The global problem of microplastics in the environment is “inspiring” scientists to find environmentally friendly and economically viable methods to remove these pollutants from the environment. Advanced oxidation processes are among the most promising methods. In this work, the potential of Fenton, photo-Fenton, and Fenton-like processes for the degradation of microplastics from low-density polyethylene (LDPE), polypropylene (PP), and poly(vinyl chloride) (PVC) in water suspensions was investigated. The influence of three parameters on the efficiency of the degradation process was tested: the pH of the medium (3–7), the mass of added iron (10–50 times less than the mass of microplastics), and the mass of added H₂O₂ (5–25 times more than the mass of added iron). The effectiveness of the treatment was monitored by FTIR-ATR spectroscopy. After 60-min treatments, the PP microparticles were found to be insensitive. In the Fenton treatment of PVC and the photo-Fenton treatment of LDPE and PVC, changes in the FTIR spectra related to the degradation of the microplastics were observed. In these three cases, the treatment parameters were optimized. It was found that a low pH (3) and a high iron mass (optimal values were 1/12 and 1/10 of the mass of the microplastics for LDPE and PVC, respectively) favored all three. The degradation of LDPE by the photo-Fenton treatment was favored by high H₂O₂ concentrations (25 times higher than the mass of iron), while these concentrations were significantly lower for PVC (11 and 15 times for the Fenton and photo-Fenton treatment, respectively), suggesting that scavenging activity occurs.

In the last two decades, microplastics (MP) have been identified as an emerging environmental pollutant. Due to their small size, MP particles may easily enter the food chain, where they can have adverse effects on organisms and the environment in general. The common methods for the removal of pollutants from the environment are not fully effective in the elimination of MP; thus, it is necessary to find a more suitable treatment method(s). Among the various approaches tested, biodegradation is by far the most environmentally friendly and economically acceptable remediation approach. However, it has serious drawbacks, generally related to the rather low removal rate and often insufficient efficiency. Therefore, it would be beneficial to use some of the less economical but more efficient methods as pretreatment prior to biodegradation. Such pretreatment would primarily serve to increase the roughness and hydrophilicity of the surface of MP, making it more susceptible to bioassimilation. This review focuses on advanced oxidation processes (AOPs) as treatment methods that can enhance the biodegradation of MP particles. It considers MP particles of the six most commonly used plastic polymers, namely: polyethylene, polypropylene, polystyrene, polyvinyl chloride, polyethylene terephthalate and polyurethane. The review highlights organisms with a high potential for biodegradation of selected MP particles and presents the potential benefits that AOP pretreatment can provide for MP biodegradation.

The harmful effects of microplastics are not yet fully revealed. This study tested harmful effects of polyethylene (PE), polypropylene (PP), polystyrene (PS), polyvinyl chloride (PVC), and polyethylene terephthalate (PET) microplastics were tested. Growth inhibition tests were conducted using three microorganisms with different characteristics: Scenedesmus sp., Pseudomonas putida, and Saccharomyces cerevisiae. The growth inhibition test with Scenedesmus sp. is relatively widely used, while the tests with Pseudomonas putida and Saccharomyces cerevisiae were, to our knowledge, applied to microplastics for the first time. The influence of concentration and size of microplastic particles, in the range of 50–1000 mg/L and 200–600 µm, was tested. Determined inhibitions on all three microorganisms confirmed the hazardous potential of the microplastics used. Modeling of the inhibition surface showed the increase in harmfulness with increasing concentration of the microplastics. Particle size showed no effect for Scenedesmus with PE, PP and PET, Pseudomonas putida with PS, and Saccharomyces cerevisiae with PP. In the remaining cases, higher inhibitions followed a decrease in particle size. The exception was Scenedesmus sp. with PS, where the lowest inhibitions were obtained at 400 µm. Finally, among the applied tests, the test with Saccharomyces cerevisiae proved to be the most sensitive to microplastics.

