The implant surface features affect the osseointegration process. Different surface treatment methods have been applied to improve the surface topography and properties. Trace of different elements may appear on the implant surface, which can modify surface properties and may affect the body’s response. The aim was to evaluate the roughness based on the surface treatment received and the amount and type of trace elements found. Ninety implants (nine different surface treatment) were evaluated. Roughness parameters were measured using white-light-interferometry (WLI). The arithmetical mean for R_a, R_q, R_t, and R_z of each implant system was calculated, and Fisher’s exact test was applied, obtaining R_a values between 0.79 and 2.89 µm. Surface chemical composition was evaluated using X-ray photoelectron spectroscopy (XPS) at two times: as received by the manufacturer (AR) and after sputter-cleaning (SC). Traces of several elements were found in all groups, decreasing in favor of the Ti concentration after the sputter-cleaning. Within the limitations of this study, we can conclude that the surface treatment influences the roughness and the average percentage of the trace elements on the implant surface. The cleaning process at the implant surface should be improved by the manufacturer before assembling the implant.

Implant dentistry constitutes a therapeutic modality in the prosthodontic treatment of partially and totally edentulous patients. This study reports a long-term evaluation of treatment by the early loading of acid-etched surface implants. Forty-eight partially and totally edentulous patients were treated with 169 TSA Defcon® acid-etched surface implants for prosthodontic rehabilitation. Implants were loaded after a healing free-loading period of 6–8 weeks in mandible and maxilla, respectively. Implant and prosthodontic clinical findings were followed during at least 17 years. Clinical results indicate a survival and success rate of implants of 92.9%, demonstrating that acid-etched surface achieves and maintains successful osseointegration. Five implants in three patients were lost during the healing period. Sixty-five prostheses were placed in 45 patients over the remaining 164 implants, 30 single crowns, 21 partially fixed bridges, 9 overdentures, and 5 full-arch fixed rehabilitations. A total of 12 implants were lost during the follow-up period. Mean marginal bone loss was 1.91 ± 1.24 mm, ranging from 1.1 to 3.6 mm. The most frequent complication was prosthetic technical complications (14.2%), followed by peri-implantitis (10.6%). The mean follow-up was of 214.4 months (208–228 months). Prosthodontic rehabilitation with an early-loading protocol over acid-etched surface implants is a successful implant treatment.

Two-pieces dental implants must provide stability of the implant-abutment-interface. The connection type and platform diameter could influence the biomechanical resistance and stress distribution. This study aims to evaluate the fatigue for different types of connections, external and internal, and different platform diameters. Three implant designs with the same length were used: (a) external hexagon/narrow platform; (b) internal double hexagon/narrow platform; (c) internal octagon/regular platform. A fatigue test was developed to establish the number of cycles needed before fracture. A 30º oblique load with a sinusoidal function of fatigue at a frequency of 15 Hz and 10% stress variation was applied to each system. The fatigue load limit (FLL) for design (a) was 190 N, being the nominal-curvature-moment (NCM) = 1.045; FLL = 150 N, with a NCM = 0.825 for (b), and FLL = 325 N, with a NCM = 1.788 for (c). The platform diameter affects the FLL, obtaining lower FLL on a narrow platform. The connection type interferes with the implant walls’ width, especially in narrow implants, making internal connections more unstable at this level. Long-term clinical studies to assess the restoration’s success rate and survival are mandatory.

The preservation of peri-implant tissues is an important factor for implant success. This study aimed to assess the influence of the surface features of a butt-joint platform on soft-tissue attachment and bone resorption after immediate or delayed implant placement. All premolars and first molars of eight Beagle dogs were extracted on one mandible side. Twelve-weeks later, the same surgery was developed on the other side. Five implants with different platform surface configurations were randomly inserted into the post-extracted-sockets. On the healed side, the same five different implants were randomly placed. Implants were inserted 1 mm subcrestal to the buccal bony plate and were connected to abutments. The primary outcome variables were the supracrestal soft tissue (SST) adaptation and the bone resorption related to the implant shoulder. The SST height was significantly larger in immediate implants (IC95% 3.9–4.9 mm) compared to delayed implants (IC95% 3.1–3.5 mm). Marginal bone loss tended to be higher in immediate implants (IC95% 0.4–0.9 mm) than in delayed implants (IC95% 0.3–0.8 mm). Linear-regression analysis suggested that the SST height was significantly affected by the configuration of the platform (0.3–1.9 mm). Roughened surface platforms resulted in higher SST height when compared to machined surface platforms. Marginal bone loss was less pronounced in roughened designs.

