PCMs (phase change materials) are ideal for thermal management solutions in buildings. This is because they release and store thermal energy during melting and freezing. When this material freezes, it releases a lot of energy in the form of latent heat of fusion or crystallization energy. Conversely, when the material melts, it absorbs the same amount of energy from its surroundings as it changes from a solid to a liquid state. In this study, Oriental spruce (Picea orientalis L.) sapwood was impregnated with three different commercial PCMs. The biological properties and the hygroscopic and thermal performance of the PCM-impregnated wood were studied. The morphology of PCM-impregnated wood was characterized through the use of scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). PCM-impregnated wood demonstrated low performance in terms of storing and releasing heat during phase change processes, as confirmed by DSC. The results show that PCMs possess excellent thermal stability at working temperatures, and the most satisfying sample is PCM1W, with a phase change enthalpy of 40.34 J/g and a phase change temperature of 21.49 °C. This study revealed that PCMs are resistant to wood-destroying fungi. After the 96 h water absorption test, the water absorption of the wood samples decreased by 28%, and the tangential swelling decreased by 75%. In addition, it has been proven on a laboratory scale that the PCM material used is highly resistant to biological attacks. However, large-scale pilot studies are still needed.

Bamboo is suitable to be a material for the production of new products that can be used indoors and outdoors. Five-, seven- and nine-ply laminated woven bamboo mat boards from semantan bamboo, Gigantochloa scortechinii, were fabricated in this study. G. scortechinii has been used commercially in a structural application and is easily available in Malaysia. The present work investigated the physico-mechanical properties and flammability of the laminated bamboo mat boards as a function of the number of ply. Phenol-formaldehyde resin was used as a binder. The panels’ density, physical, mechanical properties, formaldehyde emission and flammability were evaluated. As the number of ply increased, the density of the laminated boards decreased. Similarly, the highest modulus of elasticity was found in 5-ply laminated boards. However, the lowest modulus of rupture was also measured in 5-ply laminated boards. Regarding shear strength, 5-ply and 7-ply laminated boards outperformed 9-ply laminated boards. Meanwhile, 7-ply laminated boards exhibited the highest dimensional stability, as evidenced by the lowest water absorption and thickness swelling. In terms of flammability, all composites are classified as V-0 because the burning stops within 10 s and no flaming drips are observed.

Due to its inferior properties, oil palm wood (OPW) extracted from the inner layer of the oil palm (Elaeis guineensis) trunk, referred as inner OPW in this study, is frequently regarded as a waste. Phenolic resin treatment and lamination of inner OPW with other hardwoods may be an excellent way to improve the properties of the inner OPW. In this study, inner OPW were treated with two different concentrations (15% and 20%) of low molecular weight phenol formaldehyde resin (LmwPF) and compressed at different compression ratios (10%, 20%, and 30%). The physical and mechanical properties of the modified inner OPW’s were evaluated according to British Standards (BS) 373: 1957. The results revealed that inner OPW treated with the highest compression ratio (30%) and resin concentration (20%) exhibited the highest weight percent gain, polymer retention and density. In the following phase of the research, the treated inner OPW was used as the core layer in the fabrication of a three-layer laminated compreg hybrid composites, with untreated and treated sesenduk (Endospermum diadenum) wood serving as the face and back layers. The compression ratios of 10% and 20% and resin concentrations of 10% and 20% were used in this phase of study as laminated boards made with 30% compression ratio failed. The findings showed that resin concentration had a significant impact on both the inner OPW and the laminated compreg hybrid panels. Markedly, higher resin concentrations (20%) resulted in improved physical properties, i.e., thickness swelling and water absorption, as well as enhanced mechanical properties (modulus of rupture and modulus of elasticity). Although compression ratios had no significant effect on the properties of the laminated products, those compressed at higher compression ratios (20%) performed slightly better than the panels compressed at lower compression ratios (10%).