Flexible screen-printed electrodes (SPE) were modified in a simple manner with different composite nanomaterials based on carbon allotropes, polymers, and metallic nanoparticles, for amperometric detection of nitrites in soil. Multiwalled carbon nanotubes (MWCNT), chitosan (CS), silver nanoparticles (AgNPs), 1,8-diaminonaphthalene (1,8-DAN), and a sol-gel (SG) matrix were used for modification of the carbon paste working electrodes. Sensitive and selective detection of nitrite was achieved by using a MWCNT-CS-modified sensor, in acetate buffer at pH 5, at an applied potential of 0.58 V vs. Ag/AgCl. The MWCNT-CS-based sensor displayed a specific sensitivity of 204.4 mA·M⁻¹·cm⁻², with a detection limit of 2.3 µM (S/N = 3) in a linear range up to 1.7 mM, showing good stability, reproducibility, and selectivity towards other interfering species. A miniaturized portable system using the developed flexible electrochemical MWCNT-CS-based sensors was dedicated for the detection of nitrite in different samples of soil solutions extracted by using suction lysimeters.

The objective of this work was to develop a sustainable process for the extraction of anthocyanins from red cabbage byproducts using, for the first time, apple vinegar in extractant composition. Our results showed that the mixture 50% (v/v) ethanol–water, acidified with apple vinegar, used in the proportion of 25 g of red cabbage by-products per 100 mL of solvent, was the best solvent for the preparation of an anthocyanin extract with good stability for food applications. The chemical characterization of this extract was performed by FTIR, UV-VIS, HPLC-DAD, and ICP-OES. The stability was evaluated by determining the dynamics of the total polyphenol content (TPC) and the total monomeric anthocyanin pigment content (TAC) during storage. On the basis of the statistical method for analysis of variance (ANOVA), the standard deviation between subsamples and the repeatability standard deviation were determined. The detection limit of the stability test of TPC was 3.68 mg GAE/100 g DW and that of TAC was 0.79 mg Cyd-3-Glu/100 g DW. The red cabbage extract has high TPC and TAC, good stability, and significant application potential. The extracted residues, depleted of anthocyanins and polyphenols with potential allelopathic risks, fulfill the requirements for a fertilizing product and could be used for soil treatment.

Nanotechnology can offer a series of new “green” and eco-friendly methods for developing different types of nanoparticles, among which the development of nanomaterials using plant extracts (phytosynthesis) represents one of the most promising areas of research. This present study details the use of lavender flowers (Lavandula angustifolia Mill., well-known for their use in homeopathic applications) for the biosynthesis of silver nanoparticles with enhanced antioxidant and antibacterial properties. Several qualitative and quantitative assays were carried out in order to offer an image of the extracts’ composition (the recorded total phenolics content varied between 21.0 to 40.9 mg GAE (gallic acid equivalents)/g dry weight (d.w.), while the total flavonoids content ranged between 3.57 and 16.8 mg CE (catechin equivalents)/g d.w.), alongside modern analytical methods (such as gas chromatography-mass spectrometry—GC-MS, quantifying 12 phytoconstituents present in the extracts). The formation of silver nanoparticles (AgNPs) using lavender extract was studied by UV-Vis spectroscopy, Fourier-transform infrared spectrometry (FTIR), scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS)/zeta potential, with the selected nanoparticles having crystallite sizes of approx. 14.55 nm (AgNP-L2) and 4.61 nm, respectively (for AgNP-L4), and hydrodynamic diameters of 392.4 nm (for AgNP-L2) and 391.6 nm (for AgNP-L4), determined by DLS. A zeta potential of around −6.4 mV was displayed for both samples while presenting as large aggregates, in which nanoparticle clusters with dimensions of around 130–200 nm can be observed. The biomedical applications of the extracts and the corresponding phytosynthesized nanoparticles were evaluated using antioxidant and antimicrobial assays. The obtained results confirmed the phytosynthesis of the silver nanoparticles using Lavandula angustifolia Mill. extracts, as well as their antioxidant and antimicrobial potential.

Raw materials, such as collagen and chitosan, obtained from by-products from the food industry (beef hides and crustacean exoskeletons), can be used to obtain collagen–chitosan composite biomaterials, with potential applications in regenerative medicine. Functionalization of these composite biomaterials is a possibility, thus, resulting in a molecule with potential applications in regenerative medicine, namely clotrimazole (a molecule with antibacterial, antifungal, and antitumor activity), at a mass ratio (collagen–chitosan–clotrimazole) of 1:1:0.1. This functionalized composite biomaterial has great potential for application in regenerative medicine, due to the following properties: (1) it is porous, and the pores formed are interconnected, due to the use of a mass ratio between collagen and chitosan of 1:1; (2) the size of the formed pores is between 500–50 μm; (3) between collagen and chitosan, hydrogen bonds are formed, which ensure the unity of composite biomaterial; (4) the functionalized bio-composite exhibits in vitro antimicrobial activity for Candida albicans, Staphylococcus aureus, and Staphylococcus aureus MRSA; for the latter microorganism, the antimicrobial activity is equivalent to that of the antibiotic Minocycline; (5) the proliferation tests performed on a standardized line of normal human cells with simple or composite materials obtained by lyophilization do not show cytotoxicity in the concentration range studied (10–500) μg/mL.

The microencapsulation of bioactive compounds from rapeseed oil using sodium alginate, in the presence and absence of an ultrasonic (US) field, is reported. A Box–Behnken experimental design is used to investigate the influence of process parameters on the microencapsulation yield; then, the response surface methodology is applied, to find their values ensuring its optimum yield. The operating parameters investigated are the ratio of sodium alginate to rapeseed oil, the microencapsulation time and the concentration of the calcium chloride solution. The US bath was used at its nominal power, and the microencapsulation temperature was kept at 20 °C, with a thermostat, for all experiments. A detailed study on the comparison of the two microencapsulation techniques (in the presence and absence of the US field) was carried out. Good results were obtained in the presence of the US field for optimal conditions, when the microencapsulation yield was 90.25 ± 0.02%, higher than the microencapsulation process performed in the absence of the US field, 87.11 ± 0.02%. The results also showed that the use of the US field (optimal conditions) led to an increase in encapsulation efficiency, total phenolic content and antioxidant capacity (76.56 ± 0.02%, 324.85 ± 0.01 mg GAE/g and 57.05 ± 0.12 mg/mL). The physicochemical description of microcapsules was performed using modern characterization methods. These results indicate that by increasing the microencapsulation yield of bioactive compounds through sonication, the process aims to achieve a uniform size distribution of microcapsules.