One of the most critical problems faced by modern civilization is the depletion of freshwater resources due to their continuous consumption and contamination with different organic and inorganic pollutants. This paper considers the potential of already discovered MXenes in combination with carbon nanomaterials to address this problem. MXene appears to be a highly promising candidate for water purification due to its large surface area and electrochemical activity. However, the problems of swelling, stability, high cost, and scalability need to be overcome. The synthesis methods for MXene and its composites with graphene oxide, carbon nanotubes, carbon nanofibers, and cellulose nanofibers, along with their structure, properties, and mechanisms for removing various pollutants from water, are described. This review discusses the synthesis methods, properties, and mechanisms of water purification using MXene and its composites. It also explores the fundamental aspects of MXene/carbon nanocomposites in various forms, such as membranes, aerogels, and textiles. A comparative analysis of the latest research on this topic shows the progress in this field and the limitations for the practical application of MXene/carbon nanocomposites to solve the problem of drinking water scarcity. Consequently, this review demonstrates the relevance and promise of the material and underscores the importance of further research and development of MXene/carbon nanocomposites to provide effective water treatment solutions.

Aluminum–carbon nanotube (Al–CNT) composites represent a cutting-edge class of materials characterized by their exceptional mechanical, thermal, and electrical properties, making them highly promising for aerospace, automotive, electronics, and energy applications. This review systematically examines the impact of various fabrication methods, including conventional powder metallurgy, diffusion and reaction coupling, as well as adhesive and reaction bonding on the microstructure and performance of Al–CNT composites. The analysis emphasizes the critical role of CNT dispersion, interfacial bonding, and the formation of reinforcing phases, such as Al₄C₃ and Al₂O₃, in determining the mechanical strength, wear resistance, corrosion resistance, and thermal stability of these materials. The challenges of CNT agglomeration, high production costs, and difficulties in controlling interfacial interactions are highlighted alongside potential solutions, such as surface modifications and reinforcement strategies. The insights presented aim to guide future research and innovation in this rapidly evolving field.

The increasing reliance on electronic technologies has elevated the urgency of effective electromagnetic interference (EMI) shielding materials. This review explores the development and potential of magnetite-incorporated one-dimensional (1D) carbon nanostructure hybrids, focusing on their unique properties and synthesis methods. By combining magnetite’s magnetic properties with the electrical conductivity and mechanical strength of carbon nanostructures such as carbon nanotubes (CNTs) and carbon fibers (CFs), these hybrids offer superior EMI shielding performance. Various synthesis techniques, including solvothermal synthesis, in situ growth, and electrostatic self-assembly, are discussed in detail, highlighting their impact on the structure and properties of the resulting composites. This review also addresses the challenges in achieving homogeneous dispersion of nanofillers and the environmental and economic considerations of large-scale production. The hybrid materials’ multifunctionality, including enhanced mechanical strength, thermal stability, and environmental resistance, underscores their suitability for advanced applications in aerospace, electronics, and environmental protection. Future research directions focus on optimizing synthesis processes and exploring new hybrid configurations to further improve electromagnetic properties and practical applicability.

This paper presents an experimental study on the performance of shielding concrete with additives of magnetite nanoparticles. Two concretes with magnetite additives as well as one based concrete were tested. In order to achieve the high-performance concrete, all concrete mixes had a constant water/cement ratio of 0.45. In order to measure the mechanical properties, concrete samples were made in accordance with dimension such as 40 × 40 × 160 mm. But, for measurement of protective properties the concrete was made in accordance with dimension of rotary antennas such as 400 × 400 mm with a thickness of 10 mm. The nanoparticles Fe3O4 were synthesized by chemical condensation method. XRD have shown the presence of cubic structure of Fe3O4 spinel with crystallite size is equal to 130.0 Å. The TEM microphotograph shows that theFe3O4 nanoparticles are spherical, the range of sizes is 12‒30 nm. The magnetic retardation suggests that the magnetite nanoparticles have superparamagnetic properties. This is explained by the fact that under the influence of external magnetic field, they are single-domain, in other words, they become uniformly magnetized throughout the volume. The additives of magnetite nanoparticles at a concentration of 0.5% mass have not a negative effect on flexural strength. The samples with additives of magnetite nanoparticles showed better shielding of microwave radiation in the frequency range from 0.7 GHz to 13 GHz. The maximum efficiency of suppression of electromagnetic disturbance is equal to 19.9 dB at a frequency of 1.5 GHz with a thickness of 10 mm.

In both fundamental and applied scientific exploration, nanostructured protective materials have garnered substantial interest owing to their multifaceted utilization in the fields of medicine, pharmaceuticals, and electronics, among others. This study investigated the evolution of cutting-edge materials for electromagnetic radiation attenuation, with a specific emphasis on the incorporation of superparamagnetic magnetite nanoparticles, Fe₃O₄, into composite systems. The nanoparticles were generated through chemical condensation, meticulously adjusting the proportions of iron salts, specifically FeSO₄·7H₂O and FeCl₃·6H₂O, in conjunction with a 25% aqueous solution of ammonia, NH₄OH·H₂O. This study examined the intricate details of the crystalline structure, the precise composition of phases, and the intricate physicochemical attributes of these synthesized Fe₃O₄ nanoparticles. The analysis was conducted employing a suite of advanced techniques, including scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and energy-dispersive analysis (EDAX). The key findings of this research suggest that the magnetic nanoparticles generated through chemical condensation have an average size between 10 and 11 nm. This size was determined using BET surface area measurements, which were precise to within 0.1 nm. Moreover, this study demonstrated that incorporating superparamagnetic nanoparticles into composite materials significantly reduces microwave radiation. In particular, an optimal concentration of 0.25% by weight leads to a maximum decrease of 21.7 dB in cement specimens measuring 10 mm in thickness. Moreover, a critical threshold concentration of 0.5 weight percent is established, beyond which the interactions of nanoparticles inhibit the process of remagnetization. These investigations demonstrate that it is feasible to pursue a route towards the development of highly effective electromagnetic shielding materials tailored to specific requirements for diverse applications.