Bobbin tool friction stir welding (BTFSW) utilizes a special tool that possesses two shoulders interconnected by a pin instead of one: the top shoulder and the pin in the conventional FSW tool. This greatly simplifies the kinematics in the otherwise complicated setup of FSW since the bottom shoulder forms the bottom surface of the weld, without the need for a backing plate. Moreover, the tool enters the base metal sideways and travels, forming the joint in a straight line while rotating, without the need for downward and upward motion at the beginning and end of the process. This paper presents a study on the BTFSW tool geometry and parameters on the risk of wormhole defect formation in the AA5005 aluminum–magnesium alloy and the wormhole effect on mechanical properties. It was shown that higher stress imposed by the tool geometry on the joint has a significant influence on heating, an effect similar to the increased rotational speed. Optimal kinematic and geometrical tool properties are required to avoid wormhole defects. Although weld tensile strengths were lower (between ~111 and 115 MPa) compared with a base metal (137 MPa), the ductile fracture was obtained. Furthermore, all welds had a higher impact strength (between ~20.7 and 27.8 J) compared with the base material (~18.5 J); it was found that the wormhole defect only marginally influences the mechanical properties of welds.

Bobbin tool friction stir welding (BTFSW) is a variant of the FSW process which uses the special two-shoulder tool that forms the top and bottom of a weld surface. As such, a significant simplification of the welding setup is achieved. One of the dominant parameters of the BTFSW process is the interference between the tool shoulder pinch gap and the weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact, and bend performance were studied, and appropriate correlations were devised. The base metal was an aluminum–magnesium alloy in which the interference varied in the range of 0.1 to 0.5 mm. Wormhole defects and irregularities were found in all specimens except in the specimen welded with 0.4 mm interference. An optimal interference of 0.4 mm resulted in the best mechanical properties, which, in terms of tensile strength and reduction of area, were similar to the base metal. Furthermore, the impact strength was significantly higher, which was attributed to the grain refinement effect in the nugget zone.

Bobbin Tool Friction Stir Welding (BTFSW) is a variant of FSW process using the special two shoulder tool that forms the top and bottom weld surface. As such, a significant simplification of welding setup is achieved. One of the dominant parameters of BTFSW process is the interference between tool shoulder pinch gap and weld metal thickness. In this research, the influence of interference of the square pin tool with convex shoulders on process temperature, microstructure, tensile, impact and bend performance were studied, and appropriate correlations were devised. The base metal was aluminum-magnesium alloy, with the interference varied in the range of 0.1 to 0.5 mm. The worm defects and irregularities were found in all specimens except in specimen welded with 0.4 mm interference. Optimal interference of 0.4 mm resulted in the highest mechanical properties, which, in terms of tensile strength and reduction of area were similar to the base metal. Furthermore, impact strength was significantly higher, which was attributed to grain refinement effect in the nugget zone.

Friction stir welding (FSW) is a solid-state welding process that uses a rotating tool to soften and stir the base metal, thereby joining it. A special type of tool that has attracted the interest of researchers is the so-called bobbin tool (BTFSW), which, unlike conventional tools with one shoulder, features two shoulders that envelop the base metal from both the top and bottom sides. As a result, significant tensile stresses develop on both sides of the weld, caused by the action of both tool shoulders. In this paper, this issue was addressed by applying laser shock peening (LSP), aiming to introduce compressive stresses, which can be useful as a post-processing technique for BTFSW on both weld sides. It was found that this process completely alters residual stresses in the treated area, from tensile to compressive, through shock waves that impart plastic deformation in the surface layer. It was shown that the LSP effect is more pronounced as the accumulated energy is higher. As a consequence, the microhardness values were significantly increased in the surface and subsurface layers, reaching a maximum depth of 480 to 780 µm for the lowest and highest accumulated laser energy, respectively, while surface roughness increased. While increasing compressive stresses and microhardness in the surface layer is beneficial from the point of view of fatigue resistance, increased roughness has a detrimental effect. Accumulated energy was hereby shown to have a higher effect compared to the maximal energy applied to the specimens.

Cost calculation is of huge importance both for determining a rational and competitive price of the product and preparation of offers according to customer's demand, where deadlines for sending offers are limited. In individual and small batch produc...