Prpić V, et al. J Adv Prosthodont. 2020 Dec;12(6):376-382. https://doi.org/10.4047/jap.2020.12.6.376

Laser-powder bed fusion (LPBF) is one of the preferred techniques for producing Co-Cr metal structures for dental prosthodontic appliances. However, there is generally insufficient information about material properties related to the production process and parameters. This study was conducted on samples produced from three different commercially available Co-Cr dental alloys produced on three different LPBF machines. Identically prepared samples were used for tensile, three-point bending, and toughness tests. Light microscopy (LM), scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD) analyses of microstructure were performed after testing. Differences were observed in microstructures, which reflected statistically significant differences in mechanical properties (one-way analysis of variance (ANOVA) and Scheffé post hoc test (α = 0.05)). The material produced on the 3D Systems DMP Dental 100 had 24 times greater elongation ε than the material produced on the Sysma MySint 100 device and the EOS M100 machine. On the other hand, the material produced on the EOS M100 had significantly higher hardness (HV0.2) than the other two produced materials. However, the microstructure of the Sysma specimens with its morphology deviates considerably from the studied group. LPBF-prepared Co-Cr dental alloys demonstrated significant differences in their microstructures and, consequently, mechanical properties.

The data about bond strength between digitally produced denture base resins and artificial teeth are scarce. Several studies investigated shear bond strength values of milled denture base resins and different types of artificial teeth. The purpose of the present study was to compare and evaluate the available evidence through a systematic review. A bibliographic search was conducted in PubMed, Scopus, and Web of Science to assess adequate studies published up to 1 June 2022. This review followed the PRISMA (Preferred Reporting Items for Systematic Reviews and Meta-Analyses) guidelines. The appropriate studies that determined the shear bond strength values between milled denture base resins and artificial teeth were selected. The initial search identified 103 studies, which were included in the PRISMA 2020 flow diagram for new systematic reviews. Three studies met the inclusion criteria, and all of them present a moderate risk of bias (score 6). Two studies found no statistical differences between heat-polymerized and CAD/CAM (milled) denture base materials when attached with different types of artificial teeth, while one study showed higher values of CAD/CAM (milled) denture base materials. Bonding agents ensure bonding strength at least similar to the conventional methods. In order to improve the quality of future studies, it would be advantageous to use a larger number of specimens with standardized dimensions and a blinded testing machine operator to decrease the risk of bias.

The etiopathogenesis of dental implant failure is multifactorial and may include numerous local and systemic factors, however, studies including both local and systemic factors are still lacking. Therefore, the aim of this study was to evaluate whe...