Plasma electrolytic polishing (PEP) is an environment-friendly alternative to the conventional electrochemical polishing (EP), giving optimal surface properties and improved corrosion resistance with minimum energy and time consumption, which leads to both economic and environmental benefits. This paper is focused on the corrosion behavior of PEP treated AISI 316L stainless steel widely used as a biomaterial. Corrosion resistance of plasma electrolytic polished surfaces without/with chemical pretreatment (acid cleaning) is evaluated and compared with original non-treated (as received) surfaces by three independent test methods: electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PP), and exposure immersion test. All corrosion tests are carried out in the 0.9 wt.% NaCl solution at a temperature of 37 ± 0.5 °C to simulate the internal environment of a human body. The quality of tested surfaces is also characterized by optical microscopy and by the surface roughness parameters. The results obtained indicated high corrosion resistance of PEP treated surfaces also without chemical pretreatment, which increases the ecological benefits of PEP technology.

In order to increase the corrosion resistance of magnesium alloy AZ91 in corrosion environments containing chlorides, the alloy surface has been modified by plasma electrolytic oxidation (PEO). The chemical composition of electrolyte in the PEO process consisted of 12 g/L Na₃PO₄·12 H₂O and 1 g/L KOH, and a direct current was applied to the sample. The corrosion resistance of PEO coating and as-cast AZ91 (sample without PEO coating) was assessed using two different electrochemical methods: electrochemical impedance spectroscopy (EIS) and potentiodynamic polarisation (PDP) in 0.1 M NaCl at laboratory temperature. In addition to the electrochemical methods, the morphology of the oxidic coating was observed in the cross-sectional and top surface view by using the SEM technique. For better determination of the microstructure and PEO coating, chemical composition EDX analysis was used. The results of the experiments show that the formation of the PEO coating on AZ91 alloy has a more positive effect on the corrosion resistance in 0.1 M NaCl based on electrochemical methods than in the case of the formed coating on AZ31 alloy from the previous study. Based on electrochemical measurements in the selected environment, the formation of PEO coating on AZ91 was accompanied by a significant increase in polarisation resistance after short-term exposure compared to the as-cast surface. The EIS results showed a 73 times higher R_p value for PEO coated AZ91 when compared to the as-cast AZ91. Correspondingly, a 27 times lower i_corr value was observed for PEO coated AZ91 than in the case of substrate AZ91 in 0.1 M NaCl. At the same time, the typically porous and inhomogeneous structure of the formed PEO coating on the magnesium alloy AZ91 was demonstrated.

Plasma immersion ion implantation (PIII) of nitrogen is low-temperature surface technology which enables the improvement of tribological properties without a deterioration of the corrosion behavior of austenitic stainless steels. In this paper the corrosion properties of PIII-treated AISI 316L stainless steel surfaces are evaluated by electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PP) and exposure immersion tests (all carried out in the 0.9 wt. % NaCl solution at 37 ± 0.5 °C) and compared with a non-treated surface. Results of the three performed independent corrosion tests consistently confirmed a significant increase in the corrosion resistance after two doses of PIII nitriding.

A surface treatment process, composed of plasma electrolytic oxidation (PEO) and sealing by temporary oil preservation system containing corrosion inhibitors, was performed on AZ31 magnesium alloy in order to improve its corrosion resistance i...

The main objective of this article is to provide new information on the effects of mechanical pretreatment of AZ80 magnesium alloy ground with SiC emery papers of different grain sizes on the plasma electrolytic oxidation (PEO) process and corrosion properties of AZ80 in 0.1 M NaCl solution. Then, the roughness of the coated samples was measured by confocal microscopy. The corrosion properties of the ground and coated surfaces were determined by potentiodynamic polarization (PDP) within 1 h of exposure, and electrochemical impedance spectroscopy (EIS) was performed during 168 h of exposure at laboratory temperature. Consequently, the obtained results of the PDP measurements were evaluated by the Tafel analysis and the EIS evaluation was performed by the equivalent circuit analysis through Nyquist diagrams. The morphology and structure of PEO coatings were observed by scanning electron microscopy (SEM) through the secondary imaging technology, and the presence of certain elements in PEO coatings was analyzed by EDS analysis.