The implant surface features affect the osseointegration process. Different surface treatment methods have been applied to improve the surface topography and properties. Trace of different elements may appear on the implant surface, which can modify surface properties and may affect the body’s response. The aim was to evaluate the roughness based on the surface treatment received and the amount and type of trace elements found. Ninety implants (nine different surface treatment) were evaluated. Roughness parameters were measured using white-light-interferometry (WLI). The arithmetical mean for R_a, R_q, R_t, and R_z of each implant system was calculated, and Fisher’s exact test was applied, obtaining R_a values between 0.79 and 2.89 µm. Surface chemical composition was evaluated using X-ray photoelectron spectroscopy (XPS) at two times: as received by the manufacturer (AR) and after sputter-cleaning (SC). Traces of several elements were found in all groups, decreasing in favor of the Ti concentration after the sputter-cleaning. Within the limitations of this study, we can conclude that the surface treatment influences the roughness and the average percentage of the trace elements on the implant surface. The cleaning process at the implant surface should be improved by the manufacturer before assembling the implant.

The surface modifications of titanium dental implants play important roles in the enhancement of osseointegration. The objective of the present study was to test two different implant surface treatments on a rabbit model to investigate the osseointegration. The tested surfaces were: a) acid-etched surface with sandblasting treatment (SA) and b) an oxidized implant surface (OS). The roughness was measured by an interferometeric microscope with white light and the residual stress of the surfaces was measured with X-ray residual stress Bragg–Bentano diffraction. Six New Zealand white rabbits were used for the in vivo study. Implants with the two different surfaces (SA and OS) were inserted in the femoral bone. After 12 weeks of implantation, histological and histomorphometric analyses of the blocks containing the implants and the surrounding bone were performed. All the implants were correctly implanted and no signs of infection were observed. SA and OS surfaces were both surrounded by newly formed trabeculae. Histomorphometric analysis revealed that the bone–implant contact % (BIC) was higher around the SA implants (53.49 ± 8.46) than around the OS implants (50.94 ± 16.42), although there were no significant statistical differences among them. Both implant surfaces (SA and OS) demonstrated a good bone response with significant amounts of newly formed bone along the implant surface after 12 weeks of implantation. These results confirmed the importance of the topography and physico–chemical properties of dental implants in the osseointegration.

Titanium surface is an important factor in achieving osseointegration during the early wound healing of dental implants in alveolar bone. The purpose of this study was to evaluate sandblasted-etched surface implants to investigate the osseointegration. In the present study, we used two different types of sandblasted-etched surface implants, an SLA™ surface and a Nanoblast Plus™ surface. Roughness and chemical composition were evaluated by a white light interferometer microscope and X-ray photoelectron spectroscopy, respectively. The SLA™ surface exhibited the higher values (Ra 3.05 μm) of rugosity compared to the Nanoblast Plus™ surface (Ra 1.78 μm). Both types of implants were inserted in the femoral condyles of ten New Zealand white rabbits. After 12 weeks, histological and histomorphometric analysis was performed. All the implants were osseointegrated and no signs of infection were observed. Histomorphometric analysis revealed that the bone–implant contact % (BIC) ratio was similar around the SLA™ implants (63.74 ± 13.61) than around the Nanoblast Plus™ implants (62.83 ± 9.91). Both implant surfaces demonstrated a favorable bone response, confirming the relevance of the sandblasted-etched surface on implant osseointegration.

This study focuses on the fatigue behavior and bone-implant attachment for the more usual surfaces of the different CP-titanium dental implants. The implants studied were: as-received (CTR), acid etching (AE), spark-anodization (SA), and with a grit-blasted surface (GB). Residual stresses were determined by means of X-ray diffraction. The fatigue tests were carried out at 37°C on 160 dental implants, and the stress-failure (S-N) curve was determined. The fatigue tests showed that the grit-blasting process improved fatigue life. This is a consequence of the layer of compressive residual stresses that the treatment generates in titanium surfaces. Further, our aim was to assess and compare the short- and midterm bone regenerative potential and mechanical retention of the implants in bone of New Zealand rabbits. The mechanical retention after 4 and 10 weeks of implantation was evaluated with histometric and pull-out tests, respectively, as a measure of the osseointegration of the implants. The results demonstrated that the GB treatment produced microrough that accelerated bone tissue regeneration and increased mechanical retention in the bone bed at short periods of implantation in comparison with all other implants tested. The GB surface produced an improvement in mechanical long-time behavior and improved bone growth. These types of treated implants can have great potential in clinical applications, as evidenced by the outcomes of the current study.

The demand for synthetic graft materials in implant dentistry is rising. This systematic review aims to evaluate the survival rate of dental implants placed simultaneously with bone regeneration procedures using the material β-tricalcium phosphate, one of the most promising synthetic graft materials. The electronic search was conducted in PubMed, Scielo, and the Cochrane Central Register of Controlled Trials. Five randomized clinical trials, one non-randomized controlled clinical trial and four observational studies without control group were include. Implant survival rate and other clinical, radiographic, and histological parameters did not differ from those of implants placed simultaneously with another type of graft material, or placed in blood clots or natural alveolar ridges. Based on the available literature, β-tricalcium phosphate seems to be a promising graft material in implant dentistry. Nevertheless, more randomized clinical trials, with long follow-up periods, preoperative and postoperative CBCT, and histological analysis, are necessary to assess its long-term behavior.