This study investigates the degradation of aircraft paint and its impact on aerodynamic performance, using the PZL M-20 “Mewa” aircraft as a case study. Paint samples were collected from both damaged and intact areas of the airframe and analyzed using electron paramagnetic resonance (EPR) spectroscopy, scanning electron microscopy (SEM), and aerodynamic testing. One of the major challenges addressed in this work was the non-destructive identification of chemical aging effects in operational paint coatings and their correlation with aerodynamic behavior. The application of EPR spectroscopy in conjunction with real-world aerodynamic testing on naturally degraded surfaces represents an innovative approach that offers both scientific insight and practical guidance for maintenance practices. The results indicate significant deterioration in aerodynamic characteristics—such as increased drag and reduced lift—due to coating damage, particularly around riveted and bolted joints. EPR spectra revealed a notable increase in the density of unpaired electron spins in aged coatings, confirming ongoing oxidative degradation processes. While this study was limited to a single aircraft, the findings highlight the critical importance of regular inspection and maintenance of paint coatings to ensure flight safety and operational efficiency.

Recently an extensive growth in the market for Unmanned Aerial Vehicles (UAVs, drones) has been observed. Because of numerous advantages, their application in various areas is wide, starting with military, through civilian – specialized up to amateur. The world market for civilian commercial...

The article presents the impact of sampling interval ΔX=ΔY upon the precision of parametrical assessment of roughness of selected surfaces. Moreover this study introduces theoretical analysis of sampling interval selection based on analysis of the probability of covering an unordered set of...

The article presents an electron magnetic resonance study of metal paints in terms of identification and selection of appropriate pigment components based on the summation of spectral components. Research was carried out to assess the durability of paints on the basis of the detection of free...

The effect of a weak magnetic field (B = 0.17 T) and X-irradiation (D < 520 Gy) on the rearrangement of the defective structure of near-surface p-type silicon layers was studied. It was established that the effect of these external fields increases the positive accumulated charge in the region of spatial charge (RSC) and in the SiO₂ dielectric layer. This can be caused by both defects in the near-surface layer of the semiconductor and impurities contained in the dielectric layer, which can generate charge carriers. It was found that the near-surface layers of the barrier structures contain only one deep level in the silicon band gap, with an activation energy of Ev + 0.38 eV. This energy level corresponds to a complex of silicon interstitial atoms Si_I+Si_I. When X-irradiated with a dose of 520 Gy, a new level with the energy of Ev + 0.45 eV was observed. This level corresponds to a point boron radiation defect in the interstitial site (B_I). These two types of defect are effective in obtaining charge carriers, and cause deterioration of the rectifier properties of the silicon barrier structures. It was established that the silicon surface is quite active, and adsorbs organic atoms and molecules from the atmosphere, forming bonds. It was shown that the effect of a magnetic field causes the decay of adsorbed complexes at the Si–SiO₂ interface. The released hydrogen is captured by acceptor levels and, as a result, the concentration of more complex Si–H₃ complexes increases that of O₃–Si–H.

The aim of this study was to present a methodology for predicting changes in uric acid concentrations in the blood of chronically hemodialyzed patients based on an optical measurement of the intensity of selected wavelengths in the dialysate. Blood samples were taken from the arterial line every 30 min throughout the hemodialysis period, to measure uric acid levels. Simultaneously, optical measurements were made on dialysate flowing from the dialyzer. Uric acid concentration can be measured either directly from the blood or from dialyzer outflow with acceptable error. In addition, both methods reveal any increased dynamics in uric acid concentration in the initial phase of hemodialysis. The wavelength of the light was adjusted for optimal uric acid particle detection. Comparing the uric acid concentration measured in the blood of patients with the intensity of wave absorption in the dialysate, the functional relationship between the uric acid concentration levels was determined. Using the optical method for measuring uric acid concentration in the dialysate, the concentration of uric acid in the blood during hemodialysis can be non-invasively and accurately estimated. This method can be used to assess the adequacy of hemodialysis by computer acquisition of uric acid concentrations determined in on-line dialysate.