Microplastics are an emerging class of recalcitrant organic pollutants that are of general scientific and public interest nowadays. It would be ideal to remove microplastics from the environment through biodegradation, as biodegradation is a highly ecological and economically acceptable approach. Unfortunately, the efficiency of biodegradation of conventional plastic polymers is low. The application of a suitable pretreatment could increase the efficiency of biodegradation. In this study, the applicability of UV-C/H₂O₂ and UV-C/S₂O₈²⁻ advanced oxidation processes as pretreatments for the biodegradation of polystyrene and poly(vinyl chloride) microplastics by the yeast Candida parapsilosis was investigated. For the investigated range (pH 4–10, peroxide concentration up to 20 mM and treatment duration up to 90 min), the UV-C/H₂O₂ process proved to be more effective in degrading polystyrene microplastics, while the UV-C/S₂O₈²⁻ process was more efficient at degrading poly(vinyl chloride) microplastics. Samples pretreated under optimal conditions (90 min treatment time at a pH of 5.7 and H₂O₂ concentration of 20.0 mM for polystyrene samples; 90 min treatment time at a pH of 8.6 and S₂O₈²⁻ concentration of 11.1 mM for poly(vinyl chloride) samples) were subjected to biodegradation by Candida parapsilosis. The biodegradation conditions included an agitation speed of 156 rpm and an initial pH of 5.7 for the experiments with the polystyrene samples, while an agitation speed of 136 rpm and an initial pH of 4.9 were used for the poly(vinyl chloride) experiments. The initial value of the optical density of the yeast suspension was 1.0 in both cases. The experiments showed a positive effect of the pretreatment on the number of yeast cells on the surface of the microplastics.

Biodegradation is the most environmentally friendly and, at the same time, economically acceptable approach to removing various pollutants from the environment. However, its efficiency in removing microplastics (MPs) from the environment is generally low. The successful biodegradation of MPs requires microorganisms capable of producing enzymes that degrade MP polymers into compounds that the microorganisms can use as a source of carbon and energy. Therefore, scientists are screening and characterizing microorganisms that can degrade MPs more efficiently. These microorganisms are often isolated from sites contaminated with MPs because the microorganisms living there are adapted to these pollutants and should be able to better degrade MPs. In this study, five bacterial strains and five yeast strains were isolated from various environmental samples including activated sludge, compost, river sediment, and biowaste. Among them, screening was performed for bacteria and yeasts with the highest potential for the biodegradation of polystyrene (PS) and polyvinyl chloride (PVC) MPs, and the bacterium Delftia acidovorans and the yeast Candida parapsilosis were identified as the best candidates. Optimization of biodegradation of the selected MPs by each of these two microorganisms was performed, focusing on the influence of cell density, agitation speed and pH of the medium. It was found that within the selected experimental ranges, high values of cell density, low agitation speed, and a slightly basic medium favored the biodegradation of PS and PVC MPs by Delftia acidovorans. In the case of Candida parapsilosis, favorable conditions also included high cell density followed by a slightly higher, but not maximum, agitation speed and a weakly acidic medium. Broad spectroscopic and imaging methods indicated that Delftia acidovorans and Candida parapsilosis better adapt to PVC MPs to use it as a carbon and energy source.

The increasing presence of SARS-CoV-2 antivirals (SASs) in wastewater threatens aquatic ecosystems, making it necessary to better understand their removal efficiency during biological treatment. This study evaluates the removal percentages, kinetic mechanisms, and toxicity profiles of six SASs, daclatasvir (DCV), darunavir (DRV), favipiravir (FAV), lopinavir (LOP), remdesivir (REM), and ritonavir (RIT), using activated sludge. A full factorial design combined with response surface methodology (RSM) was used to assess the impact of pH, temperature (T), and mixed liquor suspended solids (MLSS) on SAS removal and microbial stability. The results distinguished two dominant removal pathways. DCV and LOP were primarily removed by adsorption, whereas DRV, FAV, REM and RIT were predominantly removed through biodegradation involving enzymatic transformation and bacterial co-metabolism. RSM achieved a desirability score of 0.772 and identified the optimal operating conditions (pH = 6.08, MLSS = 4.41 g/L, and T = 44.99 °C), resulting in removal efficiencies above 93% for all compounds except DRV, which remained the limiting compound with a maximum removal efficiency of 66%. Perturbation analysis showed that all tested factors have a distinct influence on process performance. These established kinetic trends should support further investigations into advanced biological wastewater treatment methods and precise ecotoxicity profiling of emerging biotransformation products.