Additive technologies allowed for the development of medicine and implantology, enabling the production of personalized and highly porous implants. Although implants of this type are used clinically, they are usually only heat treated. Surface modification using electrochemical methods can significantly improve the biocompatibility of biomaterials used for implants, including printed ones. The study examined the effect of anodizing oxidation on the biocompatibility of a porous implant made of Ti6Al4V by the SLM method. The study used a proprietary spinal implant intended for the treatment of discopathy in the c4–c5 section. As part of the work, the manufactured implant was assessed in terms of compliance with the requirements for implants (structure testing—metallography) and the accuracy of the pores produced (pore size and porosity). The samples were subjected to surface modification using anodic oxidation. The research was carried out for 6 weeks in in vitro conditions. Surface topographies and corrosion properties (corrosion potential, ion release) were compared for unmodified and anodically oxidized samples. The tests showed no effect of anodic oxidation on the surface topography and improved corrosion properties. Anodic oxidation stabilized the corrosion potential and limited the release of ions to the environment.

In this study, we aimed to determine the effect of long-term exposure to artificial urine on the physical properties of CoCrMo alloy with biodegradable heparin-releasing polymeric coatings. Variants of polymer coatings of poly(L,L-lactide-ɛ-caprolactone) (P(L,L-L/CL)) and poly(D,L-lactide-ɛ-caprolactone) (P(D,L-L/CL)) constituting the base for heparin-releasing (HEP) polyvinyl alcohol (PVA) coatings were analyzed. The coatings were applied by the dip-coating method. Heparin was used to counteract the incrustation process in the artificial urine. The study included tests of wettability, resistance to pitting and crevice corrosion, determination of the mass density of metal ions penetrating into the artificial urine, and the kinetics of heparin release. In addition, microscopic observations of surface roughness and adhesion to the metal substrate were performed. Electrolytically polished CoCrMo samples (as a reference level) and samples with polymer coatings were used for the tests. The tests were conducted on samples in the initial state and after 30, 60, and 90 days of exposure to artificial urine. The analysis of the test results shows that the polymer coatings contribute by improving the resistance of the metal substrate to pitting and crevice corrosion in the initial state and reducing (as compared with the metal substrate) the mass density of metal ion release into the artificial urine. Moreover, the PVA + HEP coating, regardless of the base polymer coatings used, contributes to a reduction in the incrustation process in the first 30 days of exposure to the artificial urine.

Titanium alloys belong to the metal biomaterials that are one of the most widely used in medicine. In recent years, in order to reduce the use of vanadium, Ti6Al4V alloy is increasingly replaced by Ti6Al7Nb alloy. In addition, to ensure the best possible biocompatibility, its surface is subjected to appropriate modifications, for example, anodic oxidation. Despite the extensive use of anodic oxidation of titanium implants in orthopedics, there are few works focused on a detailed analysis of the chemical composition of the surface layers. In addition, the effect of treatments before anodic oxidation on the properties of the produced layer has not been analyzed. Thus, the purpose of this study was to analyze in detail the chemical composition of the passive layer of Ti6Al7Nb alloy obtained by anodic oxidation preceded by sandblasting. Moreover, the physicochemical properties of the analyzed surface affecting biocompatibility were determined. For this purpose, surface observation, wettability and roughness tests, microhardness tests, electrochemical tests and phase composition analysis were carried out. In addition, the preclinical suitability, of the surface modified in this way, was evaluated by cytotoxicity tests.