In this paper, chitosan (CS)/graphene oxide (GO) composite films were prepared, and the effect of γ-ray irradiation on the properties of composite films was investigated. The irradiation crosslinking reaction occurred in composite films with the existence of acetic acid, and the properties changed upon the various irradiation dose. The swelling degree of the composite film with 0 wt % GO decreased with the increasing of the irradiation dose, but the swelling degree of which with GO increased instead. The thermal stability increased with the increasing of the irradiation dose, but the effect of the irradiation on the thermal stability weakened as the increasing of the content of GO, due to the enhanced irradiation resistance performance. The tensile strength increased firstly and decreased subsequently with the increasing of the irradiation dose and the content of GO. Composite films showed the enhanced antibacterial activity against Bacillus subtilis, compared to Escherichia coli and Staphylococcus aureus. The antibacterial activity weakened with the increasing of the content of GO. The antibacterial activity was relatively stronger when the irradiation dose was 20 KGy. In addition, the structural, crystal, and morphological properties of composite films were characterized by FT-IR, XRD, and SEM. It is worth noting that the GO was pre-functionalized via KH560 for the better compatibility with CS matrix.

Efflorescence is aesthetically undesirable to all cementitious materials products and mainly results from the carbonation of hydrates and salt precipitation. Alternative binders without portlandite formation theoretically have much lower efflorescence risk, but in practice, the efflorescence of ettringite-rich systems is still serious. This study reports the impacts of mineral additives on the efflorescence of ettringite-rich systems and the corresponding microstructural evolution. The effects of silica fume, limestone powder, and diatomite on efflorescence and the capillary pore structure of mortars were investigated from a multi-scale analysis. The composition and microstructure of efflorescent phases were revealed by optical microscope (O.M.), in-situ Raman spectroscopy, and Scanning Electron Microscopy (SEM). Results indicate that the addition of mineral additives can efficiently inhibit the efflorescence of reference, especially with silica fume. Similar to the ettringite-rich system, the efflorescence substances of all modifies are composed of ettringite and CaCO₃, indicating that the addition of mineral admixture does not lead to chemical reactions, lower capillary absorption coefficient of mineral additives modified specimen, the denser pore structure and the lower efflorescence degree.