Thin (ca. 340 nm) chitosan coatings were deposited onto glass substrates via dip-coating, then modified with the methanol solution of decanoic anhydride (0.17-56 mM). NMR, FTIR and XPS measurements confirmed that the acylation degree increased from 18 % to 45 %, and at the highest degree, the whole layer was acylated homogeneously by the reagent molecules. The coating thickness increased (up to 60 %), and the refractive index decreased (from 1.541 to 1.532) due to the acylation, that was determined by UV-visible spectroscopy. The AFM did not reveal morphological changes, but wetting tests showed that the acylation rendered the coating hydrophobic (water contact angle increased from ca. 75° to 100°). The contact angle, however, decreased to 85° due to the development of a second molecular layer of the decanoic acid by-product at the highest (over 25 mM) reagent concentrations. XRD studies showed a self-assembling structuring of the alkyl-chains in the bulk phase, which occurred in the case of the highest degree of acylation. This also manifested itself in a significant decrease of the layer hygroscopicity: the swelling degree decreased from 40 % to 8 % in a saturated water atmosphere monitored by spectroscopic ellipsometry.

Chitosan coatings of 353 ± 12 nm thickness were prepared on glass and zinc substrates by dip-coating method to study their barrier-behaviour. The coatings were chemically modified to increase their degree of acetylation (DA) from ca. 44 % up to ca. 98 % resulting a quasi-chitin coating. The effect of the acetylation reaction was studied by infrared spectroscopy, and the structural changes of the native and acetylated coatings were investigated by UV-Vis spectrophotometry and X-ray diffraction. The surface properties of the coated samples were characterized by wettability measurements - advancing water contact angle decreased from ca. 80° (native) to ca. 43° (fully acetylated) - and microscopic (SEM, AFM) studies. The barrier behaviour of the chitosan layer depending on the DA was evaluated by electrochemical impedance spectroscopy studies and with a special mesoporous silica - chitosan bilayer system by measuring the amount of dye (Rhodamine 6G) accumulated in the silica through the chitosan coating during an impregnation step. These methods showed significant decrease in the barrier-effect of the coatings with increasing DA (accumulation of approximately six times more dye and a reduction of charge transfer resistance by an order of magnitude), due to the structural and ionization changes in the coatings.

Creating supersaturating drug delivery systems to overcome the poor aqueous solubility of active ingredients became a frequent choice for formulation scientists. Supersaturation as a solution phenomenon is, however, still challenging to understand, and therefore many recent publications focus on this topic. This work aimed to investigate and better understand the pH dependence of supersaturation of telmisartan (TEL) at a molecular level and find a connection between the physicochemical properties of the active pharmaceutical ingredient (API) and the ability to form supersaturated solutions of the API. Therefore, the main focus of the work was the pH-dependent thermodynamic and kinetic solubility of the model API, TEL. Based on kinetic solubility results, TEL was observed to form a supersaturated solution only in the pH range 3–8. The experimental thermodynamic solubility-pH profile shows a slight deviation from the theoretical Henderson–Hasselbalch curve, which indicates the presence of zwitterionic aggregates in the solution. Based on pK_a values and the refined solubility constants and distribution of macrospecies, the pH range where high supersaturation-capacity is observed is the same where the zwitterionic form of TEL is present. The existence of zwitterionic aggregation was confirmed experimentally in the pH range of 3 to 8 by mass spectrometry.

The optically active dibenzoyltartaric acid, tartaric acid, and its sodium salts were successfully applied to the optical resolution of (1R,2S)(1S,2R)-2-(methylamino)-1-phenylpropan-1-ol (EPH) and (1R,2R)(1S,2S)-2-amino-1-(4-nitrophenyl)propane-1,3-diol (AD) as resolving agents. It was observed that both compounds’ resolution using a mixture of salts of quasi-racemic resolving agents showed a change in chiral recognition under the same conditions compared to the result of the use of the single enantiomeric resolving agent. The changes are followed by detailed analytical (XRD, FTIR, and DSC) studies. Meanwhile, the DASH indexing software package was also tested on powder XRD patterns of pure initial materials and intermediate salt samples of high diastereomeric excess.

The glass transition temperature (T_g) is undoubtedly one of the most important characteristics of polymers, and investigating its dependence on their structure and composition is crucial from both fundamental and application points of view. This study deals with the unexpected relationship between T_g and the average molecular weight between crosslinking points (M_c) in nanophase-separated polystyrene-l-poly(dimethylsiloxane) (PSt-l-PDMS) and polystyrene-l-poly(dimethylsiloxane)/divinylbenzene (PSt-l-PDMS/DVB) polymer conetworks. In order to reveal the correlation between the T_g and M_c, a library of PSt-l-PDMS and PSt-l-PDMS/DVB conetworks was synthesized, and their compositions and T_gs were determined. Instead of the expected increase of T_g with decreasing M_c, a reverse correlation was found. Namely, the T_g decreases with decreasing M_c in these conetworks. Correlation analyses showed that the T_g linearly depends on 1/M_c, similar to the Fox–Flory relationship for homopolymers with their M_n, that is, T_g = T_g,ꝏ −K/M_c for the investigated conetworks, independent of the absence or presence of relatively low amounts of DVB as an additional small molecular weight crosslinker. This means that the PDMS macrocrosslinker acts like scissors by interrupting the mobility of the crosslinked PSt chains in the conetworks, and the T_g of the PSt segments will be close to that of PSt homopolymers with the same M_n as M_c, as found by comparison. Consistent with previous findings with other conetworks, the presence of the scissors effect of the macromolecular crosslinker in the PSt-l-PDMS and PSt-l-PDMS/DVB conetworks indicates that the scissors effect is a general phenomenon for polymer conetworks formed by crosslinking with a macromolecular crosslinker. The observed unusual T_g versus M_c relationship in the conetworks can be utilized in designing such novel materials with predetermined T_gs required for targeted applications.

In this paper we report the synthesis of a N, S co-doped metal free carbon cryogel obtained from a marine biomass derived precursor using urea as nitrogen source. Natural carrageenan intrinsically contains S and inorganic salt. The latter also serves as an activating agent during the pyrolytic step. The overall 11.6 atomic % surface heteroatom concentration comprises 5% O, 4.6% N and 1% S. The purified and annealed final carbon (CA) has a hierarchical pore structure of micro-, meso- and macropores with an apparent surface area of 1070 m²/g. No further treatment was applied. The gas adsorption potential of the samples was probed with H₂, CO₂ and CH₄, while the electrocatalytic properties were tested in an oxygen reduction reaction. The atmospheric CO₂ and CH₄ storage capacity at 0 °C in the low pressure range is very similar to that of HKUST-1, with the CO₂/CH₄ selectivity below 20 bar, even exceeding that of the MOF, indicating the potential of CA in biogas separation. The electrocatalytic behavior was assessed in an aqueous KOH medium. The observed specific gravimetric capacitance 377 F/g was exceeded only in B, N dual doped and/or graphene doped carbons from among metal free electrode materials. The CA electrode displays almost the same performance as a commercial 20 wt% Pt/C electrode. The oxygen reduction reaction (ORR) exhibits the 4-electron mechanism. The 500-cycle preliminary stability test showed only a slight increase of the surface charge.