A comparative study of the physicochemical properties of natural bentonite clays of Pogodayevo (Republic of Kazakhstan, mod. 1) and Dash-Salakhli (Republic of Azerbaijan, mod. 2) deposits and modification of the bentonite clay with polyhydroxocations of iron (III) and aluminium (III). The amount of bentonite in the concentration of iron (aluminum) was 5 mmol Me³⁺/g. It was established that the modification of natural bentonites using polyhydroxocations of iron (III) (mod. 1_Fe_5-c, mod. 2_Fe_5-c) and aluminum (III) (mod. 1_Al_5-c, mod. 2_Al_5-c) by the method of “co-precipitation” leads to a change in their chemical composition, structural and sorption properties. The results showed that hydroxy-aluminum cations ([Al₃O₄(OH)₂₄(H₂O)₁₂]⁷⁺) and poly-hydroxyl-Fe or polyoxo-Fe were intercalated into clay layers, which led to an increase in the values of d₀₀₁ and specific surface areas compared to those of the original bentonite, from 37 to 120 m²/g for the Pogodaevo bentonite and from 51 to 172 m²/g respectively, for bentonite from the Dash-Salakhli deposit. It is shown that modified sorbents based on natural bentonite are finely porous objects with a predominance of pores of 1.5–8.0 nm in size. As a result, there is a significant increase in the specific surface area of sorbents. Modification of bentonite with polyhydroxocations of iron (III) and aluminum (III) by the “co-precipitation” method also leads to an increase in the sorption capacity of the sorbents obtained with respect to nickel (II) cations. Modified bentonites were used for the adsorption of Ni (II) ions from the model solution. Ni (II) was absorbed in a neutral pH solution. The study of equilibrium adsorption showed that the data are in good agreement with the Langmuir isotherm model. The maximum adsorption capacity of the Ni (II) obtained from the Langmuir equation was 25.0 mg/g (mod. 1_Al_5-c), 18.2 mg/g (mod. 2_Al_5-c) for Al-bentonite and 16.7 mg/g (mod. 1_Fe_5-c), 10.1 (mod. 2_Fe_5-c) for Fe-bentonite. The kinetics of adsorption is considered. The high content of Al-OH anion exchange centers in them determines the higher sorption activity of Al-modified bentonites.

The physicochemical properties of natural bentonite and its sorbents were studied. It has been established the modification of natural bentonites using polyhydroxoxides of iron (III) (mod.1_Fe_5-c) and aluminum (III) (mod.1_Al_5-c) by the “co-precipitation” method led to changes in their chemical composition, structure, and sorption properties. It was shown that modified sorbents based on natural bentonite are finely porous (nanostructured) objects with a predominance of pores of 1.5–8.0 nm in size. The modification of bentonite with iron (III) and aluminum compounds by the “co-precipitation” method also leads to an increase in the sorption capacity of the obtained sorbents with respect to bichromate and arsenate anions. A kinetic analysis showed that, at the initial stage, the sorption process was controlled by an external diffusion factor, that is, the diffusion of the sorbent from the solution to the liquid film on the surface of the sorbent. The sorption process then began to proceed in a mixed diffusion mode when it limited both the external diffusion factor and the intra-diffusion factor (diffusion of the sorbent to the active centers through the system of pores and capillaries). To clarify the contribution of the chemical stage to the rate of adsorption of bichromate and arsenate anions by the sorbents under study, kinetic curves were processed using equations of chemical kinetics (pseudo-first-order, pseudo-second-order, and Elovich models). It was found that the adsorption of the studied anions by the modified sorbents based on natural bentonite was best described by a pseudo-second-order kinetic model. The high value of the correlation coefficient for the Elovich model (R² > 0.9) allows us to conclude that there are structural disorders in the porous system of the studied sorbents, and their surfaces can be considered heterogeneous. Considering that heterogeneous processes occur on the surface of the sorbent, it is natural that all surface properties (structure, chemical composition of the surface layer, etc.) play an important role in anion adsorption.

A comparative study of the physicochemical properties of natural bentonite clays of Pogodayevо (Republic of Kazakhstan, mod.1) and Dash-Salakhli (Republic of Azerbaijan, mod.2) deposits and modification of the bentonite clay with polyhydroxocations of iron (III) and aluminium (III). It-wasestablished that the modification of natural bentonitesusing polyhydroxocations of iron (III) and aluminium(III) by the method of "co-precipitation" leads to a change in their chemical composition, structural and sorption properties. The results showed that hydroxy-aluminum cations ([Al3O4(OH)24(H2O)12]7+) and poly-hydroxyl-Fe or polyoxo-Fe were intercalated into clay layers, which led to an increase in the values of d001 and specific surface areas compared to those of the original bentonite, from 37 to 120 for the Pogodaevo bentonite and from 51 to 172 respectively for bentonite from the Dash-Salakhli deposit. It is shown that modified sorbents based on natural bentonite are finely porous objects with a predominance of pores of 1.5−6.0 nm in size. As a result, there is a significant increase in the specific surface area of sorbents. Modification of bentonite with polyhydroxocations of iron (III) and aluminium (III) by the "co-precipitation" method also leads to an increase in the sorption capacity of the sorbents obtained with respect to nickel (II) cations. Modified bentonites were used for the adsorption of Ni (II) ions from the model solution. Ni (II) was absorbed in a neutral pH solution. The study of equilibrium adsorption showed that the data are in good agreement with the Langmuir isotherm model. The maximum adsorption capacity of the Ni (II) monolayer obtained from the Langmuir equation was 25.0 mg/g (mod. 1_Al_5-c), 18.2 mg/g (mod. 2_Al_5-c) for Al-bentonite and 16.7 mg/g (mod. 1_Fe_5-c), 10.1 (mod. 2_Fe_5-c) for Fe-bentonite. The kinetics of adsorption is considered. The high content of Al-OH anion exchange centresin them determines the higher sorption activity of Al-modified bentonites.

