This paper presents the results of a comprehensive study of the structure, phase composition, thermal corrosion, and tribological properties of multilayer gradient coatings based on YSZ/NiCrAlY obtained using detonation spraying. X-ray phase analysis showed that the coatings consist entirely of metastable tetragonal zirconium dioxide (t’-ZrO₂) phase stabilized by high temperature and rapid cooling during spraying. SEM analysis confirmed the multilayer gradient phase distribution and high density of the structure. Wear resistance, optical profilometry, wear quantification, and coefficient of friction measurements were used to evaluate the operational stability. The results confirm that the structural parameters of the coating, such as porosity and phase gradient, play a key role in improving its resistance to thermal corrosion and CMAS melt, which makes such coatings promising for use in high-temperature applications. It is shown that a dense and thick coating effectively prevents the penetration of aggressive media, providing a high barrier effect and minimal structural damage. Tribological tests in the temperature range from 21 °C to 650 °C revealed that the best characteristics are observed at 550 °C: minimum coefficient of friction (0.63) and high stability in the stage of stable wear. At room temperature and at 650 °C, there is an increase in wear due to the absence or destabilization of the protective layer.

This article presents a comprehensive study of the mechanical and tribological properties of detonation coatings in the NiCr-Al system. Using the detonation spraying technology, NiCr-Al homogeneous (HC) and gradient coatings (GCs) were produced, and their characteristics were determined. Modern analytical instruments were used in the course of the study. The results showed that the microhardness of the NiCr-Al GC was approximately 30% higher compared to the NiCr-Al HC. According to nanoindentation results, the elasticity modulus and nanohardness of the NiCr-Al GC were twice as high as those of the NiCr-Al homogeneous coating. Tribological tests conducted using the rotational ball-on-disk contact geometry showed that the wear rate of the NiCr-Al GC was significantly lower, while the friction coefficients of both coatings were approximately similar. According to the adhesion strength tests, the strength of the NiCr-Al GC was recorded at 38.7 ± 6.9 MPa, while that of the NiCr-Al HC was approximately 25.4 ± 3.1 MPa. High-temperature tribological tests revealed that the wear resistance of the NiCr-Al GC was 2.5 times higher than that of the NiCr-Al HC. The conducted studies demonstrated that the coating structure, particularly the distribution of elements, has a significant influence on its mechanical and tribological properties. Overall, the NiCr-Al GC exhibited superior mechanical and tribological performance.

This study examined the impact of hybridization on the mechanical properties of glass–epoxy laminates by incorporating metal oxides and graphite particles into the resin matrix. Basic mechanical tests were conducted, followed by accelerated thermal aging tests. Results showed an increase in bending strength ranging from 12% to almost 30% depending on the used additive. Static tensile tests indicated a 10% increase in strength for materials modified with flake graphite. Accelerated aging tests resulted in a 20% decrease in elastic modulus and 10% decrease in tensile strength. Additives did not improve tensile strength but increased stiffness by 30% for laminates with flake graphite. Fatigue and conductivity tests were also performed, revealing enhanced thermal conductivity and reduced impedance in materials modified with graphite flakes. The study suggests that additives can enhance the mechanical properties of glass–epoxy laminates, making them suitable for applications in automotive and aerospace industries.

This study aimed to examine the impact of graphite morphology on the water absorption and fatigue properties of biopolyamide-based composites. Graphite was incorporated into the polymer matrix in two distinct forms—flake and expanded—to evaluate its effect on key performance characteristics...