The article presents the results of primary crystallization, wear resistance and SEM studies of chromium cast iron inoculated with ferrotitanium and rare earth elements as a mischmetal inoculating mixture. Thermal-derivative analysis method was used to conduct studies of primary crystallization in two types of testers, namely ATD-C and ATD-Is, reflecting two different cooling speeds. Wear resistance tests were performed with the use of modified pin-on-disk method on Tribotester 3-POD device, where the samples were moving in circular motion in metal-mineral friction system. Silicon carbide was used as a counter sample. The studies allowed to determine the influence of selected inoculants on the microstructure and wear resistance of the studied samples. All characteristic crystallization temperatures of samples casted into ATD-Is testers increased, as well as wear resistance of each inoculated samples compared to the non-inoculated sample. It was proven that TiC and REE compounds are effective inoculants for chromium carbides and that REE compounds can work as underlay for TiC crystallization.

Paper presents the results of studies on primary crystallization and wear resistance of high chromium cast iron inoculated with ferrotitanium intended for work in abrasive conditions. Primary crystallization was examined with use of TDA method, wear tests of the samples were conducted using the modified pin-on-disk method.

Medium-alloy ductile iron with a SiMo ferritic matrix has very good heat resistance. The addition of chromium and aluminum also increases this resistance. This article presents the impact of chromium and aluminum on the structure of SiMo cast iron, especially their impact on the deformation of the spherical graphite precipitates and the formation of M₆C and M₃C₂ carbide phases. These carbides are formed in a ferritic matrix or at the grain boundaries, resulting in increased hardness and a drastic reduction in impact strength. The article presents the influence of heat treatment on the material’s microstructure and resistance to abrasive wear. Chromium and aluminum additions can also indirectly reduce the abrasive wear resistance of SiMo cast iron. The presented research shows the possibility of doubling the abrasive wear resistance of SiMo cast iron.

This paper presents the results of research conducted in the field of the technology of surface hardening of castings from unalloyed and low-alloy nodular cast iron using the laser remelting method. The range of studies included macro- and microhardness measurements using Rockwell and Vickers methods as well as metallographic microscopic examinations using a scanning electron microscope. Moreover, abrasive wear resistance tests were performed using the pin-on-disk method in the friction pair of nodular cast iron—SiC abrasive paper and the reciprocating method in the friction pair of nodular cast iron—unalloyed steel. Analysis of the test results shows that the casting surface layer remelting by laser for unalloyed nodular cast iron results in a greater improvement in its resistance to abrasive wear in the metal–mineral system, as compared to low-alloy cast iron. Additionally, carrying out the laser hardening treatment of the surface layer made of the tested grades of nodular cast iron is justified only if the tribological system of the cooperating working parts and allowable dimensional changes during their operation are known.

In the paper the results and analysis of abrasive wear studies were shown for two grades of cast steels: low-alloyed cast steel applied for heavy machinery parts such as housing, covers etc. and chromium cast steels applied for kinetic nodes of pin-sleeve type. Studies were performed using the modified in Department of Foundry pin-on-disc method

The article shows results of studies of primary crystallization and wear resistance of Cr-Ni-Mo cast steel intended for work in corrosive and abrasive conditions. The studies of primary crystallization were conducted with use of TDA method and modified tester allowing measurement casting cooling time influence on the cooling and crystallization curves of studied alloys. After heat treatment of examined cast steel wear tests of the samples were conducted on pin-on-disc type device.