Greater specific energy densities in lithium-ion batteries can be achieved by using three-dimensional (3D) porous current collectors, which allow for greater areal mass loadings of the electroactive material. In this paper, we present the use of embroidered current collectors for the preparation of thick, pouch-type Li-ion batteries. Experiments were performed on LiFePO₄ (LFP) water-based slurries using styrene-butadiene rubber (SBR) as binder and sodium carboxymethyl cellulose (CMC) as thickener, and formulations of different rheological characteristics were investigated. The electrochemical performance (cyclic voltammetry, rate capability) and morphological characteristics of the LFP half-pouch cells (X-ray micro computed tomography and scanning electron microscopy) were compared between the formulations. An optimum electrode formulation was identified, and a mechanism is proposed to explain differences between the formulations. With the optimum electrode formulation, 350 µm casted electrodes with high mechanical stability were achieved. Electrodes exhibited 4–6 times greater areal mass loadings (4–6 mAh cm⁻²) and 50% greater electroactive material weight than with foils. In tests of half- and full-pouch embroidered cells, a 50% capacity utilization at 1C-rate and 11% at 2C-rate were observed, with a full recovery at C/5-rate. The cycling stability was also maintained over 55 cycles.

The integration of electrical functionality into flexible textile structures requires the development of new concepts for flexible conductive material. Conductive and flexible thin films can be generated on non-conductive textile materials by electroless metal deposition. By electroless copper deposition on lyocell-type cellulose fabrics, thin conductive layers with a thickness of approximately 260 nm were prepared. The total copper content of a textile fabric was analyzed to be 147 mg per g of fabric, so that the textile character of the material remains unchanged, which includes, for example, the flexibility and bendability. The flexible material could be used to manufacture a thermoelectric sensor array and generator. This approach enables the formation of a sensor textile with a large number of individual sensors and, at the same time, a reduction in the number of electrical connections, since the conductive textile serves as a common conductive line for all sensors. In combination with aluminum, thermoelectric coefficients of 3–4 µV/K were obtained, which are comparable with copper/aluminum foil and bulk material. Thermoelectric generators, consisting of six junctions using the same material combinations, led to electric output voltages of 0.4 mV for both setups at a temperature difference of 71 K. The results demonstrate the potential of electroless deposition for the production of thin-film-coated flexible textiles, and represent a key technology to achieve the direct integration of electrical sensors and conductors in non-conductive material.

Si holds great promise as an alloying anode material for Li-ion batteries with improved energy density because of its high theoretical specific capacity and favorable operation voltage range. However, the large volume expansion of Si during electrochemical reaction with Li and the associated adverse effects strongly limit its prospect for application. Here, we report on the use of three-dimensional instead of flat current collectors for high-capacity Si anodes in an attempt to mitigate the loss of electrical contact of active electrode regions as a result of structural disintegration with cycling. The current collectors were produced by technical embroidery and consist of interconnected Cu wires of diameter <150 µm. In comparison to Si/Li cells using a conventional Cu foil current collector, the embroidered microwire network-based cells show much enhanced capacity and reversibility due to a higher degree of tolerance to cycling.