The implant surface features affect the osseointegration process. Different surface treatment methods have been applied to improve the surface topography and properties. Trace of different elements may appear on the implant surface, which can modify surface properties and may affect the body’s response. The aim was to evaluate the roughness based on the surface treatment received and the amount and type of trace elements found. Ninety implants (nine different surface treatment) were evaluated. Roughness parameters were measured using white-light-interferometry (WLI). The arithmetical mean for R_a, R_q, R_t, and R_z of each implant system was calculated, and Fisher’s exact test was applied, obtaining R_a values between 0.79 and 2.89 µm. Surface chemical composition was evaluated using X-ray photoelectron spectroscopy (XPS) at two times: as received by the manufacturer (AR) and after sputter-cleaning (SC). Traces of several elements were found in all groups, decreasing in favor of the Ti concentration after the sputter-cleaning. Within the limitations of this study, we can conclude that the surface treatment influences the roughness and the average percentage of the trace elements on the implant surface. The cleaning process at the implant surface should be improved by the manufacturer before assembling the implant.

The surface modifications of titanium dental implants play important roles in the enhancement of osseointegration. The objective of the present study was to test two different implant surface treatments on a rabbit model to investigate the osseointegration. The tested surfaces were: a) acid-etched surface with sandblasting treatment (SA) and b) an oxidized implant surface (OS). The roughness was measured by an interferometeric microscope with white light and the residual stress of the surfaces was measured with X-ray residual stress Bragg–Bentano diffraction. Six New Zealand white rabbits were used for the in vivo study. Implants with the two different surfaces (SA and OS) were inserted in the femoral bone. After 12 weeks of implantation, histological and histomorphometric analyses of the blocks containing the implants and the surrounding bone were performed. All the implants were correctly implanted and no signs of infection were observed. SA and OS surfaces were both surrounded by newly formed trabeculae. Histomorphometric analysis revealed that the bone–implant contact % (BIC) was higher around the SA implants (53.49 ± 8.46) than around the OS implants (50.94 ± 16.42), although there were no significant statistical differences among them. Both implant surfaces (SA and OS) demonstrated a good bone response with significant amounts of newly formed bone along the implant surface after 12 weeks of implantation. These results confirmed the importance of the topography and physico–chemical properties of dental implants in the osseointegration.

Titanium surface is an important factor in achieving osseointegration during the early wound healing of dental implants in alveolar bone. The purpose of this study was to evaluate sandblasted-etched surface implants to investigate the osseointegration. In the present study, we used two different types of sandblasted-etched surface implants, an SLA™ surface and a Nanoblast Plus™ surface. Roughness and chemical composition were evaluated by a white light interferometer microscope and X-ray photoelectron spectroscopy, respectively. The SLA™ surface exhibited the higher values (Ra 3.05 μm) of rugosity compared to the Nanoblast Plus™ surface (Ra 1.78 μm). Both types of implants were inserted in the femoral condyles of ten New Zealand white rabbits. After 12 weeks, histological and histomorphometric analysis was performed. All the implants were osseointegrated and no signs of infection were observed. Histomorphometric analysis revealed that the bone–implant contact % (BIC) ratio was similar around the SLA™ implants (63.74 ± 13.61) than around the Nanoblast Plus™ implants (62.83 ± 9.91). Both implant surfaces demonstrated a favorable bone response, confirming the relevance of the sandblasted-etched surface on implant osseointegration.

The demand for synthetic graft materials in implant dentistry is rising. This systematic review aims to evaluate the survival rate of dental implants placed simultaneously with bone regeneration procedures using the material β-tricalcium phosphate, one of the most promising synthetic graft materials. The electronic search was conducted in PubMed, Scielo, and the Cochrane Central Register of Controlled Trials. Five randomized clinical trials, one non-randomized controlled clinical trial and four observational studies without control group were include. Implant survival rate and other clinical, radiographic, and histological parameters did not differ from those of implants placed simultaneously with another type of graft material, or placed in blood clots or natural alveolar ridges. Based on the available literature, β-tricalcium phosphate seems to be a promising graft material in implant dentistry. Nevertheless, more randomized clinical trials, with long follow-up periods, preoperative and postoperative CBCT, and histological analysis, are necessary to assess its long-term behavior.

The surface modification by the formation of apatitic compounds, such as hydroxyapatite, improves biological fixation implants at an early stage after implantation. The structure, which is identical to mineral content of human bone, has the potential to be osteoinductive and/or osteoconductive materials. These calcium phosphates provoke the action of the cell signals that interact with the surface after implantation in order to quickly regenerate bone in contact with dental implants with mineral coating. A new generation of calcium phosphate coatings applied on the titanium surfaces of dental implants using laser, plasma-sprayed, laser-ablation, or electrochemical deposition processes produces that response. However, these modifications produce failures and bad responses in long-term behavior. Calcium phosphates films result in heterogeneous degradation due to the lack of crystallinity of the phosphates with a fast dissolution; conversely, the film presents cracks, which produce fractures in the coating. New thermochemical treatments have been developed to obtain biomimetic surfaces with calcium phosphate compounds that overcome the aforementioned problems. Among them, the chemical modification using biomineralization treatments has been extended to other materials, including composites, bioceramics, biopolymers, peptides, organic molecules, and other metallic materials, showing the potential for growing a calcium phosphate layer under biomimetic conditions.

Current patterns of preventive antibiotic prescribing are encouraging the spread of antimicrobial resistance. Recently, the Spanish Society of Implants (SEI) developed the first clinical practice guidelines published to date, providing clear guidelines on how to prescribe responsible and informed preventive antibiotic therapy (PAT) based on the available scientific evidence on dental implant treatments (DIs). The present document aims to summarise and disseminate the recommendations established by this expert panel. These were based on the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement. Studies were analysed using the Scottish Intercollegiate Guidelines Network (SIGN) checklist templates and ranked according to their level of evidence. They were then assigned a level of recommendation using the Grading of Recommendations, Assessment, Development and Evaluation system (GRADE). Guidelines were established on the type of PAT, antibiotic and dosage of administration in the placement of DIs without anatomical constraints, in bone augmentation with the placement of DIs in one or two stages, placement of immediate DIs, sinus elevations, implant prosthetic phase, as well as recommendations in patients allergic to penicillin. Therefore, the PAT must be adapted to the type of implant procedure to be performed.