The use of immediate implants in the aesthetic area is a technique widely used in modern implantology. The characteristics of the patient, the implant, and the surgical procedure used may influence the final results. The aim was to assess whether the implant design affects primary (P.S.) and secondary stability (S.S.), bone level (B.L.), and PES/WES evaluation. Twenty implants with two different designs (n = 10) were immediately placed and randomly located in the upper anterior maxilla with no grafting material. Implant-Stability-Quotient (ISQ), B.L., and Pink-Esthetic-Score/White-Esthetic-Score (PES/WES) were evaluated. Shapiro–Wilk normality test was performed to determine the sample normality, as the data did not follow a normal distribution, the Wilcoxon-Mann–Whitney test was applied (p < 0.05). ISQ was determined at placement (PS): control 59.1 (C.I.54.8–63.3); experimental 62.2(C.I.60.1–64.2) and three months after placement (SS): control 62.2.1 (C.I.53.3–71.0); experimental 67.2(C.I.65.8–68.5). The BL was measured at three months after placement: control 0.38 mm (C.I.− 0.06 to + 0.83); experimental 0.76 mm (C.I.0.33–1.19) and at 12 months post-loading: control 0.07 mm (C.I.− 0.50–0.65); experimental 0.90 mm (C.I.0.38–1.42). PES/WES values were evaluated for the control group: 15 (C.I.12.68–17.32), and for the experimental group 15.20 (C.I.11.99–18.41). No significant differences were shown between both implant designs. A good grade of osseointegration and primary/secondary stability was achieved, as well as proper maintenance of crestal bone and adequate PES/WES scores. The criteria for selection for the ideal patient for immediate implant placement is essential.ClinicalTrials Protocol ID: NCT04343833.

The aims of this study were to evaluate the effect on shear bond strength (SBS), adhesive remnant, and enamel surface of repeated bonding of new brackets on the same tooth using different methods of enamel conditioning. One hundred and thirty-five bovine incisors were used. Brackets were bonded to enamel using one of the following conditioning procedures: (1) 37 per cent phosphoric acid, (2) 37 per cent phosphoric acid (prior to first bond but not for further bonds), (3) Transbond Plus Self Etching Primer® (TSEP), and (4) non-rinse-conditioner (NRC). Brackets were sequentially bonded and debonded three times following the same conditioning procedure with the exception of group 2 where 37 per cent phosphoric acid was not reapplied prior to the second and third bonding sequences. SBS and adhesive remnant were evaluated for each debond. Scanning electron microscopy observations were made for each conditioning sequence. Statistical analysis was undertaken using ANOVA, Mann–Whitney, and Kruskal–Wallis tests. Bond strength and adhesive remnant values were similar across the four groups for the first and second bonding sequences. At the third sequence, SBS was significantly less (P < 0.008) for group 2 (5.71 ± 1.56 MPa) than for group 1 (9.42 ± 2.75 MPa) and the adhesive remnant was significantly lower (P < 0.008) for group 2 (6.93% ± 3.34) than for the other groups (group 1: 16.95 ± 4.99 per cent, group 3: 14.40 ± 5.11 per cent, and group 4: 14.60 ± 5.33 per cent). When comparing the SBS and adhesive remnant of the three bonding/debonding sequences within each group, both the SBS and adhesive remnant for group 2 (SBS: 5.71 ± 1.56 MPa and adhesive remnant: 6.93 ± 3.34%) at the third sequence were significantly less (P < 0.017) than at the first (SBS: 10.44 ± 3.55 MPa and adhesive remnant: 13.81 ± 5.59%) and second (SBS: 9.23 ± 2.69 MPa and adhesive remnant: 15.32 ± 6.85%) sequences. Enamel changes were similar across all groups. TSEP and NRC produced bonds that were similar to acid etching. When acid etching is used, it is possible to avoid etching for a second bond but not for following bonds.