Wearable E-textile systems should be comfortable so that highest efficiency of their functionality can be achieved. The development of electronic textiles (functional textiles) as a wearable technology for various applications has intensified the use of flexible wearable functional textiles instead of wearable electronics. However, the wearable functional textiles still bring comfort complications during wear. The purpose of this review paper is to sightsee and recap recent developments in the field of functional textile comfort evaluation systems. For textile-based materials which have close contact to the skin, clothing comfort is a fundamental necessity. In this paper, the effects of functional finishing on the comfort of the textile material were reviewed. A brief review of clothing comfort evaluations for textile fabrics based on subjective and objective techniques was conducted. The reasons behind the necessity for sensory evaluation for smart and functional clothing have been presented. The existing works of literature on comfort evaluation techniques applied to functional fabrics have been reviewed. Statistical and soft computing/artificial intelligence presentations from selected fabric comfort studies were also reviewed. Challenges of smart textiles and its future highlighted. Some experimental results were presented to support the review. From the aforementioned reviews, it is noted that the electronics clothing comfort evaluation of smart/functional fabrics needs more focus.

Functional finishing brings an alteration on the mechanical and surface properties of textile materials and henceforth influences the tactile properties. In this work, Kawabata evaluation systems (KES) for fabrics were utilized to notice the changes in the tactile properties of fabrics resulting from different finishing types such as inkjet printing, screen printing, and coating. The effects of functional finishing on the fabric’s tactile property were inconsistent with reference to the course of decrease or increase being dependent on the types of finishes. The findings showed that KES can be employed as a promising tool to sort out the suitable functional finishing types in terms of tactile properties. Amongst the implemented finishing types, inkjet printing offered superior tactile properties with respect to tensile energy (softness), shear rigidity, compressional softness, bending stiffness (drapability), and surface properties. The KES results confirmed that low-stress mechanical properties are strongly associated with the tactile property and might assist as a quality profile data source for guaranteeing the production and development of a virtuous quality product. The result encourages further utilization of the KES for functional fabric tactile property evaluation.

This paper investigates the effects of warp yarns ratios on the ballistic performances of three-dimensional (3D) warp interlock p-aramid fabrics. Four 3D warp interlock variants with different binding and stuffer warp yarns ratios were designed and developed. Except for warp yarns ratios, similar fabric parameters and manufacturing conditions were considered. Two-dimensional (2D) woven fabric having similar material characteristics and recommended for female seamless soft body armor are also considered for comparisons. Five ballistic panels, one from 2D plain weave fabric and the rest four from the other 3D warp interlock variants were prepared in a non-angled layer alignment and non-stitched but bust-shaped molded form. The ballistic test is carried out according to NIJ (National Institute of Justice) standard-level IIIA. Back Face Signature (BFS) was then modeled and measured to compute both trauma and panels’ energy-absorbing capability. The result showed significant ballistic improvement in the 3D warp interlock variant with optimum warp yarns ratios over traditional 2D plain weave fabrics. 3D warp interlock fabric panel made with 66.6% binding and 33.3% stuffer warp yarn ratio revealed both lower BFS depth and higher energy absorbing capacity (%) than other panels made of 2D plain weave and 3D warp interlock fabric variants.

The global demand for fiber-based products is continuously increasing. The increased consumption and fast fashion current in the global clothing market generate a significant quantity of pre-and post-production waste that ends up in landfills and incinerators. The present study aims to obtain a new waste-based composite material panel for construction applications with improved mechanical properties that can replace traditional wood-based oriented strand boards (OSB). The new composite material is formed by using textile wastes as a reinforcement structure and a combination of bi-oriented polypropylene films (BOPP) waste, polypropylene non-woven materials (TNT) waste and virgin polypropylene fibers (PP) as a matrix. The mechanical properties of waste-based composite materials are modeled using the Taguchi method based on orthogonal arrays to maximize the composite characteristics’ mechanical properties. Experimental data validated the theoretical results obtained.

Research approaches on the use of ecotechnologies like ozone assisted processes for the decolorization of textiles are being explored as against the conventional alkaline reductive process for the color stripping of the cotton textiles. The evaluation of these ecotechnologies must be performed to assess the environmental impacts. Partial “gate to gate” Life Cycle Assessment (LCA) was implemented to study the ozone based decolorization process of the reactive dyed cotton textiles. Experiments were performed to determine input and output data flows for decolorization treatment of reactive dyed cotton textile using the ozonation process. The functional unit was defined as “treatment of 40 g of reactive dyed cotton fabric to achieve more than 94% color stripping”. Generic and specific data bases were also used to determine flows, and International Life Cycle Data system (ILCD) method was selected to convert all flows into environmental impacts. The impact category “Water resource depletion” is the highest for all the ozonation processes as it has the greatest relative value after normalization amongst all the impact indicators. Electricity and Oxygen formation were found to be the major contributors to the environmental impacts. New experimental conditions have been studied to optimize the impacts.

Materials used in the technical application including composite reinforcements and ballistic fabrics should show not only good mechanical performance but also better deformational behaviors. Meanwhile, three dimensional (3D) warp interlock fabrics have been widely employed in such applications to substitute the two dimensional (2D) fabrics because of their enhanced through-the-thickness performance and excellent formability. The deformational behaviors of such 3D warp interlock fabrics have been also influenced by various internal and external parameters. To understand and fill this gap, the current paper investigates the effects of the warp yarn interchange ratios inside the fabric structure on the formability behaviors of dry 3D warp interlock p-aramid fabrics. Four 3D warp interlock architecture types made with different binding and stuffer warp yarn interchange ratios were designed and manufactured. An adapted hydraulic-driven stamping bench along with hemispherical punch was utilized for better forming behavior analysis such as in-plane shear angle and its recovery, material drawing-in and its recovery, deformational depth recovery, and required stamping forces. Based on the investigation of various formability behaviors, the formability of (3D) warp interlock fabrics were greatly influenced by the binding and stuffer warp yarns interchange ratio inside the 3D warp interlock structure. For example, preform 3D-8W-0S exhibited a maximum deformational height recovery percentage of 5.1%, whereas 3D-4W-8S recorded only 0.72%. Preform 3D-8W-4S and 3D-8W-8S revealed 1.45% and 4.35% recovery percentages toward the deformational height at maximum position. Besides, sample 3D-4S-8W revealed the maximum drawing-in recovery percentage of 43.13% and 46.98% in the machine and cross direction, respectively, around the preform peripheral edges. On the contrary, samples with higher binding warp yarns as 3D-8W-0S show the maximum drawing-in recovery percentages values of 31.21% and 34.99% in the machine and cross directions respectively.