Recently, the most critical issue related to the use of natural fibre-reinforced polymer composites (NFRPC) is the degradation properties of composites exposed to the environment. NFRPC’s moisture absorption behaviour has adverse effects on the composite’s mechanical properties and dimensional stability. The purpose of this study is to analyse the mechanical properties of epoxy composites reinforced by jute–ramie hybridisation. This study also analysed the effect of stacking sequence hybridisation of the jute–ramie composite on water absorption behaviour. A five-layer different type of stacking sequence of single and hybrid jute–ramie is produced with the hand lay-up method. The results obtained from this study found that the mechanical properties and water absorption behaviour of a single jute fibre are lower compared to a single ramie fibre. The hybrid of jute–ramie has been able to increase the performance of composite compared to pure jute composites. The mechanical properties of the hybrid jute–ramie composite show a reduction effect after exposure to an aqueous environment due to the breakdown of fibre matrix interfacial bonding. However, after 28 days of immersion, all types of the stacking sequence’s mechanical properties are still higher than that of pure epoxy resin. In conclusion, the appropriate sequence of stacking and selecting the material used are two factors that predominantly affect the mechanical properties and water absorption behaviour. The hybrid composites with the desired and preferable properties can be manufactured using a hand-lay-up technique and used in the various industrial applications.

This study aims to produce and investigate the potential of biodegradable Polylactic Acid (PLA)-based composites mixed with chitosan and Turmeric Essential Oil (TEO) as an anti-microbial biomaterial. PLA has good barrier properties for moisture, so it is suitable for use as a raw material for making packaging and is included in the GRAS (Generally Recognized As Safe). Chitosan is a non-toxic and antibacterial cationic polysaccharide that needs to be improved in its ability to fight microbes. TEO must be added to increase antibacterial properties due to a large number of hydroxyl (-OH) and carbonyl functional groups. The samples were prepared in three different variations: 2 g of chitosan, 0 mL TEO and 0 mL glycerol (Biofilm 1), 3 g of chitosan, 0.3 mL TEO and 0.5 mL of glycerol (Biofilm 2), and 4 g of chitosan, 0.3 of TEO and 0.5 mL of glycerol (Biofilm 3). The final product was characterized by its functional group through Fourier transform infrared (FTIR); the functional groups contained by the addition of TEO are C-H, C=O, O-H, and N-H with the extraction method, and as indicated by the emergence of a wide band at 3503 cm⁻¹, turmeric essential oil interacts with the polymer matrix by creating intermolecular hydrogen bonds between their terminal hydroxyl group and the carbonyl groups of the ester moieties of both PLA and Chitosan. Thermogravimetric analysis (TGA) of PLA as biofilms, the maximum temperature of a biofilm was observed at 315.74 °C in the variation of 4 g chitosan, 0.3 mL TEO, and 0.5 mL glycerol (Biofilm 3). Morphological conditions analyzed under scanning electron microscopy (SEM) showed that the addition of TEO inside the chitosan interlayer bound chitosan molecules to produce solid particles. Chitosan and TEO showed increased anti-bacterial activity in the anti-microbial test. Furthermore, after 12 days of exposure to open areas, the biofilms generated were able to resist S. aureus and E. coli bacteria.

The investigation of hybrid, woven, natural fiber-reinforced polymer composites as a substitute reinforcement for fiber polymer composites has recently caught the interest of academics, industry, and researchers. Woven, natural fiber composites have been implemented in many different applications, including parts for automobiles, household items, flooring, aerospace, and ballistic materials. Therefore, this research seeks to establish the thermal and mechanical characteristics of composites made from rattan strips (RS) and glass fiber (GF)-reinforced epoxy resin (ER). Other than that, the impact of layering configurations with respect to the thermal and mechanical characteristics of the RS and GF will be determined. Hand lay-up and a hydraulic press machine produce hybrid, woven RS and GF laminates. The hybrid composite’s mechanical properties will be investigated using impact, tensile, and flexural tests. The hybrid woven of the GF/RS/RS/RS/GF composite sequence demonstrated the highest mechanical properties in comparison to other sequences. The increase from one to three layers of RS in the core layer of GF hybrid composites enhanced the flexural, impact, and tensile properties. In addition, the hybridization of rattan and GF is more thermally stable, as recorded by the high decomposition temperature. As a finding of the research, the woven RS and GF hybrid is a potential material for automotive applications such as car bumpers, for example.