifications in the functional groups and crystal phase. The 90PLA specimen had the best mechanical properties, with a maximum force and displacement of 51.13 N and 7.21 mm, respectively. The porosity of the PLA/PCL blend decreased with increasing PLA concentration so that the density and flexural properties of the PLA/PCL blend increased. The higher PCL content decreased the stiffness of the PLA molecular chain, consequently reducing its flexural properties.

The manufacturing of materials, in conjunction with green technology, emphasises the need to employ renewable resources to ensure long-term sustainability. Re-exploring renewable elements that can be employed as reinforcing materials in polymer composites has been a major endeavour. The research goal is to determine how well palm kernel cake filler (PKCF) performs in reinforced epoxy composites. In this study, PKCF with 100 mesh was mixed with epoxy resin (ER) in various ratios ranging from 10% to 40% by weight. Hand lay-up with an open mould is proposed as a method for fabricating the specimen test. Surface modification of PKCF with varying concentrations of NaOH (5 wt.% and 10 wt.%) will be contrasted with the untreated samples. Using Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC), the effect of alkaline treatment will be examined. The tensile and maximum flexural strength of the untreated PKCF/ER composite were determined in this work, with a 30 wt.% of PKCF having the highest tensile strength of 31.20 MPa and the highest flexural strength of 39.70 MPa. The tensile and flexural strength were reduced to 22.90 MPa and 30.50 MPa, respectively, when the filler loading was raised to 40 wt.%. A 5 wt.% alkali treatment for 1 h improved the composites’ mechanical characteristics. Lastly, an alkali treatment can aid in the resolution of the problem of inadequate matrix and filler interaction. Alkaline treatment is a popular and effective method for reducing the hydroxyl group in fillers and, thus, improving interfacial bonding. Overall, palm kernel cake is a promising material used as a filler in polymer composites.