Zeolite-based composite nanomaterials represent a versatile and mechanistically rich platform for the removal of organic micropollutants (OMPs)—including pharmaceuticals, endocrine-disrupting compounds, pesticides, and per- and polyfluoroalkyl substances (PFAS)—from contaminated water systems. Although pristine zeolite frameworks provide well-defined microporous architectures, tunable Si/Al ratios, and ion-exchange capacity, their intrinsic hydrophilicity restricts interaction diversity and limits performance toward the structurally heterogeneous OMPs prevalent in real aquatic environments. Composite integration with carbonaceous nanophases, functional polymers and surfactants, and catalytically active metal oxide nanoparticles substantially extends this interaction repertoire, yielding multifunctional materials whose adsorption performance exceeds that of the individual components. Drawing on a systematic survey of peer-reviewed literature published between 2016 and 2026, this review develops a mechanism-oriented, structure–property–performance framework examining five dominant adsorption mechanisms—electrostatic attraction, π–π stacking, hydrogen bonding, hydrophobic partitioning, and micropore confinement—in relation to composite nanoarchitecture, surface chemistry, and structural parameters. The modulating influence of realistic water matrix conditions on adsorption efficiency is critically assessed, alongside challenges of regeneration, long-term stability, metal leaching, and the persistent gap between laboratory-scale synthesis and scalable deployment. Priority research directions are identified, including standardized performance evaluation under environmentally representative conditions and rational design of hierarchical multifunctional nanocomposites from earth-abundant and waste-derived precursors.

Background: Chamaenerion latifolium is a perennial herbaceous plant of the Onagraceae family. The purpose of this study was to evaluate and compare the volatile chemical components of the aerial parts of Chamaenerion latifolium growing in the Republic of Kazakhstan. Method: The leaves and stems of Chamaenerion latifolium were extracted with hexane and analysed by gas chromatography-mass spectrometry (GC-MS). Results: The regularisation of peak areas method was used to calculate the concentrations of the sixty-five identified compounds. Conclusion: Among them, the major components are alkanes (leaves 31.339%, stems 48.158%), esters (leaves 10.216%, stems 12.196%), alcohols (leaves 5.483% and stems 5.14%), aldehydes (leaves 3.155%, stems 1.592%), triterpenoids (leaves 2.247% stems 3.785%).

The physicochemical and adsorption properties of granular sorbents based on natural bentonite and modified sorbents based on it have been studied. It was found that modification of natural bentonite with iron (III) polyhydroxocations (mod. 1_Fe_5 GA) and aluminum (III) (mod. 1_Al_5 GA) by the “co-precipitation” method leads to a change in their chemical composition, structure, and sorption properties. It is shown that modified sorbents based on natural bentonite are finely porous (nanostructured) objects with a predominance of pores measuring 1.5–8.0 nm, with a specific surface area of 55–65 m²/g. Modification of bentonite with iron (III) and aluminum compounds by the “co-precipitation” method also leads to an increase in the sorption capacity of the obtained sorbents with respect to bichromate and arsenate anions and nickel cations by 5-10 times compared with natural bentonite. The obtained sorption isotherms were classified as Langmuir type isotherms. Kinetic analysis showed that at the initial stage the sorption process is controlled by an external diffusion factor, i.e. refers to the diffusion of sorbent from solution into a liquid film on the surface of the sorbent. Then the sorption process begins to proceed in a mixed diffusion mode, when it limits both the external diffusion factor and the internal diffusion factor (the diffusion of the sorbent to the active centers through the system of pores and capillaries). To determine the contribution of the chemical stage to the rate of adsorption of bichromate and arsenate anions and nickel(II) cations with the studied granular sorbents, kinetic curves were processed using the equations of chemical kinetics (pseudo-second-order model). As a result, it was found that the adsorption of the studied anions by modified sorbents based on natural bentonite is best described by a pseudo-second-order kinetic model. It is shown that the use of natural bentonite for the development of technology for the production of granular sorbents based on it has an undeniable advantage, firstly, in terms of its chemical and structural properties, it is easily and effectively modified, and secondly, having astringent properties, granules are easily made on its basis, which turn into ceramics during high-temperature firing. The result is a granular sorbent with high physical and mechanical properties. Since bentonite is an environmentally friendly product, the technology of recycling spent sorbents is also greatly simplified.