This article presents a facile synthesis method used to obtain new composite films based on polylactic acid and micro-structured hydroxyapatite particles. The composite films were synthesized starting from a polymeric solution in chloroform (12 wt.%) in which various concentrations of hydroxyapatite (1, 2, and 4 wt.% related to polymer) were homogenously dispersed using ultrasonication followed by solvent evaporation. The synthesized composite films were morphologically (through SEM and atomic force microscopy (AFM)) and structurally (through FT-IR and Raman spectroscopy) characterized. The thermal behavior of the composite films was also determined. The SEM and AFM analyses showed the presence of micro-structured hydroxyapatite particles in the film’s structure, as well as changes in the surface morphology. There was a significant decrease in the crystallinity of the composite films compared to the pure polymer, this being explained by a decrease in the arrangement of the polymer chains and a concurrent increase in the degree of their clutter. The presence of hydroxyapatite crystals did not have a significant influence on the degradation temperature of the composite film.

In this work, we report facile synthesis and characterization of new cellulose acetate-hydroxyapatite membranes for water purification and biomedical applications. The membranes were synthesized from a polymer solution in N, N’-dimethylformamide (12% wt.) where different concentrations of hydroxyapatite (1, 2, 4% wt. based on the amount of polymer) were dispersed using sonication. The synthesis of membranes was carried out by precipitation employing phase inversion using deionized water. The morphological and structural characterization of the synthesized membranes was carried out using SEM, EDS and FT-IR. Thermal characterization (TGA & DTG) and water flows analysis of the synthesized membranes was also carried out. The SEM analysis confirmed the presence of hydroxyapatite micro/nanostructured particles in the membrane as well as significant changes in the morphology of the membranes surface. The presence of inorganic compounds was also found to influence the thermal or hydrodynamic properties of the composite membranes, leading to a more stable hydrodynamic behavior, flow variation in time being much lower compared to the control membrane of cellulose acetate