Based on compressive strength, sulfate resistance, mass change, and relative dynamic elastic modulus tests, and XRD and SEM analysis, the effects of sodium chloride (NaCl) and gypsum on the mechanical properties and resistance to sulfate attack of slag-based geopolymer concrete activated by quicklime as well as the mechanism of action were studied. The results indicate that: (1) with appropriate dosages of NaCl or gypsum, the compressive strength of geopolymer concrete can be increased by 55.8% or 245.3% at 3 days and 23.9% or 82.3% at 28 days, respectively. When NaCl and gypsum are combined, Friedel’s salt, Kuzel’s salt, and NaOH are generated, and the strength is increased by 90.8% at 3 days, and 180.3% at 28 days. (2) With 2% NaCl alone, the mass loss is reduced from 5.29% to 2.44%, and the relative dynamic elastic modulus is increased from 0.37 to 0.41. When compounded with 7.5% gypsum, the mass is increased by 0.26%, and the relative dynamic elastic modulus is increased to 1.04. With a further increase of NaCl to 4%, the mass is increased by 0.27%, and the relative dynamic elastic modulus is increased to 1.09. The sulfate corrosion resistance coefficient of geopolymer concrete is increased from 0.64 to 1.02 when it is immersed with 7.5% gypsum alone for 90 days, and it can be further increased to 1.11 when compounded with 4% NaCl. (3) The geopolymer prepared with sodium chloride: gypsum: quicklime: slag = 4:7.5:13.5:75 can be used to replace 32.5 slag Portland cement in plain concrete. The cost and carbon emissions are reduced by 25% and 48%, respectively, and the sulfate corrosion resistance coefficient is higher by 38.8% than with slag Portland cement.

In this paper, uniaxial compressive strength (UCS) test and three-point bending (TPB) test, together with an acoustic emission (AE) system, were performed to investigate the mechanical properties and AE characteristic changes of concrete with different graphite powder (GP) content. The results show that: (1) Poor adhesion and low interlocking of graphite with cement stone increase the initial defects of concrete, reducing its elastic modulus and the cyclo-hoop effect, and thus weakening the compressive strength. (2) For concrete with a low graphite content, the second sharp rise in ringing counts or energy released during the compressive process can be regarded as a failure alarm. However, as GP content increases, the second sharp rise fades away, while the first sharp rise becomes more visible. At high GP content, the first sharp rise is better for predicting failure. (3) The initial defects caused by GP significantly lower the initial fracture toughness, but its bridging effect greatly increases the critical crack mouth opening displacement and thus significantly enhances the unstable fracture toughness of concrete, by up to 9.9% at 9% GP content. (4) In contrast to compressive process, the sharp increase in AE signals preceding failure during the fracture process cannot be used to predict failure because it occurs too close to the ultimate load. However, as GP can significantly increase the AE signals and damage value in the stable period, such failure precursor information can provide a safety warning for damage development.

The performance analysis of mixed-exhaust turbofan engine with multi-annular rotating detonation duct burner (RDDB) is conducted for the first time, considering that the flow path of the bypass duct is ideal for a rotating detonation combustor (RDC). The configuration of the multi-annular rotating detonation combustor is constructed aiming at the advantages of a wider operation range and uniform outlet parameters over the single-annular one. Then, a parametric analysis model of the mixed-exhaust turbofan engine with a rotating detonation duct burner is developed. Thereafter, the effects of duct burner parameters on the engine performance and operating characteristics are investigated. The mixed-exhaust turbofan engine with a rotating detonation duct burner shows superior overall performance to that of one with an isobaric afterburner (ICAB) over a wide operation range. The separate-exhaust rotating detonation duct burner can hold characteristics that are higher than those of the mixed-exhaust one at lower values of fan pressure ratio, while the mixed-exhaust one corresponds to lower values of turbine inlet temperature. When the rotating detonation duct burner is “on,” the low-pressure rotor operating line moves toward the surge line on the low corrected shaft speed side but away from the surge line on the high corrected shaft speed side.

The associated effect of sodium chloride and dihydrate gypsum on the mechanical performance of a slag-based geopolymer activated by quicklime was investigated by compressive strength, shrinkage, and square circle anti-cracking tests of mortar with a 0.5 water–binder ratio and a 1:3 binder–sand ratio, as well as paste soundness, powder X-ray diffraction (XRD), thermogravimetric analysis (TGA), scanning electron microscopy with energy dispersive spectroscopy (SEM-EDS), and mercury intrusion porosimetry (MIP) of the paste. The results indicate that (1) when dihydrate gypsum is used alone, it combines with calcium aluminate hydrate (C-A-H) to form calcium sulfoaluminate hydrate (AFt), which encourages the hydration process of slag. A 7.5% addition can result in an increase of 97.33% and 36.92% in 3-day and 28-day compressive strengths, respectively. When NaCl is used by itself, it facilitates the condensation of the aluminum silicate tetrahedron unit and generates zeolite. A 2% dosage can lead to a 66.67% increase in the 3-day compressive strength, while causing a 15.89% reduction in the 28-day compressive strength. (2) The combined effect of 2% NaCl and 7.5% gypsum results in the formation of needle-like and rod-shaped AFt, Friedel’s salt, and plate-like Kuzel’s salt in the geopolymer. This leads to an increase in 3-day and 28-day compressive strengths by 148% and 37.85%, respectively. Furthermore, it reduces the porosity by 18.7%. (3) Both NaCl and gypsum enhance the paste soundness of the slag-based geopolymer, and they do no harm to the crack resistance of the geopolymer. The drying shrinkage of the geopolymer at 28 days is just 0.48 × 10⁻³, which is only 66.7% of OPC. This slag-based geopolymer has a simple preparation process, good volume stability, low raw material cost, low energy consumption, and low carbon emissions. It can be used instead of 32.5 slag Portland cement in plain concrete applications, and has high engineering, economic, and environmental values.

Dolomite rock powder (the waste stone residue in the production of machine-made sand and stone processing) and iron tailings powder formed by mineral processing industry are solid wastes, which occupy land resources, pollute the environment and release toxic substances without reasonable processing. The dolomite rock powder and iron tailings powder composing a large number of active substances could be advantageous to the cement-based materials. In this study, the electrical resistivity of cement paste and concrete was measured. Meanwhile, the influence of dolomite rock powder and iron tailings powder on the compressive strength of concrete was investigated. The electric flux of concrete was determined to estimate the chloride ion permeability. The scanning electron microscope (SEM) and X-ray diffraction were obtained to investigate the hydration of cement paste. Results showed the electrical resistivity of all specimens presented in this order: specimens with iron tailings < specimens with dolomite rock powder < blank specimens < specimens with ground granulated blast-furnace slag (GGBS) < specimens with fly ash. The correlation between electrical resistivity and curing age of cement paste or concrete has been deduced as a quadratic function. The addition of GGBS could improve the compressive strength of concrete. Meanwhile, when the other three types of mineral admixtures were added, 5% by mass ratio of the total binder materials was the optimum for the compressive strength. The curing ages, the fly ash, the GGBS and 5% dolomite rock powder or 5% iron tailings powder demonstrated a positive effect on the chloride ion impermeability. However, when higher dosages of dolomite rock powder or iron tailings powder were added, the effect was the opposite. Finally, the compactness of the microstructure and the Ca(OH)₂ of cement paste could be improved by a small dosage of dolomites or iron tailings (less than 5%).